Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (96)
- Posterpräsentation (30)
- Zeitschriftenartikel (23)
- Beitrag zu einem Tagungsband (15)
- Forschungsdatensatz (4)
- Dissertation (2)
- Buchkapitel (1)
- Sonstiges (1)
Sprache
- Englisch (160)
- Deutsch (10)
- Mehrsprachig (1)
- Russisch (1)
Referierte Publikation
- nein (172) (entfernen)
Schlagworte
- Additive manufacturing (172) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (79)
- 9 Komponentensicherheit (70)
- 8.5 Röntgenbildgebung (55)
- 5 Werkstofftechnik (39)
- 9.4 Integrität von Schweißverbindungen (30)
- 8.0 Abteilungsleitung und andere (24)
- 9.3 Schweißtechnische Fertigungsverfahren (24)
- 9.6 Additive Fertigung metallischer Komponenten (20)
- 5.4 Multimateriale Fertigungsprozesse (17)
- 5.2 Metallische Hochtemperaturwerkstoffe (16)
Selective Laser Melting (SLM) technique allows to produce parts with complex geometry. Due to the rapid solidification and heat gradient during production, SLM results in presence of residual stress. The present study shows the influence of manufacturing parameters on surface residual stress of Ti-6Al-4V SLM parts. High tensile stresses in the front surface are found. Heat Treatment conditions relax residual stresses almost to zero. High scanning speed during manufacturing results in higher tensile stresses in the surface.
Additive Manufacturing (AM) by Selective Laser Melting (SLM) offers ample scope for producing geometrically complex parts as compared to the traditional subtractive manufacturing strategies. However, the residual stresses developed during the processing can reduce the load bearing capacity as well as induce unwanted distortion, limiting the application of SLM parts.
IN718 manufactured by SLM process can show high tensile residual stresses in the surface as high as the yield strength of the wrought alloy. On the other hand, residual stresses in the bulk Show considerably lower stress values, even in compression, indicating a stress re-distribution during deposition of the SLM layers.
Laser beam processes are increasingly used in the field of additive manufacturing.
Prominent methods are either powderbed-based like Laser Metal Fusion (LMF), or utilizing a powder nozzle like Laser Metal Deposition (LMD). While LMF allows the manufacturing of complex structures, build rate, part volumes and material flexibility are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, and materials can be changed easily during the process. However LMD shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates and increased material flexibility. In this paper, combined manufacturing with additive technologies LMF and LMD is described. Its benefit for industry with emphasis on turbomachinery is shown. As reality test for the innovation, an industrial turbine blade is manufactured.
Several Additive Manufacturing (AM) processes are based on the deposition of a powder to form a powder-bed layer-by-layer which typically has a low packing density (35-50%) and consequently hinders the ability of sintering ceramic parts to full density.
The layerwise slurry deposition (LSD) is an innovative process for the deposition of layers in AM. In the LSD, a slurry with no or small organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle to form thin layers with a high packing density (55-60%). When coupled with a printing head or with a laser, the LSD enables novel AM technologies inspired to the 3D printing or selective laser sintering, but taking advantage of having a highly dense powder-bed. This approach has been successfully applied to silicate ceramics, but implementing technical ceramic slurries is more challenging, because the water is drained too quickly from the suspension into the pores of the previous porous layer forming a cast.
In this presentation, the variables involved in the LSD will be analyzed and the latest improvements in the deposition setup will be described. The application of the LSD to technical ceramics has the potential of generating additive manufacturing parts which in the green state are comparable to those produced by slip casting.
The layerwise slurry deposition (LSD) is an innovative process for the deposition of layers in AM. In the LSD, a slurry with no or low organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle to form thin layers with a high packing density (55-60%). The LSD therefore shares aspects both of tape casting and slip casting. The LSD differentiates from the classical powder-based AM layer deposition, which typically are able to achieve only a low packing density (35-50%), consequently hindering the ability of sintering ceramic parts to full density. The LSD is coupled with the principles of selective laser sintering (SLS) or binder printing, to generate novel processes which take advantage of the possibility of achieving a highly dense powder-bed.
This presentation will describe the most recent developments in the application of the LSD to technical ceramics, in particular Al2O3 and SiC, discussing potential and issues connected to the layer deposition and the selective laser sintering of such layers.
Additive Manufacturing by Selective Laser Melting (SLM) offers ample scope for producing geometrically complex parts as compared to the traditional subtractive manufacturing strategies. However, the residual stresses (RS) developed during the processing can reduce the load bearing capacity as well as induce unwanted distortion, limiting the application of SLM parts. In the present work, residual stresses in additivly manufactured IN718 part were analised by means of neutron diffraction and synchrotron X-ray diffraction.
The process of laser metal deposition can be applied in many ways. Mostly, it is relevant to coating, for repair welding and for additive manufacturing. To increase the effectiveness and the productiveness, a good process understanding is necessary. Statistical test planning is effectual and often used for this purpose. For financial and temporal reasons, a restriction of the test space is reasonable. In this case, it is recommended to use a D-optimal experimental design which is practically applied to extend existing test plans or if process Limits are known. This paper investigates the applicability of a D-optimum experimental design for the laser metal deposition. The results are compared to the current results of a full factorial test plan.
Known restrictions are used for the limitation of the test space. Ti6Al4 is utilized as Substrate material and powder. Comparable results of the D-optimal experimental design and of the full factorial test plan can be demonstrated. However, 80 % of time can be saved by the experimental procedure. For this reason, the application of D-optimal experimental design for laser metal deposition is recommend.
Laser metal deposition is described with its applications for additive manufacturing. The necessary process chain is discussed, with regard to weld bead dimensions and 3D build-up strategy. Metallurgical cross sections, x-ray and tensile tests are conducted. As demonstrative components, a gas turbine burner and a turbine blade are shown
The process of laser cladding has become more important during recent years because of its broad application for cladding, repair or additive manufacturing. In the field of mechanical engineering, one use is the repair of turbine blades. For high quality and reliability of the repaired components, it is necessary to adjust the weld bead geometry to the specific repair task. The bead geometry influences the metallurgical bonding and the degree of dilution as well as the formation of defects like pores or cracks. Therefore, it is important to know the effects of the different parameters on the welding bead. A valuable tool to meet this industrial challenge is the design of experiments (DoE). In this context, the user can choose between a huge number of test plans. Greater Profit of information is expected by a larger test range. In order to confirm the acceptance, a five-step full factorial test plan is compared to a central composite design in this paper. Moreover, the limits of the experimental range are indicated and restrictions can be derived. As the results show, the essential effects are detected with a full factorial test plan as well as with a central composite design. Merely the effect strength could not always be specified unambiguously. On this account and in consideration of cost efficiency, the use of central compound design is recommended in industrial applications.
In the present study, Ti-6Al-4V bridge-like specimens were manufactured additively by selective laser melting (SLM) under different laser scanning speed conditions in order to compare the effect of process energy density on the residual stress state. Subsurface residual stress analysis was conducted by means of synchrotron diffraction in energy dispersive mode for three conditions: as-built on base plate, released from base plate, and after heat treatment on the base plate. The quantitative residual stress characterization shows a correlation with the qualitative bridge curvature method. Computed tomography (CT) was carried out to ensure that no stress relief took place owing to the presence of porosity. CT allows obtaining spatial and size pores distribution which helps in optimization of the SLM process.
High tensile residual stresses were found at the lateral surface for samples in the as-built conditions. We observed that higher laser energy density during fabrication leads to lower residual stresses. Samples in released condition showed redistribution of the stresses due to distortion. A method for the calculation of the stress associated to distortion of the parts after cutting from base plate is proposed. The distortion measurements were used as input for FEM simulations.
Laser metal deposition is described with its applications for additive manufacturing. The necessary process chain is discussed, with regard to weld bead dimensions and 3D build-up strategy. Metallurgical cross sections, x-ray and tensile tests are conducted. As demonstrative components, a gas turbine burner and a turbine blade are shown.
Additive manufacturing (3D printing) of ceramics and other materials offers significant advantages compared to conventional production processes for several applications. While ceramics have been extensively investigated in this regard, additive manufacturing of geopolymers have received much less attention to date. In the present contribution we study a ‘standard’ metakaolin-based geopolymer, a fly ash-based geopolymer and a silica-based one-part geopolymer regarding their suitability for additive manufacturing via selective laser curing. Model geometries such as bars and cuboids could be produced by this route. After selective laser curing the specimens were additionally cured at 80 °C for 24 h. The specimens were studied by means of scanning electron microscopy (SEM) and powder X-ray diffraction (XRD). SEM showed that the precursors in all geopolymers had reacted partially and geopolymeric gel had formed. XRD confirmed these results and additionally revealed that the crystalline byproducts (zeolites) in the one-part geopolymer differed from the byproducts observed in conventionally produced samples. This indicates that also the geopolymerization reactions differ between the two synthesis routes. The mechanical strength after selective laser curing and 80 °C-curing appeared to be highest for the metakaolin-based geopolymer. However, SEM also showed that a significant volume of macropores remained in most regions of all specimens, while some regions in the metakaolin-based geopolymer appeared to be significantly denser. These preliminary results demonstrate that selective laser curing offers potential for the production of geopolymers, but more research has to be undertaken to optimize the process.
Additive Manufacturing (AM) by Selective Laser Melting (SLM) offers ample scope for producing geometrically complex parts in comparison to the traditional subtractive manufacturing strategies. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.
The combination of tomographic, microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on material and component properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. This logic thread equally holds for industrial and academic research, and valorizes expensive experiments such as those carried out at synchrotron sources, which cannot be daily repeated.
I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing. Examples of micro-structured inhomogeneous materials will be given, such as Composites, Ceramics, Concrete, and Additively manufactured parts. I will also show how X-ray refraction computed tomography (CT) can be highly complementary to classic absorption CT, being sensitive to internal interfaces.
Additionally, I will present a new technique in our portfolio, Neutron Diffraction, which is extremely well suited to the study of internal stresses, both residual and under external load.
Additive Manufacturing (AM) allows for the unique combination of building highly complex parts with integrated functional design. One particular design feature is known as lattice structures, which provide opportunities for innovative applications in the high-temperature regime of gas turbines. These structures require the development of reliable manufacturing methods to produce dependable structural integrity and geometrical accuracy. Consequently, the subsequent validation of these thin structures must also be examined in depth and differently than with current approaches.
In this study, a holistic assessment of Ni based high temperature lattice structures is pursued, utilizing a systematic design-follows-complexity approach. Single struts of different geometries and orientations are investigated first, then combined to a variety of unit cell types and finally multiplied to complex lattice structures.
Initial test trials with these thin structures proved a dependency of geometrical accuracy, microstructure and structural properties to the AM process setup. The trials underlined the need for design guidelines and a distinction between bulk and thin structures, as they showed differences in microstructural and mechanical behaviour. By application of high resolution, non destructive characterization methods such as computer tomography (CT and µCT), evaluation of defects and the thin structures’ metrology has been performed. First results revealed a number of defects compromising the structural integrity and therefore limiting the lifing behaviour. This was confirmed in destructive testing (e.g. tensile and compression). Furthermore, it was proven that the distribution, the number, the size and the type of defects are also dependent on the AM process setup.
While there are large potentials for use of lattice structures in gas turbine applications, the experiments indicate the strong need for an increased understanding of manufacturing and design for these complex structures and that this gap needs to be bridged.
Laser metal deposition (LMD) has been applied as coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing.
Laser metal deposition (LMD) has been applied as coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing.
The residual stress distribution of IN718 parts produced by Selective Laser Melting (SLM) technique was studied by means of neutron diffraction.
Two deposition hatching lengths were considered in the fabrication. Both lateral (building direction) and top (finishing) near-surface regions were characterized. Measurements on samples in as-built condition and after release from the plate proved the presence of stress gradients both in-plane and along the building direction.
As-built samples presented in top region a longitudinal stress relief for large hatching, whereas small one showed tensile stresses around (200MPa) in the middle, evolving towards compression at the tip of the sample (down to -300MPa). Towards the lateral edge, longitudinal stresses shifted also to compression. The transverse stresses for large hatching were relief in the middle, whereas for small hatching shifted to compression at the edge. As for the normal component, this was more homogenous: stress-relief was proved for large hatching and, in contrast, was in compression (-200MPa) for small hatching. In the building direction (lateral region from base plate to top) of the sample with large hatching all stress components showed tensile values near the base plate (particularly high for normal component around 300MPa), decreasing towards compression to the top, where they were almost released.
After release, in the top region, the longitudinal stress component for small hatching showed high compressive stresses in the central part (down to -250MPa). In contrast, for large hatching a stress relief was found. In the transversal direction, this behavior was inverted: a small hatching released stresses more effectively, while a large hatching presented high tensile stresses (around 200MPa). As for the normal component (i.e., building direction), the sample with small hatching was found in compression, while that with large hatching was stress-released or slightly in tension (around 100MPa). In the lateral surface region, all components showed similar behavior: a small hatching promoted high compressive stresses along the building direction, whereas a large hatching showed small tensile values at the bottom, which balance towards the top region. There is an overall shift of stresses in 3 directions towards tension when compared with as-built condition for top region. In contrast, the lateral region is stress-relief or shifted towards compression after cutting from baseplate.
In conclusion, hatching length parameter strongly influenced the 3D distribution of residual stress in SLM produced parts.
Capsule summary
THE MATERIALS
Manufacturers can use preceramic polymers to produce ceramic components in a range of compositions using a variety of additive manufacturing technologies. Preceramic polymers even can overcome some of the problems that are intrinsic to additive manufacturing in general.
THE APPLICATION
Modifying the composition, molecular architecture, and molecular weight of preceramic polymers allows adaptation of these materials to specific processing requirements of individual additive manufacturing technologies.
THE OPPORTUNITY
Further development of new additive manufacturing technologies, in addition to improvement of existing technologies, will enable manufacturing of advanced ceramic components with enhanced mechanical characteristics and new functional properties.
Additive Manufacturing provides an important enabling technology for the digital transformation of the economy. As an emerging technology it has seen a remarkable development over the last three decades. Nevertheless, it is far from a broad adoption with several barriers to overcome yet. One of the major challenges is the lack of standards. The critical role of standardization for innovation is generally recognized, still the topic too often has been neglected in strategic roadmapping exercises for emerging technologies. Too little is known about the complex dynamics and interrelations of standardization and innovation. The anticipation of standardization needs and the timely and efficient implementation of standards is challenging. This paper aims at contributing to a better understanding of the role that standards play in the multi-dimensional system of innovation. It analyzes the trajectories of innovation in Additive Manufacturing in a systematic and holistic way, focusing on standardization activities with regard to coordination, stakeholders involved, the timing and types of standards developed. Putting standardization in context of the multi-dimensional innovation system of Additive Manufacturing the research shows where standards can support the diffusion of an emerging technology.