Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2014 (23) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (8)
- Vortrag (5)
- Beitrag zu einem Tagungsband (4)
- Posterpräsentation (4)
- Buchkapitel (1)
- Dissertation (1)
Sprache
- Englisch (23) (entfernen)
Schlagworte
- AC weld pool support (2)
- Electron backscatter diffraction (2)
- Graphene (2)
- Kikuchi pattern (2)
- Wasserstoff (2)
- Welding of aluminum (2)
- Welding of thick metal plates (2)
- 3D FE-simulation (1)
- AC magnetic fields (1)
- Additive manufacturing (1)
Eingeladener Vortrag
- nein (5)
Today’s light weight design trends lead to a growing application of high-strength structural steels (yield strength ≥ 690 MPa). The mechanical properties of the weld and the component safety have to meet the increased requirements of these steel grades. However, high residual stresses in welded components are detrimental to their safety and integrity. Analyses concerning weld stresses in high-strength steels welded under component related restraint conditions revealed that heat control significantly affects global and local stresses. This occurs especially in highly restrained joints due to superimposing local and global stresses and may cause crack-critical stress-levels. In this study weld tests were performed with plates of high-strength steel in a special test facility. The experimental setup allowed transferring defined restraint conditions to the test welds similarly to real components. Temperature and reaction forces due to restraint were observed online while welding and cooling of multilayer-component MAG-welds. Mobile X-ray diffraction was used for local stress determination in the weld seam areas of the restrained specimens. It was found that interpass temperature has a major influence on the local and global welding forces and stresses. Thus, among the analysed results especially transverse residual stresses of the heat affected zone were strongly affected.
Emergency response units increasingly use pressure cylinders made from fibre composites for breathing air as elements of personal protective equipment (PPE). Such applications expose the composite cylinders to harsh temperature and handling conditions. At least in Europe, standards have been used for certifying PPE, which are designed and mandatory for the approval of pressure receptacles for the transport of dangerous goods. Therefore, service conditions specific to PPEs are not accounted for in these standards. In this paper, BAM (Federal Institute for Materials Research and Testing) investigates the residual safety of a composite cylinder design at the end of their designated service life of 15 years. The cylinders (test pressure PH 450 bars; 6.8 Litres) are of one design type with aluminium liner and fully wrapped with carbon fibres, which is commonly considered a “Type III” cylinder. All cylinders were used as PPE by the Berlin fire department and randomly picked in three samples of 25 cylinders each before tested.
At BAM, the cylinder samples underwent hydraulic load cycle tests (LCT), conventional burst tests (BT) and so called slow burst tests (SBT). A concept for quantification of strength degradation already introduced by BAM was applied. This concept is based on a probabilistic assessment of the average strength and scatter of each sample of cylinders. The strength distributions of the used PPEcylinders is shown and analysed. Some unexpected effects are shown and a refinement of the statistical assessment is introduced.
The impact of pressure, sliding velocity and property variation of constituents on the sliding behaviour of a model tribofilm was studied with the method of movable cellular automata (MCA). Whereas a clear pressure dependency of the coefficient of friction (COF) was always observed and could be correlated with the structure formation in terms of varying thickness of a mechanically mixed layer, the impact of the other parameters was either negligible or rather weak. Only if a brittle-to-ductile Transition of the oxide-based tribofilm was assumed, a significant decrease in the COF level was predicted.
Temperature-dependent property changes can be neglected during MCA modelling, unless this transition takes place. For magnetite-based tribofilms, the transition temperature is beyond 800 °C, i.e. a temperature leading to fading effects during braking anyway. Thus, it could be concluded that, except for very severe braking conditions, sliding simulations with the MCA method yield meaningful results without considering temperature-dependent mechanical properties.
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested
Surface cracks havenoinfluenceon thefatiguelife
Samples with cracks in the electrode indentation /HAZ where tested
Stiffness curves are not significantly influenced by surface cracks
3D FE-Simulation demonstrate no changes of stress due to surface imperfections
Optical and scanning electron microscopy, as well as electron microprobe analysis and electron backscatter diffraction, have been used to study diffusion processes that occur in a diffusion pair that consistsof a single-crystal CMSX-10 nickel-base superalloy and polycrystalline nickel, at temperatures of 1050–1250°C. It has been found that, in this system, the distributions of γ-stabilizing elements (Cr, Co, W, and Re) are described by the Boltzmann solution for diffusion between two semiinfinite plates of a binary alloy. The processing of these distributions has shown that the diffusion coefficients of Cr, Co, W, and Re in the multicomponent system are close to those in binary alloys of these elements with Ni. The diffusion redistribution of the elements leads to the dissolution of the γ′ phase in the nickel-base superalloy, growth of nickel grains toward the superalloy constituent of the diffusion pair, and the formation of porosity on both sides of the migrating interface, which is determined from a crystal misorientation of the alloy single crystal and nickel grains.
Computational Advances
(2014)
Fibre Reinforced Plastics (e.g. CFRP, GFRP) characteristically show nonlinear stress-strain behaviour due to intralaminar shear loading. The determination of the in-plane shear stiffness and strength for this class of material is difficult and common test standards and methods of analysis are partially inaccurate. The identification of the in-plane shear properties was made with an especial designed “picture frame test device” which enables shear loading up to 950N/mm. Therefore the strength limit can be reached at specimens with adequate thickness and a high safety factor against buckling. Due to the chosen design the maximum of the shear loading and the final failure occur in the centre of the specimen. The experiments match with the numerical analysis.
The one-phase methods described in Chapter 2 were shown to be able to predict casting to some extent, but could not depict segregation, sedimentation and blockage occurring during flow. On the other hand, the distinct element methods described in Chapter 3 did not take into account the presence of two phases in the system and describes concrete as distinct elements interacting through more or less complex laws. A reliable numerical model of a multiphase material behaviour shall take into account both phases (solid and liquid). From the numerical point of view, concrete flow shall be seen therefore as the free surface flow of a highly-concentrated suspension of rigid grains.
The roles of microalloying niobium, titanium and vanadium for controlling austenite grain growth, microstructure evolution and hardness were investigated at different simulated heat affected zones (HAZ) for high strength low alloy (HSLA) S690QL steel. High resolution FEG-SEM has been used to characterize fine bainitic ferrite, martensite and nanosized second phases at simulated coarse and fine grain HAZs. It was found that for Ti bearing steel (Ti/N ratio is 2) austenite grain had the slowest growth rate due to the presence of most stable TiN. The fine cuboidal particles promoted intragranular acicular ferrite (IGF) formation. Nb bearing steel exhibited relatively weaker grain growth retardation compared with titanium bearing steels and a mixed microstructure of bainite and martensite was present for all simulated HAZs. IGF existed at coarse grain HAZ of Ti+V bearing steel but it was totally replaced by bainite at fine grain HAZs. Hardness result was closely related to the morphology of bainitic ferrite, intragranular ferrite and second phases within ferrite. The microstructure and hardness results of different simulated HAZs were in good agreement with welded experimental results.
The term „Alternative Solvents“ often refers to ionic liquids (ILs), mainly to distinguish these substances from traditional (i.e., molecular) solvents.
In applications, any „alternative“ is required to perform better than something that is proven and tested.
To bring ILs into practical use, availability and costs are the fundamental points to be addressed.
There are two ways to proceed:
▬ tailoring a molecule, implanting the expected characteristics
advantage: optimization of the targeted performance possible
risks: outcome not always foreseeable, costly and time-intensive (“trial and error“)
▬ to target on mixtures of well-characterized ILs with molecular solvents
advantage: substance characteristics are known, less costly, less time-consuming,
mixture composition another tunable parameter
risks: the same but with less impact
For the basic engineering of technical processes, knowledge of phase equilibria, particularly of
mixtures, over a broad (p,T) range is mandatory.
This contribution reports on recent experimental results from our laboratory:
▬ the solubility of CO2 in a mixture of water and [bmim][CH3SO4]
▬ the solubility of CO2 in a mixture of methanol and [bmim][PF6]
Thermally reduced graphite oxide (TRGO), containing only four single carbon layers on average, was combined with ammonium polyphosphate (APP) and magnesium hydroxide (MH), respectively, in polypropylene (PP). The nanoparticle's influence on different flame-retarding systems and possible synergisms in pyrolysis, reaction to small flame, fire behavior and mechanical properties were determined. TRGO has a positive effect on the yield stress, which is decreased by both flame-retardants and acts as a synergist with regard to Young's modulus. The applicability and effects of TRGO as an adjuvant in combination with conventional flame-retardants depends strongly on the particular flame-retardancy mechanism. In the intumescent system, even small concentrations of TRGO change the viscosity of the pyrolysing melt crucially. In case of oxygen index (OI) and UL 94 test, the addition of increasing amounts of TRGO to PP/APP had a negative impact on the oxygen index and the UL 94 classification. Nevertheless, systems with only low amounts (≤1 wt%) of TRGO achieved V-0 classification in the UL 94 test and high oxygen indices (>31 vol%). TRGO strengthens the residue structure of MH and therefore functions as a strong synergist in terms of OI and UL 94 classification (from HB to V-0).
-Background-
Laboratory leaching tests on treated wood were performed during a European robustness study in the framework of the validation of a tank leaching test procedure that has been proposed for construction products in order to determine the potential release of dangerous substances which can be transferred to soil and groundwater. The release of substances has to be determined also for materials treated with biocidal products according to the requirements of the European Biocidal Products Regulation. A similar leaching test procedure was already harmonised for treated wood for this purpose. Both test procedures were applied in parallel to wood treated with the same preservative to investigate whether the results of these tests can replace each other. Additional experiments were performed to further investigate unexpected effects of L/A ratio on leaching of copper and duration of storage of treated test specimens.
-Results-
Both procedures generate similar results concerning cumulative emissions of tebuconazole, copper, dissolved organic carbon and total nitrogen. The emission rates with time are in comparable ranges for both leaching protocols. Emissions of copper increased with decreasing L/A ratios. Strong correlation of copper concentrations and dissolved organic carbon as well as total nitrogen concentrations in eluates indicates that this observation is caused by co-elution of copper with organic substances. Duration of storage of treated test specimens affected emissions for the investigated wood preservative.
-Conclusions-
Based on these findings, results from both test procedures can be used to describe leaching characteristics and avoid double testing of treated wood to fulfil the requirements of the European regulations for either biocides or construction products. Leaching of substances from treated wood is a complex process that depends on its chemical composition and ageing processes.
The most successful additive manufacturing (AM) technologies are based on the layer-by-layer deposition of a flowable powder. Although considered as the third industrial revolution, one factor still limiting these processes to become completely autonomous is the often necessary build-up of support structures. Besides the prevention of lateral shifts of the part during the deposition of layers, the support assures quality and stability to the built process. The loose powder itself surrounding the built object, or so-called powder-bed, does not provide this sustenance in most existent technology available. Here we present a simple but effective and economical method for stabilizing the powder-bed, preventing distortions in the geometry with no need for support structures. This effect, achieved by applying an air flow through the powder-bed, is enabling an entirely autonomous generation of parts and is a major contribution to all powder-based additive manufacturing technologies. Moreover, it makes powder-based AM independent of gravitational forces, which will facilitate crafting items in space from a variety of powdery materials.
The determination of the fatigue life in technical alloys containing large and small defects must rely on a propagation model which accounts for short and long crack growth. Recently an analytical model which incorporates propagation in the short crack regime and plastic correction for the crack driving force has been presented by two of the authors.
This work is intended to show further validation of the model, taking into account data sets for different materials with different testing conditions.
Despite the assumptions about missing parameters, the value of which had to be taken from the literature, the predictions showed a fairly good approximation of the fatigue lives. A possible interpretation of the results in terms of multiple crack initiation and propagation at higher loads is proposed.