The study deals with the influence of the heat input on the thermal cycles and Charpy impact toughness for hybrid laser-arc welding of 25 mm thick structural steel S355J2 using a 20-kW high-power laser in combination with an electromagnetic weld pool support. The main focus is on the change of the mechanical properties over the entire seam thickness. The cooling times were measured using a pyrometer in combination with an optical fibre in three different locations near to fusion lines corresponding to different heights of the seam. Also, Charpy impact specimens were taken from different parts of the weld joint corresponding to the different heights. The influence of the heat input was investigated for 1.8 kJ mm-1 and 3.2 kJ mm-1. Despite the observed decreased values of both t8/5-cooling time and the Charpy impact toughness in the root part of the seam, the required values could be reached in dependance on applied heat input.
It is already known that the laser beam welding (LBW) or hybrid laser-arc welding (HLAW) processes are sensitive to manufacturing tolerances such as gaps and misalignment of the edges, especially at welding of thick-walled steels due to its narrow beam diameter. Therefore, the joining parts preferably have to be milled. The study deals with the influence of the edge quality, the gap and the misalignment of edges on the weld seam quality of hybrid laser-arc welded 20 mm thick structural steel plates which were prepared by laser and plasma-cutting. Single-pass welds were conducted in butt-joint configuration. An AC magnet was used as a contactless backing. It was positioned under the workpiece during the welding process to prevent sagging. The profile of the edges and the gap between the workpieces were measured before welding by a profile scanner or a digital camera, respectively. With a laser beam power of just 13.7 kW, the single-pass welds could be performed. A gap bridgeability up to 1 mm at laser-cut and 2 mm at plasma-cut samples could be reached respectively. Furthermore, a misalignment of the edges up to 2 mm could be welded in a single-pass. The new findings may eliminate the need for cost and time-consuming preparation of the edges.
-Elektromagnetische Schmelzbadstütze wurde beim
Laserhybridschweißen von Dickblechen erfolgreich zur
Unterdrückung der Tropfenbildung eingesetzt
-Auch bei „schlechteren“ Kantenqualitäten konnten einlagige
Schweißnähte mit hoher Qualität erzielt werden
-Spaltüberbrückbarkeit bis zu 2 mm (bei plasmageschnittenen
Proben) konnte gewährleistet werden
-Homogenere Verteilung des Zusatzwerkstoffes wurde erzielt