High-strength structural steels are used in machine, steel, and crane construction with yield strength up to 960 MPa. However, welding of these steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of microstructure, local stress/strain, and local hydrogen concentration. In addition to the three main factors, the used arc process is also important for the performance of the welded joint. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of high-strength steel grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been increasingly used for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared with the Conv. A. Economic benefits of using this arc type are a reduction of necessary weld beads and required filler material. In the present study, the susceptibility to HAC in the heat-affected zone (HAZ) of the high-strength structural steel S960QL was investigated with the externally loaded implant test. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. Both conducted test series showed same embrittlement index “EI” of 0.21 at diffusible hydrogen concentrations of 1.3 to 1.6 ml/100 g of arc weld metal. The fracture occurred in the HAZ or in the weld metal (WM). However, the test series withMod. SA showed a significant extension of the time to failure of several hours compared with tests carried out with Conv. A.
High-strength steels with yield strength of 960 MPa are susceptible to hydrogen-assisted cracking (HAC) during welding processing. In the present paper, the implant test is used to study HAC in a quenched and tempered steel S960QL and a high-strength steel produced by thermo-mechanical controlled process S960MC. Welding is performed using the gas metal arc welding process. Furthermore, diffusible hydrogen concentration (HD) in arc weld metal is determined. Based on the implant test results, lower critical stress (LCS) for complete fracture, critical implant stress for crack initiation, and embrittlement index (EI) are determined. At HD of 1.66 ml/100 g, LCS is 605 MPa and 817 MPa for S960QL and S960MC, respectively. EI is 0.30 and 0.46 for S960QL and S960MC, respectively. Fracture surfaces of S960QL show higher degradation with reduced deformation. Both, higher EI of S960MC and fractography show better resistance to HAC in the HAZ of S960MC compared to S960QL.
Effect of weld penetration depth on hydrogen-assisted cracking of high-strength structural steels
(2019)
The need for steels with highest mechanical properties is a result of the increasing demands for energy and resource efficiency. In this context, high-strength structural (HSS) steels are used in machine, steel and crane construction with yield strength up to 960 MPa. However, welding of HSS steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of (1) microstructure, (2) local stress/strain and (3) local hydrogen concentration. In addition to the three main factors, the used weld-arc process is also important for the performance of the welded joint, especially when using modern arc variants. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of HSS grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been used increasingly for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared to the conventional process. Economic benefits of using this arc type are: a reduced number of necessary weld beads and a lower weld seam volume, which result in decreased total welding time and costs. Nonetheless, investigations on a high-strength S960QL showed significantly higher hydrogen concentrations in the weld metal at a reduced seam opening angle with Mod. SA. This indicates an increased susceptibility of the welded component to HAC. Hence, existing recommendations on HAC-avoidance cannot be transferred directly to the Mod. SA-process. In the present study, the susceptibility to HAC of the HSS steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded implant test was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). However, the test series with Mod. SA showed a significant extension of the time to failure of several hours compared to tests carried out with Conv. A.