Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (15)
- Beitrag zu einem Tagungsband (10)
- Zeitschriftenartikel (7)
- Monografie (2)
- Buchkapitel (1)
- Forschungsbericht (1)
Referierte Publikation
- nein (36) (entfernen)
Schlagworte
- Additive Manufacturing (7)
- Fatigue (4)
- Fracture Mechanics (4)
- Additive manufacturing (3)
- Cyclic R-curve (3)
- Fatigue life (3)
- Fatigue strength (3)
- Fracture mechanics (3)
- Kitagawa-Takahashi diagram (3)
- Residual stress (3)
- AlSi10Mg (2)
- Bauteilauslegung (2)
- Bruchmechanik (2)
- Diffraction (2)
- Endurance limit (2)
- Experimental procedure (2)
- Fail-safe (2)
- Failure Assessment Diagram (2)
- Fatigue crack propagation threshold (2)
- L-PBF (2)
- Microstructure (2)
- Residual Stress (2)
- Short crack (2)
- Steel 316L (2)
- Structural Integrity (2)
- Turbine disk (2)
- Weldments (2)
- 316L (1)
- AISI 316L (1)
- Acero 316L (1)
- Acero alta resistencia (1)
- Achsschenkel (1)
- AlSi10Mg alloy (1)
- Analytisches Modell (1)
- Bainitischer Schmiedestahl (1)
- Bauteilbewertung (1)
- Betriebsfestigkeit (1)
- Bruch (1)
- Bruchmechanische Auslegung (1)
- Bruchmechanische Kennwerte (1)
- Bruchmechanische Konzepte (1)
- Burst (1)
- Component Assessment (1)
- Component assessment (1)
- Constraint (1)
- Constraint faktor (1)
- Crack Tip Opening Displacement (CTOD) (1)
- Crack closure effect (1)
- Crack propagation (1)
- Crack propagation resistance (1)
- Crack-closure (1)
- Crack-tip constraint (1)
- Curvas FCGR (1)
- Cyclic J-integral (1)
- Cyclic R-Curve (1)
- Cyclic R-curve analysis (1)
- Damage Tolerance (1)
- Damage tolerance (1)
- Defects (1)
- Determinación Kth intrínseco (1)
- EA4T railway axle steel (1)
- Effective crack propagation data (1)
- Einflussfaktoren auf Rissfortschrittsdaten (1)
- Environmental conditions (1)
- FEM (1)
- Fabricación Aditiva (1)
- Fatigue Crack Propagation (1)
- Fatigue S-N curve (1)
- Fatigue assessment (1)
- Fatigue crack propagation (1)
- Fatigue crack propagation stagesdefects (1)
- Fatigue lifetime prediction (1)
- Fatigue limit (1)
- Fatigue properties (1)
- Finite Element Analysis (1)
- Fit4AM (1)
- HAZ (1)
- HCF (1)
- Heat treatment (1)
- High strength steel (1)
- IBESS-Prozedur (1)
- Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- J-Integral (1)
- Kerbschlagarbeit (1)
- Korrelation (1)
- Kritische Last (1)
- LCF (1)
- Laser powder bed fusion (1)
- Ligamentplastifizierung (1)
- Mecánica de Fractura (1)
- Mismatch (1)
- Overspeed (1)
- PBF-LB/M (1)
- Predicción vida a fatiga (1)
- Probabilistic Assessment (1)
- Probetas miniatura (1)
- Process Monitoring (1)
- Process Simulation (1)
- Recomendaciones procedimiento de ensayo (1)
- Representative Specimens (1)
- Residual Stresses (1)
- Restlebensdauer (1)
- Rissausbreitung (1)
- Rissschließeffekte (1)
- Rissschließfunktion (1)
- Rissspitzenbelastung (1)
- Risswiderstand (1)
- S-N diagram (1)
- Schadenstolerante Bauteilauslegung, (1)
- Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Short crack Propagation (1)
- Sicherheit (1)
- Small-scale specimens (1)
- Stretch-Zone (1)
- Structural integrity (1)
- Struktur Integrität (1)
- Tensile properties (1)
- Turbinenscheibe (1)
- miniature specimens; FCGR curves; intrinsic threshold (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (36) (entfernen)
Eingeladener Vortrag
- nein (15)
Die neue Generation von bainitischen Schmiedestählen bietet auf der einen Seite ein erhebliches Festigkeitspotenzial, das es im Sinne des Leichtbaus auch für zyklisch belastete Sicherheitsbauteile zu heben gilt. Auf der anderen Seite geht mit dieser Festigkeitssteigerung im Vergleich zu Vergütungsstählen ein Verlust an Duktilität und Zähigkeit einher. Am Beispiel des Demonstratorbauteils Achsschenkel ging das Forschungsvorhaben der Frage nach, wie ein Freigabeprozess zu gestalten ist, damit das Festigkeitspotenzial der neuen Stähle zuverlässig ausgenutzt werden kann. Als Ergebnis wird eine Vorgehensweise dargestellt, die den Eigenschaften der neuen Generation von Schmiedestählen Rechnung trägt, um den sicheren Betrieb der Komponenten zu gewährleisten.
The process-structure-property-performance relationship is a fundamental paradigm in metal additive manufacturing (AM). The knowledge of how process parameters and post-process treatments influence the material properties and therefore the structural integrity of additively manufactured metallic components is of paramount importance. With respect to this, one of the unsolved problems related to the unique AM process is the reliability of witness samples for part qualification. Focusing on the Laser Powder Bed Fusion (PBF-LB/M) process, the microstructure and therefore the mechanical performance of test coupons are not representative of parts of the same material in every case. This work summarizes part of the results of an ongoing cooperation between BAM and BASF, which aims at addressing this issue by designing dedicated specimens, representative of the fatigue properties of the real component. The considered case study consisted in the fabrication and characterization of the fatigue properties of a pressure vessel made of AISI 316L. The first phase of the project was devoted to the process monitoring to understand the relationship between process parameters and temperature distribution during the fabrication of the component. Finite element models were tuned on the experimental data from the process monitoring and simulations of the temperature field in the component were conducted. The numerical results were in good agreement with the temperature profiles measured during the fabrication of the component. The second phase dealt with the evaluation of the fatigue and fatigue crack propagation properties on specimens extracted from different regions of the pressure vessel. The experimental investigations showed significant differences in hoop and longitudinal direction. A clear dependence of the fatigue properties on heat accumulation (temperature distribution) and defect size was pointed out. The third phase encompassed the fabrication and testing of the representative specimens. Numerical simulations were used to design specimens displaying the same temperature profile as in the most critical region of the component. The fatigue testing of the representative specimens is subject of ongoing work.
The Kitagawa-Takahashi (KT) diagram is a well-established tool in the fatigue community for the prediction of the fatigue limit of metallic materials in presence of defects. Nevertheless, its determination is associated with a large number of fatigue tests carried out on specimens with artificial defects (notches) to describe the fatigue limit-defect size relationship in the short crack regime. The preparation of the specimens and the execution of the tests is time expensive. Therefore, few phenomenological models have been introduced in the past to provide a first approximation of the KT diagram based solely on the fatigue limit for smooth specimen and the fatigue crack propagation threshold for long cracks. Despite the use of such models is widely spread, these suffer from problems related to the uncertainties of the material parameters. Furthermore, the mechanics of short cracks, which is the physical mechanism behind the concept of the fatigue limit, is not considered. This work discusses the advantages and drawbacks of using short fatigue crack propagation models for predicting the fatigue limit of flawed metallic materials. The KT diagrams for a EA4T railway axle steel in as-received and full-hardened condition are approximated by means of the cyclic R-curve method.
Structural alloys are largely employed in key industrial sectors and their demand is predicted to rise rapidly for the next decades. Most of these materials require a large amount of energy for extraction and manufacturing, which causes the emission of greenhouse gases and other pollutants. Therefore, strategies for improving the sustainability of structural metallic alloys are urgently needed.
Additive Manufacturing (AM), in particular Laser Powder Bed Fusion (PBF-LB/M), aims to be a sustainable manufacturing process, as it allows the build-up of complex geometry in near net-shape from 3D models, while minimizing material waste and the energy required for the process and post-process treatments.
Nevertheless, the application of additively manufactured parts in structural safety-relevant applications is still hindered by the poor fatigue performance. The cause of this has been mainly attributed to the presence of manufacturing defects and surface roughness. Therefore, a huge effort has been made to optimize the process parameters and to introduce post-process treatments to minimize the defect content. However, material flaws cannot be fully eliminated, but these can be considered in a damage tolerance framework for the prediction of the fatigue performance of additively manufactured metallic materials, which is essential for part design and qualification.
This work aims at presenting different modelling strategies for the prediction of the fatigue limit of AM metals. Simple empirical models and more complex models based on fatigue short crack propagation are proposed. The investigated material is an AlSi10Mg alloy fabricated by PBF-LB/M and subjected to two different low-temperature heat-treatments (265°C for 1 h and 300°C for 2h). The results show that the models can provide good approximation of the fatigue limits and help in the interpretation of the scatter of fatigue data.
Die Anwendung bruchmechanischer Methoden zur schadenstoleranten Bauteilauslegung ist für zyklische Lasten im Bereich der Paris-Geraden Stand der Technik. Technisch relevant sind jedoch häufig geringere Lasten im Schwellenwertbereich der d𝑎/d𝑁-Δ𝐾-Kurve. Aufgrund des großen Einflusses von Rissschließeffekten ist dessen Bestimmung jedoch nicht nur aufwändig, sondern auch potenziell fehlerbehaftet. Die Bauteilauslegung erfolgt zweckmäßigerweise auf der Basis effektiver, d. h. rissschließkorrigierter Rissfortschrittsdaten. Von großer Bedeutung ist auch der intrinsische Schwellenwert, unterhalb dessen keine Risserweiterung mehr eintritt. In diesem Forschungsprojekt erfolgte eine Untersuchung des Einflusses verschiedener Prüfverfahren und Umgebungsbedingungen auf die Ermittlung des Schwellenwerts gegen Ermüdungsrissausbreitung Δ𝐾th. Es wurden statistisch abgesicherte Empfehlungen zur experimentellen Ermittlung des intrinsischen Schwellenwerts Δ𝐾th,eff abgeleitet. Dieser dient auch als Eingangsparameter einer weiterentwickelten Prozedur zur Bauteilauslegung auf der Basis bei einem Lastverhältnis von 𝑅 ≈ 0,8 ermittelter, effektiver, Rissfortschrittsdaten. Es zeigte sich, dass die bei einem Lastverhältnis von 𝑅 ≈ 0,8 in Laborluft bei höherer Prüffrequenzen (≥90 Hz) ermittelten Schwellenwerte eine konservative Abschätzung des intrinsischen Schwellenwerts erlaubten. Bei Lastverhältnissen 𝑅 ≪ 0,8 wurde ein teilweise stark ausgeprägter Einfluss extrinsischer Effekte auf das Rissfortschrittsverhalten festgestellt. Eine Untersuchung der Bruchflächen ergab Oxidschichtdicken in der Größenordnung mehrerer hundert Nanometer. Bei Reduktion der Prüffrequenz auf ≈55 Hz und Prüfung in feuchter Luft (60 % r.F. und 80 % r.F.) konnte auch bei 𝑅 = 0,8 Rissschließen beobachtet werden. Die weiterentwickelte Prozedur zur Bauteilauslegung auf Basis effektiver Rissfortschrittsdaten lieferte aber stets konservative Ergebnisse in einem tolerierbaren Fehlerbereich und ist deshalb zur Anwendung geeignet. Die im Projekt gewonnenen Erkenntnisse tragen zu einer robusten Bauteilauslegung auf bruchmechanischer Basis bei. Der stark reduzierte Versuchsumfang bei Nutzung effektiver Rissfortschrittsdaten gegenüber der Ermittlung von spannungsverhältnisabhängigen Rissfortschrittskurven beschleunigt und vereinfacht die Bauteilauslegung auf Basis bruchmechanischer Methoden.
Fraucture mechanics-based probablistic structural integrity assessment for aero-engine turbine disk
(2023)
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The aim of this work is to present part of a fracture mechanics-based probabilistic assessment procedure under development which aims at calculating the critical rotational speed of the turbine disk based on the numerical-analytical solutions and regulations for the failure probability. In particular, the rim-peeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of J-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. The analytical solutions to calculate the crack driving force for the lab representative specimen are used for the Monte Carlo simulations, the result of which has been assessed in the form of a Failure Assessment Diagram (FAD). The results of the probabilistic structural integrity assessment show good agreement between Monte Carlo simulations and certification values for the disk in terms of expected failure mode and value of the critical speed.
The fatigue assessment of welded joints requires several input data, which can be subdivided into three categories: geometry, material and loading. The number of input data depends essentially on the complexity of the models employed and on the level of accuracy of the analysis. It is common practice to use safety factors in design to account for the scatter of the input parameters. Nevertheless, overly-conservative factors lead often to unrealistic estimations of fatigue life. This work presents a fracture mechanics-based model for the structural integrity assessment of welded joints under constant amplitude fatigue loading, in which the local geometry at the weld toe and the fatigue crack growth properties are considered statistically distributed. The approach is validated against a large number of experimental data.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of 𝐽-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest 𝐽 -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. In addition, probabilistic aspects are also considered in the calculations.
The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation.
Bei der Auslegung von Achsschenkeln für Nutzfahrzeuge wird für den Überlastfall ein fail-safe-Kriterium (kontrolliertes Versagen) als Basisphilosophie angesetzt. Gefordert wird, dass sich der Achsschenkel auch unter Akzeptanz begrenzten Risswachstums hinreichend elastisch-plastisch verformen kann, ohne dass es zum Bruch kommt. Der Fahrer soll anschließend anhand der bleibenden Verformungen bemerken können, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Eine Voraussetzung für dieses Bauteilverhalten ist eine hinreichende Bruchzähigkeit des Werkstoffs. Diese, wie auch die Rissspitzenbeanspruchung, müssen ermittelt werden, um den bruchmechanischen Sicherheitsnachweis führen zu können. Zur Ermittlung der mechanisch-technologischen und bruchmechanischen Werkstoffeigenschaften wurde ein Prüfkonzept entwickelt, bei dem die Proben an der potenziell kritischen Stelle direkt aus den geschmiedeten Achsschenkeln entnommen werden. Die experimentelle Werkstoffcharakterisierung bildet dann die Beanspruchungsbedingungen beim Überlastereignis ab. Im Rahmen der Produktion stehen jedoch nur Kerbschlagarbeitswerte zur Verfügung und aufwändige bruchmechanische Versuche sollen vermieden werden. Deshalb wurde eine Korrelation zur Abschätzung der vorhandenen Bruchzähigkeit aus der Kerbschlagarbeit herangezogen. Es ergibt sich eine Ergebnismatrix, die die Einflussgrößen Versagenswahrscheinlichkeit, Temperatur und Bruchzähigkeit verknüpft. Abschließend wird ein erster Vergleich der abgeschätzten mit den experimentell ermittelten Bruchzähigkeitswerten gezogen. Dieser weist aus, dass die abgeschätzten Werte geringfügig konservativ sind.
Die sichere Auslegung von Bauteilen kommt an der Anwendung bruchmechanischer Methoden heute nicht mehr vorbei. Das vorliegende Buch bietet eine Einführung in diese Methoden mit besonderen Schwerpunkten auf dem aktuellen Stand der bruchmechanischen Kennwertermittlung und den Methoden der analytischen bruchmechanischen Bauteilbewertung. Es beschreibt die Mechanismen von Risswachstum und Bruch, die grundlegenden Konzepte der Bruchmechanik, die analytische Ermittlung der Rissspitzenbelastung in Bauteilen sowie die Anwendung der Bruchmechanik in unterschiedlichen Kontexten. Der Schwerpunkt liegt dabei auf der praktischen Anwendung u. a. anhand von Demonstrationsbeispielen, die im Detail nachvollzogen werden können.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on productionsimilar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rimpeeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of -integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations.
The largest percentage of component life under fatigue loading conditions is spent in the short crack regime and in the initial phase of long cracks. The use of Fracture Mechanics in the characterization of fatigue crack growth rate curves has proven to be a useful and adequate tool in the prediction of fatigue lifetimes as long as certain conditions are satisfied. All the above implies the need for a methodical and accurate procedure of assessment of the material response in order to achieve a reliable prediction of lifetime in components under safe conditions, based on the damage tolerance approach. It also highlights the need to analyse the response of increasingly reduced thicknesses, which, as time goes by, show greater differences with respect to those commonly studied and defined in standards and design guidelines, as well as to the experimental studies that can be found in the literature at present. Some examples of thin-walled components are turbine blades or certain additively manufactured parts where, additionally, variations in material properties can occur locally and should also be examined.
Se presenta una guía completa del procedimiento experimental para la determinación del valor umbral ΔKth intrínseco y caracterización de curvas FCGR sobre el acero de alta resistencia S960QL empleando probetas de pequeña escala. El análisis se realiza comparando probetas SENB de diferentes geometrías, distinguiendo entre “convencionales” y “miniatura”. Las primeras con espesor (B) de 6 mm y anchura (W) de 19, y las segundas con B = 3 y dos valores distintos de W, 4 y 6 mm. A fin de identificar el valor umbral ΔKth intrínseco, la relación de cargas (R) aplicada en todos los ensayos fue 0,8. La técnica de caída de potencial (DCPD) se utilizó para la monitorización del tamaño de grieta a lo largo de los ensayos.
La evaluación de los resultados experimentales confirma la equiparación de resultados entre las distintas geometrías y configuraciones de ensayo practicadas, así como la viabilidad de emplear probetas de pequeña escala en la determinación del valor umbral ΔKth intrínseco. Esto abre nuevas perspectivas en lo relativo al empleo de probetas de reducidas dimensiones en la caracterización de materiales a fatiga. A su vez, permite ofrecer una serie de recomendaciones para reproducir con éxito ensayos semejantes utilizando probetas de pequeñas dimensiones de acero y otros materiales metálicos.
La tecnología de fabricación aditiva (AM) continúan progresando y permitiendo alcanzar diseños cada vez más complejos y optimizados. La industria química es uno de los sectores donde componentes AM han adquirido un gran interés. La falta hasta la fecha de una directiva europea que regule la inspección, certificación y aceptación de equipos sometidos a presión hace necesario progresar en esta línea. El objetivo que se persigue en este trabajo es el de desarrollar una metodología de diseño sobre componentes fabricados aditivamente basada en la estimación de vida a fatiga de las zonas más susceptibles de sufrir dicho tipo de fallo. El estudio comprende diversas facetas de análisis, simulaciones numéricas, análisis de la microestructura del material y una extensa campaña experimental. La evaluación de la integridad estructural se realiza aplicando mecánica de fractura. La historia térmica a lo largo del proceso de fabricación determina la microestructura del componente en cada región y, por ende, influye en las propiedades mecánicas en cada una. Se presentan los resultados preliminares de un proyecto de investigación en curso dirigido a la caracterización de propiedades mecánicas en recipientes de presión producidos por fusión láser en lecho de polvo (L-PBF, por sus siglas en inglés) de acero inoxidable 316L. Se detallan los resultados preliminares en términos de velocidad de crecimiento de grietas por fatiga (FCGR), y se comparan los resultados de probetas extraídas de diferentes regiones de los depósitos.
Design methodology of vessel produced by L PBF stainless steel using representative specimens
(2022)
This work presents the preliminary results of an ongoing project with a double objective: on the one hand, the characterisation of the mechanical properties against fatigue damage of an additively manufactured 316 stainless steel produced by laser powder bed-based (L-PBF) technology; on the other hand, the implementation of numerical simulation techniques able to predict the mechanical behaviour of the material in order to optimise and reduce the design costs of vessels used in the chemical sector. The current state of the work developed in this research framework allows showing the first batch of experimental results of crack propagation rate (FCGR) and high cycle fatigue (HCF) tests. The geometry of the vessels studied presents three clearly differentiated regions, either in terms of thickness (11-15 mm) or concerning the inclination of the walls to the direction of manufacturing (0º - 45º). The experimental campaign carried out so far allows identifying the differences in behaviour when comparing different extraction locations around the vessel. This is due to the variations in thermal cycles that the deposited material undergoes during the manufacturing process. Therefore, this causes variations in the microstructure which lead to changes in the response of the material. In this work, these differences are analysed qualitatively and quantitatively from the results of FCGR and HCF, thus allowing to locate the regions with the highest risk in terms of structural integrity against fatigue. This preliminary phase together with the numerical simulation of the additive manufacturing process are key to achieving a reliable description and modelling of the material. The latter will make it possible to address the priority aim of this project, involving the manufacture of independent samples whose properties are representative of the original material extracted from the reference vessels. It is, therefore, a comprehensive methodology for the design of additively manufactured components based on the localised fatigue mechanical properties of representative specimens.
This plenary lecture aims at showing the progress in the experimental determination of the fatigue propagation resistance in metals and its application to fatigue assessment. In particular, different new experimental techniques are introduced, which allow a better description of the crack propagation resistance from short to long crack regime. These data can be then applied in the fatigue assessment to predict the fatigue limit and the total life of metallic components.
The damage tolerance approach is widely used in the design and estimation of inspection intervals of safety-relevant metallic components subject to fatigue loading. The approach relies on the knowledge of the fatigue crack propagation characteristics, wherein a relevant role is played by the fatigue crack propagation threshold. Nevertheless, the use of material data determined by testing on conventional specimens is not straightforward in the case of thin-walled components such as turbine blades or additively manufactured parts, in which the local variation of material properties in highly stressed regions must be considered. In these cases, the possibility of investigating the fatigue crack propagation properties on a limited portion of material is crucial. For this purpose, a new test procedure has been developed for small-scale specimens which allows the determination of the intrinsic fatigue crack propagation threshold and the near-threshold regime. The validity and limitations of the method are demonstrated on the high strength steel S960QL, along with a comparison with data determined by testing on conventional geometries.
Additive manufacturing (AM) is becoming increasingly important in engineering applications due to the possibility of producing components with a high geometrical complexity allowing for optimized forms with respect to the in-service functionality. Despite the promising potential, AM components are still far from being used in safety-relevant applications, mainly due to a lack of understanding of the feedstock-process-properties-performance relationship. This work aims at providing a full characterization of the fatigue behavior of the additively manufactured AISI 316L austenitic stainless steel and a direct comparison with the fatigue performance of the wrought steel. To this purpose, a set of specimens has been produced by laser powder bed fusion (L-PBF) and subsequently heat treated at 900 °C for 1 hour for complete stress relief, whereas a second set of specimens has been machined out of hot-rolled plates. Low cycle fatigue (LCF) and high cycle fatigue (HCF) tests have been conducted for characterizing the fatigue behavior. The L-PBF material had a higher fatigue limit and better finite life performance compared to wrought material. Both, LCF and HCF-testing revealed an extensive cyclic softening.
Al-Si alloys produced by Laser Powder Bed Fusion (L-PBF) techniques allow the fabrication of lightweight free-shape components that find space in aerospace, automotive, biomedical and military applications. Due to the high cooling rates occurring during the building process, L-PBF AlSi10Mg alloys exhibit an ultra-fine microstructure that leads to superior mechanical properties in the as-built condition compared to conventional cast Al-Si materials. Nevertheless, L-PBF processing induces high thermal gradients, leading to deleterious residual stress levels that must be considered to avoid part distortion and unpredicted failures. In order to relax detrimental residual stress and to increase the ductility, post-processing stress relief treatments are generally performed. In as-built condition the hypoeutectic AlSi10Mg microstructure consist of fine α-Al cells containing uniformly dispersed silicon nanoparticles, which are, in addition, surrounded by a eutectic Si network. Above 260°C the silicon interconnectivity starts to breakdown into spheroidized particles and to coarsen. At the same time, the heating residual stresses are relieved.
The objective of the contribution is to investigate, under different heat treatment conditions, the evolution of microstructure and residual stresses in view of optimizing the fatigue performance of the alloy. To this purpose various heat treatments in a range of temperatures between 265°C and 300°C for a duration between 15 minutes and 2 hours are performed. The microstructure modifications are analysed using a scanning electron microscope and the residual stress state is measured by laboratory X-ray diffraction.