Polyether and -ester urethanes (PU) were exposed to artificial weathering at 40 °C and artificial UV radiation in a weathering chamber. In 3 parallel exposures, humidity was varied between dry, humid, and wet conditions. Material alteration was investigated by various analytical techniques like size exclusion chromatography
(SEC), liquid chromatography-infrared spectroscopy (LC-FTIR), thermal-desorption gas chromatography-mass spectrometry (TD-GC-MS), fluorescence mapping and dynamic mechanical analysis (DMA). Our results show that depending on the weathering conditions, different degradation effects can be observed. By means of SEC an initial strong decrease of the molar masses and a broadening of the mass distributions was found. After a material dependent time span this was followed by a plateau where molar mass changes were less significant. A minor moisture-dependent degradation effect was only found for polyester PU. Fluorescence measurements on two materials revealed an increase in the luminescence intensity upon weathering process reaching a saturation level after about 500 h. The changes in the optical properties observed after different exposure conditions and times were very similar. The TD-GC-MS data showed the fate of the stabilizers and antioxidant in the course of weathering. LC-FTIR measurements revealed a change in peak intensities and the ratio of urethane and carbonyl bands.
Einfluss einer druckschwellinduzierten Degradation von Fahrbahndeckenbeton auf die schädigende AKR
(2020)
In den letzten Jahren sind im deutschen Bundesautobahnnetz verstärkt Schäden an vor 2005 errichteten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Neben dem AKR-fördernden Einfluss von alkalihaltigen Taumitteln werden Fahrbahndecken zyklischen mechanischen Belastungen infolge des Verkehrs und Zwangsspannungen durch klimatische Einwirkungen ausgesetzt. Solche mechanischen Belastungen werden bisher in keinem AKR-Prüfverfahren berücksichtigt. Die zyklischen Belastungen können zu einer Degradation des Betongefüges führen, die ggf. einen AKR-fördernden Einfluss hat. Dieser Beitrag stellt Untersuchungen vor, die zur Beantwortung der Frage nach dem Einfluss einer zyklischen mechanischen Belastung auf den AKR-Schadensprozess beitragen. Dabei wird der Hypothese nachgegangen, dass die ermüdungsinduzierte Degradation zu einer Erhöhung des Stofftransports führt.
Dieser hat einen Einfluss auf die AKR-Schadensentwicklung, da die Reaktionspartner zunächst zum Reaktionsort transportiert werden müssen. Daher wird angenommen, dass sich mit dem Stofftransport auch die AKR-Schädigung verstärkt. Es werden Betonproben aus typischen Fahrbahndeckenbetonen einer vorgeschalteten zyklischen Druckschwellbelastung ausgesetzt.
Die Degradation infolge der Vorbelastung wird simultan mittels ZfP-Verfahren charakterisiert. Anschließend werden die Auswirkungen der zyklischen Vorschädigung auf den Stofftransport sowie auf die AKR vergleichend an Prüfkörpern ohne und mit Vorschädigung untersucht. Die Ergebnisse lassen den Schluss zu, dass die zyklische Vorschädigung sowohl den Stofftransport als auch die AKR fördert.
The impact fracture behavior of two common high-density polyethylene grades for container applications were intensively studied by the instrumented Charpy impact test after well-defined exposure to UV-irradiation. Individual stages of the impact event, such as crack initiation and crack propagation energy as well as maximum impact load, were investigated from the recorded load–deflection curves. UV-induced material property changes were further investigated by infrared spectroscopy, differential scanning calorimetry, and dynamic-mechanical analysis as well as density measurements. Based on the results of the Charpy impact test, three indicators were identified to describe the extend of photooxidation on high-density polyethylene: (a) a reduced Charpy impact strength—at least to half of its initial value for a distinctly brittle impact fracture, (b) a marked decrease in the crack propagation contribution to the impact strength, and (c) an increase of the brittle features of the fracture surface.
The physical and chemical effects of diesel and biodiesel fuels on two high-density polyethylene (PE-HD) types were investigated. Both semi-crystalline PE-HD are common thermoplastic materials for container and storage tank applications. Biodiesel, a composition of unsaturated fatty acid esters from renewable resources, was chosen as it is regarded a possible green alternative to fossil fuels. The study aims at identifying significant differences between biodiesel and conventional diesel fuels based on the differences in the chemical nature of the two. The physical effects of the fuels on the polymer at first comprises the sorption behavior, i.e. kinetics and final equilibrium concentration. Not only are both fuels absorbed by the amorphous phase of the semi-crystalline PE-HD, they also induce a plasticization effect that modifies the molecular mobility and therefore also the characteristic yielding properties, manifest in the obtained stress-strain curves. The chemical effects related to degradation phenomena is investigated by a long-term storage scenario using partially immersed tensile test specimens in diesel and biodiesel. We were able to confirm the proposed co-oxidation mechanism by Richaud et al. for polyethylene-unsaturated penetrant systems on a larger scale based on practical tensile tests. One of the investigated polyethylene grades subjected to tensile drawing showed a significant loss of plastic deformation and the onset of premature failure after 150 days of storage in biodiesel. Further biodiesel storage showed a systematically reduced elongation at break before necking. None of these effects were observed in diesel. Oxidation of fuels and polymer after progressing storage times were analyzed by the evolution of carbonyl species in FT-IR/ATR spectroscopy.