Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (30)
- Posterpräsentation (15)
- Beitrag zu einem Tagungsband (13)
- Zeitschriftenartikel (9)
- Dissertation (1)
- Forschungsbericht (1)
Schlagworte
- KorroPad (34)
- Korrosion (31)
- Nichtrostender Stahl (30)
- EPR (21)
- Corrosion resistance (20)
- Heat treatment (19)
- Wärmebehandlung (19)
- Korrosionsbeständigkeit (16)
- Lochkorrosion (16)
- Stainless steel (14)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (30)
Ageing at 600 °C (from 0.1 h up to 20 h) leads to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries of the lean duplex stainless steel (LDSS) X2CrNiN22-2. This leads to sensitisation due to chromium depletion and decreased pitting corrosion resistance proven by the results of various electrochemical methods (DL-EPR and determination of CPT, Epit). These results were compared with the KorroPad method, which uses an agar-based gel-electrolyte for the detection of stainless steel surfaces prone to pitting corrosion. However, the standard configuration of the KorroPad showed no differentiation for the various ageing conditions. Therefore, modified versions of the KorroPad with two, five and ten times higher NaCl and potassium ferrocyanide III (K3[Fe(CN)6]) concentrations were successfully used to visualise the behaviour detected by DL-EPR, Epit and CPT. Therefore, the KorroPad method can also detect a microstructure related reduction of pitting corrosion resistance, which can drastically reduce the experimental effort to generate sensitisation diagrams for stainless steels.
Durch eine breite Beteiligung von Schleifmittelherstellern, -anwendern und wissenschaftlichen Einrichtungen im projektbegleitenden Ausschuss (PA) konnte der vielschichtige Themenkomplex „Schleifen“ im Kontext zu den Projektzielen umfassend untersucht werden. Es wurden praxisrelevante Parameterfelder definiert, die eine erfolgreiche Aufklärung der Projektfragestellung ermöglichten.
Im Zuge der Untersuchungen wurde ein signifikanter Einfluss beim Einsatz von Granulatschleifbändern auf das Korrosionsverhalten geschliffener Oberflächen festgestellt. Damit zeigten geschliffene Oberflächen regelmäßig eine schlechtere Korrosionsbeständigkeit als Oberflächen, die mit sonst gleichen Parametern mit einlagig gestreuten Bändern bearbeitet wurden.
Die durch einige Untersuchungsergebnisse aus vorangegangenen AiF-Vorhaben ursprünglich verfolgte These, dass Unterschiede in der Korrosionsbeständigkeit auf die Kornart der Schleifmittel Korund bzw. SiC zurückzuführen ist, konnte nur bedingt bestätigt werden. Bei den systematischen Untersuchungen innerhalb dieses Projektes erwies sich der Einfluss der Kornart im Vergleich zum Einfluss des Schleifbandtyps (Granulat bzw. einlagig gestreutes Korn) als weniger relevant.
Durch weiterführende Untersuchungen konnten auf Oberflächen, die mit Granulatschleifbändern bearbeitet wurden, große Materialaufplattungen aus Eigenmaterial festgestellt werden. Das Eigenmaterial wird dabei im Schleifprozess zunächst abgetragen und aufgrund der Topografie des Schleifbandes zeitweise auf den Bändern festgehalten. Später lösen sich diese Materialanhäufungen vom Band ab und können prozessbedingt durch Wärme- und Krafteinwirkung auf den bearbeiteten Oberflächen aufgeplattet werden. Durch REM und KorroPad Untersuchungen ließen sich Bereiche mit solchen Eigenmaterialaufplattungen eindeutig als wesentliche Ausgangspunkte für Korrosionsprozesse identifizieren. Das aufgeplattete Material ist stark verformt, thermisch beeinflusst und bildet eine Spaltgeometrie zur Bauteiloberfläche aus. Diese Veränderungen führen zur Störung der Passivschichtausbildung in diesen Bereichen und verursachen damit eine erhöhte Korrosionsanfälligkeit der Oberflächen.
Durch gezielte Nachbearbeitungsprozesse ist es möglich, die Eigenmaterialaufplattungen von den Oberflächen zu entfernen. Im Rahmen des Vorhabens wurde dazu eine Nachbearbeitung mittels Schleifvlies geprüft, die zu einer Entfernung der Eigenmaterialaufplattungen und damit zu einer Wiederherstellung der erwarteten Korrosionsbeständigkeit führte. Wird der Endschliff von Oberflächen mit einlagig gestreutem Korn ausgeführt, sind ebenfalls keine korrosionsrelevanten Materialaufplattungen zu erwarten.
Die in einem vorhergehenden AiF Vorhaben IGF 17136 N/1 entwickelte Methode der KorroPad-Prüfung konnte auch hier erfolgreich für die Untersuchung der Auswirkung unterschiedlicher Prozessparameter auf die Korrosionsbeständigkeit der Oberflächen eingesetzt werden. Zudem erwies sich das EPR-SL-Verfahren als ein weiterer Ansatz, um die Passivschichtstabilität verschieden geschliffener Oberflächen vergleichend untersuchen zu können.
Mit den nun vorliegenden Erkenntnissen können kmU künftig durch Anpassungen und Optimierung von Schleifprozessen eine gute Korrosionsbeständigkeit der bearbeiteten Oberflächen sicherstellen. Die Optimierung der Prozessparameter und -schritte kann durch den Einsatz der KorroPad-Prüfung Inhouse erfolgen und somit die laufende Fertigung im Rahmen der Qualitätsprüfung überwacht und dokumentiert werden.
Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit des Duplex-Stahls 1.4062
(2018)
Die Korrosionsbeständigkeit von Schweißverbindungen aus dem Duplex-Stahl 1.4062 wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Oberflächennachbehandlung der Schweißnaht beeinflusst. Je nach zukünftigem Anwendungsbereich und geforderter Korrosionsbeständigkeit wird die Schweißnaht geschliffen, gebeizt, elektropoliert oder gestrahlt, um die beim Schweißen entstandenen Anlauffarben zu entfernen. Gestrahlte Oberfläche sind in der industriellen Praxis häufig anzutreffen, da sie deutlich einfacher und kostengünstiger herzustellen sind als gebeizte oder elektropolierte Oberflächen. Die Auswahl des Strahlmittels bestimmt auch die Prozesskosten, wobei das Strahlen mit Korund effektiver als das Strahlen mit Glasperlen ist. Ziel der Untersuchungen war es festzustellen, ob das Strahlen aus Sicht der Korrosionsbeständigkeit äquivalent zu anderen Nachbehandlungsverfahren ist. Diese Fragestellung wird im Vortrag beantwortet indem geschliffene, gebeizte, mit Korund gestrahlte und mit Glasperlen gestrahlte Schweißverbindungen vergleichend untersucht werden. Die Ergebnisse der Untersuchungen von den Strahlmitteln und den gestrahlten Oberflächen werden mit den Ergebnissen der Salzsprühnebelprüfung, den kritischen Lochkorrosionspotentialen und der KorroPad-Prüfung korreliert.
Einfluss industrieller Korundschleifprozesse auf die Korrosionsbeständigkeit nichtrostender Stähle
(2018)
Im Vortrag werden Ergebnisse des AiF Forschungsvorhabens "Optimierung industrieller Korundschleifprozesse zur Sicherstellung der Korrosionsbeständigkeit nichtrostender Stähle" vorgestellt, die den Einfluss verschiedener Schleifmittel auf die Korrosionsbeständigkeit geschliffener Oberflächen nichtrostender Stähle belegen. Es konnte ein signifikanter Einfluss durch die Verwendung von Granulatschleifbändern nachgewiesen werden, der die Korrosionsbeständigkeit der Oberflächen reduziert. Grund sind auf der Oberfläche zurückbleibende Materialaufplattungen von Eigenmaterial aus dem Schleifprozess. Es wurden unterschiedliche Korrosionsuntersuchungen durchgeführt und durch Oberflächenanalytik im Rasterelektronenmikroskop untermauert.
Normung der KorroPad-Prüfung zum Nachweis lochkorrosionsanfälliger Oberflächen und Werkstoffzustände
(2018)
Mit der KorroPad-Prüfung kann die Lochkorrosionsbeständigkeit nichtrostender Stähle auf sehr einfache, schnelle und kostengünstige Weise eingeschätzt werden. Das KorroPad ist damit für Hersteller, Verarbeiter und Anwender nichtrostender Stähle eine interessante Alternative zu zeitintensiven Langzeitversuchen und komplexen elektrochemischen Untersuchungsmethoden. Die prinzipiellen Funktionsweise der KorroPad-Prüfung wird im Vortrag beschrieben, um anschließend verschiedene Anwendungen vorzustellen. Exemplarisch werden dazu die Bewertung von Schleif-, Strahl- und Passivierungsprozessen, die der Einfluss von Schwefel und die werkstoffbezogene Nachweisgrenze der KorroPad-Prüfung. Abschließend wird auf ein geplantes Vorhaben zur Normung der KorroPad-Prüfung eingegangen.
Der Vortrag behandelt zunächst die wesentlichen Grundlagen der elektrolytischen Korrosion, die für das Verständnis der Eigenschaften korrosionsbeständiger (nichtrostender) Stähle notwendig sind. Anschließend wird das Phänomen der Passivität vorgestellt und die Wirkung von Legierungselementen auf Gefüge und Korrosionsbeständigkeit erläutert.
Der Vortrag behandelt zunächst die wichtigsten lokalen Korrosionserscheinungen (Spaltkorrosion, Interkristalline Korrosion, Lochkorrosion und Spannungsrisskorrosion), die bei korrosionsbeständigen (nichtrostenden) Stählen auftretenden können und gibt wichtige Hinweise zu deren Vermeidung. Außerdem werden die verschiedenen Werkstoffklassen (Ferrite, Austenite, Martensite und Duplexstähle) im Bereich der nichtrostenden Stähle vorgestellt und auf die Eigenschaften und Besonderheiten eingegangen.
Der Vortrag behandelt zunächst das Vorgehen bei der Beurteilung der Korrosionsbelastung unter atmosphärischen Bedingungen, wobei ausgewählte Einflussfaktoren (Chlorid-Gehalt und Schwefeldioxid-Gehalt) näher betrachtet werden. Anschließend wird die bisherige und die aktualisierte Normung der Werkstoffauswahl am Beispiel des Bauwesens vorgestellt und auf die verschiedenen Beständigkeitsklassen im Bereich der nichtrostenden Stähle eingegangen. Abschließend werden beispielhaft Schadensfälle und aktuelle Fragestellungen vom Fachbereich 7.6 zum Einsatz nichtrostender Stähle vorgestellt und erläutert.
Electrochemical tests, hardness measurements, and microstructure analysis are performed to study the influence of austenitizing, quenching, and tempering parameters on the corrosion resistance of the martensitic stainless steel grade X50CrMoV15 (1.4116). Different heat treatment states were studied using an adapted EPR-Test to evaluate the chromium distribution and depletion caused by the formation and dissolution of chromium rich carbides. The EPR results were correlated with pitting corrosion behavior, demonstrating the strong effect of heat treatment parameters on the susceptibility of martensitic stainless steels to corrosion phenomena.
The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials).
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Hardness and pitting corrosion resistance are the major quality criteria of cutlery. Both are achieved by the heat treatment (austenitization, quenching and tempering) of the normally used martensitic stainless steels. The established quality control method regarding the pitting corrosion resistance is an alternating immersion test in 1 % NaCl solution at 60 °C according to DIN EN ISO 8442. This standard test shows a high deviation, which limits any optimization of the heat treatment process. New approaches for corrosion testing of martensitic stainless-steels were developed and used in the last years to connect the weak pitting corrosion resistance of martensitic stainless-steels with the phenomenon of chromium depletion. The tempering temperatures used in the industrial heat treatment of cutlery are too low to explain the appearance of chromium depletion. For this reason, a systematic investigation of three heat treatment parameters (austenitization time, cooling speed and tempering temperature) were performed on the martensitic stainless-steels X50CrMoV15 (1.4116) to detect their contribution to chromium depletion. The electrochemical potentiodynamic reactivation (EPR), which is very sensitive to any change of the microstructure, was used to quantify the degree of chromium depletion. The KorroPad indicator-test was applied to correlate low pitting corrosion resistance to the presence of chromium depletion. The results of all investigations allow conclusions about the very small process window, which is necessary to achieve cutlery with high pitting corrosion resistance.
The KorroPad indicator test was invented at the Federal Institute for Materials Research and Testing to detect stainless-steel surfaces susceptible to pitting corrosion. The KorroPad indicator test is thus an interesting alternative for manufacturers, processors, users and researchers to time consuming exposition experiments and complex electrochemical investigations, which are normally used to reveal surface-related processing errors resulting in reduced pitting corrosion resistance. Furthermore, the KorroPad indicator test can be used to visualize alloy- and microstructure-related factors causing susceptibility to pitting corrosion. The detection limit of the KorroPad indicator test was characterized in this work using reference alloys with different chromium content (5 % to 18 %). The alloy-specific detection limit was shifted successfully to higher chromium content by increasing the concentrations of NaCl and K3[Fe(CN)6]. The modified KorroPads can now be used to establish an alloy-specific quality control regarding the pitting corrosion resistance of different stainless steel grades.
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion re-sistance due to chromium depletion.
The corrosion resistance of stainless-steels grades is of high importance for the technical safety in different environmental conditions. Processing and surface finish influences the corrosion resistance of ferritic stainless steels, which may be considered for some application in marine environment. Three ferritic stainless steel alloys (X2CrNi12, X2CrTiNb18 and X2CrMoTi18-2) were exposed in four different surface finishes (rolled, dry grinding, glass beaded and electro polished) for five years in marine environment to obtain reliable information about the corrosion resistance. All samples were assessed after 22 and 60 months according to DIN EN ISO 10289 in validation degrees from 1 to 10. Complementary investigation using accelerated chamber test (salt spray test followed by four weeks storage at 30 °C / 80 % relative humidity) and short-term electrochemical methods (electrochemical potentiodynamic reactivation, pitting potentials and the KorroPad method) were conducted to compare their results. The presentation gives an overview on all methods and the generated results, which show benefits and restrictions of long-term, accelerated and short-term corrosion tests.
The quenching and partitioning (Q&P) heat treatment enables a higher deformability of high strength martensitic steels. The Q&P heat treatment was applied on the martensitic stainless steel 1.4034 (X46Cr13) to study the influence of partitioning time. Therefore, extensive characterizations of the mechanical properties, focussing on the materials behaviour under different mechanical load scenarios, were performed. A comprehensive analysis of the microstructural evolution was per-formed for different heat treatment and mechanical loading states. A complete solution of chromium carbides was detected to be a first requirement for successful Q&P heat treatment. The comparison of common quenching and tempering with the Q&P heat treatment verifies the extensively enhanced materials strength whereat the formability is still acceptable. The microstructural reason was detected to be an increasing aus-tenite fraction due to austenite reversion at subgrain boundaries of martensite besides the stabilising of retained austenite. Further a distinctive strength differential effect was observed.