The sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of design and welding-induced residual stress can lead to crack formation and ultimately to component failure, particularly in interaction with the degradation of the microstructure and mechanical properties high-strength steels during the repair process.
In this context, component-related investigations (FOSTA-P1311/IGF-Nr. 20162 N) focusing on welding residual stress evolution during local thermal gouging and rewelding of S500MLO and S960QL are carried out using in-situ digital image correlation (DIC) and ex-situ X-ray diffraction methods (XRD). Therefore, self-restrained specimens were systematically gouged and rewelded with defined welding heat control (heat input, working temperature) and parameters. By means of structural mechanics calculations, geometries of self-restrained specimens were identified, that represent defined rigidity conditions of repair welds of real components. It could be shown that with increasing restraint intensity significantly higher residual stresses occur in the weld metal and heat affected zone. Furthermore, it revealed that the transverse stresses along the weld seam decrease at the weld seam ends leading to different stress state during gouging and welding. XRD analysis of the local residual stresses after cooling to RT longitudinal and transverse to the weld direction showed a good comparability with global DIC analyses.
Carbon arc-air gouging is a common technology when repairing defects in welded structures. Often this technique is applied in repeated cycles even on the same location of the joint. Due to the multiple heat input by gouging and subsequent re-welding, the residual stresses are strongly influenced. This can become crucial when microstructure and mechanical properties are adversely affected by multiple weld reparations. Knowledge about the relation of gouging and residual stresses is scarce but important when high strength steels, which are sensitive to residual stresses, are processed. The present study shows the effect of repair welding on a high strength steel structural element. The weld and the heat affected zone were subjected to multiple thermal cycles by gouging and subsequent repair welding. The residual stresses were determined by X-ray diffraction at different positions along the joint. The results showed that the residual stress level has increased by the repair cycles. This is most pronounced for the heat affected zone. Adapted welding procedures may prevent detrimental residual stress distributions.