In the present work, electron backscatter diffraction was used to determine the microscopic dislocation structures generated during creep (with tests interrupted at the steady state) in pure 99.8% aluminium. This material was investigated at two different stress levels, corresponding to the power-law and power-law breakdown regimes. The results show that the formation of subgrain cellular structures occurs independently of the crystallographic orientation. However, the density of these cellular structures strongly depends on the grain crystallographic orientation with respect to the tensile axis direction, with <111> grains exhibiting the highest densities at both stress levels. It is proposed that this behaviour is due to the influence of intergranular stresses, which is different in <111> and <001> grains.
The manufacturability of metallic alloys using laser-based additive manufacturing methods such as laser powder bed fusion has substantially improved within the last decade. However, local melting and solidification cause hierarchically structured and crystallographically textured microstructures possessing large residual stress. Such microstructures are not only the origin of mechanical anisotropy but also pose metrological challenges for the diffraction-based residual stress determination. Here we demonstrate the influence of the build orientation and the texture on the microstructure and consequently the mechanical anisotropy of as-built Inconel 718. For this purpose, we manufactured specimens with [001]/[011]-, [001]- and [011]/[111]-type textures along their loading direction. In addition to changes in the Young’s moduli, the differences in the crystallographic textures result in variations of the yield and ultimate tensile strengths. With this in mind, we studied the anisotropy on the micromechanical scale by subjecting the specimens to tensile loads along the different texture directions during in situ neutron diffraction experiments. In this context, the response of multiple lattice planes up to a tensile strain of 10% displayed differences in the load partitioning and the residual strain accumulation for the specimen with [011]/[111]-type texture. However, the relative behavior of the specimens possessing an [001]/[011]- and [001]-type texture remained qualitatively similar. The consequences on the metrology of residual stress determination methods are discussed.
Additive manufacturing methods such as laser powder bed fusion (LPBF) allow geometrically complex parts to be manufactured within a single step. However, as an aftereffect of the localized heat input, the rapid cooling rates are the origin of the large residual stress (RS) retained in as-manufactured parts. With a view on the microstructure, the rapid directional cooling leads to a cellular solidification mode which is accompanied by columnar grown grains possessing crystallographic texture. The solidification conditions can be controlled by the processing parameters and the scanning strategy. Thus, the process allows one to tailor the microstructure and the texture to the specific needs. Yet, such microstructures are not only the origin of the mechanical anisotropy but also pose metrological challenges for the diffraction-based RS determination. In that context the micromechanical elastic anisotropy plays an important role: it translates the measured microscopic strain to macroscopic stress. Therefore, it is of uttermost importance to understand the influence of the hierarchical microstructures and the texture on the elastic anisotropy of LPBF manufactured materials.
This study reveals the influence of the build orientation and the texture on the micro-mechanical anisotropy of as-built Inconel 718. Through variations of the build orientation and the scanning strategy, we manufactured specimens possessing [001]/[011]-, [001]-, and [011]/[111]-type textures. The resulting microstructures lead to differences in the macroscopic mechanical properties. Even further, tensile in-situ loading experiments during neutron diffraction measurements along the different texture components revealed differences in the microstrain response of multiple crystal lattice planes. In particular, the load partitioning and the residual strain accumulation among the [011]/[111] textured specimen displayed distinct differences measured up to a macroscopic strain of 10 %. However, the behavior of the specimens possessing [001]/[011]-and [001]-type texture was only minorly affected. The consequences on the metrology of RS analysis by diffraction-based methods are discussed.
For the precise determination of orientations in polycrystalline materials, electron backscatter diffraction (EBSD) requires a consistent calibration of the diffraction geometry in the scanning electron microscope (SEM). In the present paper, the variation of the projection center for the Kikuchi diffraction patterns which are measured by EBSD is calibrated using a projective transformation model for the SEM beam scan positions on the sample. Based on a full pattern matching approach between simulated and experimental Kikuchi patterns, individual projection center estimates are determined on a subgrid of the EBSD map, from which least-square fits to affine and projective transformations can be obtained. Reference measurements on single-crystalline silicon are used to quantify the orientation errors which result from different calibration models for the variation of the projection center.
A historical tool for crystallographic analysis is provided by the Hilton net, which can be used for manually surveying the crystal lattice as it is manifested by the Kikuchi bands in a gnomonic projection. For a quantitative analysis using the Hilton net, the projection centre as the relative position of the signal source with respect to the detector plane needs to be known. Interplanar angles are accessible with a precision and accuracy which is estimated to be ≤0.3o. Angles between any directions, e.g. zone axes, are directly readable. Finally, for the rare case of an unknown projection-centre position, its determination is demonstrated by adapting an old approach developed for photogrammetric applications.
It requires the indexing of four zone axes [uvw]i in a backscattered Kikuchi diffraction pattern of a known phase collected under comparable geometric conditions.
We present special applications of electron backscatter diffraction (EBSD) which aim to overcome some of the limitations of this technique as it is currently applied in the scanning electron microscope. We stress that the raw EBSD signal carries additional information which is useful beyond the conventional orientation determination. The background signal underlying the backscattered Kikuchi diffraction (BKD) patterns reflects the chemical composition and surface topography but also contains channeling-in information which is used for qualitative real-time orientation imaging using various backscattered electron signals. A significantly improved orientation precision can be achieved when dynamically simulated pattern are matched to the experimental BKD patterns. The breaking of Friedel’s rule makes it possible to obtain orientation mappings with respect to the point-group symmetries. Finally, we discuss the
determination of lattice parameters from individual BKD
patterns. Subgrain structure in a single quartz grain. The increased noise level in the left map reflects the lower precision of a standard orientation determination using band detection by the Hough transform. The right map results from the same experimental raw data after orientation refinement using a pattern matching approach. The colors correspond an adapted inverse pole figure color key with a maximum angular deviation of about 2° from the mean orientation.
During the processing of superconducting Nb3Sn wire, several intermediate intermetallic phases including a previously encountered Cu-Nb-Sn phase show up. The yet unknown crystal structure of this phase is now identified by a combination of different experimental techniques and database search to be of the hexagonal NiMg2 type with a proposed composition of about (Nb0.75Cu0.25)Sn2. The structure determination started from an evaluation of the lattice parameters from EBSD Kikuchi patterns from quenched material suggesting hexagonal or orthorhombic symmetry. A database search then led to the hexagonal NiMg2 type structure, the presence of which was confirmed by a Rietveld analysis on the basis of high energy synchrotron X-ray powder diffraction data. Assuming a partial substitution of Nb in orthorhombic NbSn2 by Cu, the change of the valence electron concentration provokes a structural transformation from the CuMg2 type for NbSn2 to the NiMg2 type for (Nb0.75Cu0.25)Sn2. In the previous literature the (Nb0.75Cu0.25)Sn2 phase described here has occasionally been referred to as Nausite.
The effect of electrochemical charging of hydrogen on the structure of a lean duplex stainless steel LDX 2101® (EN 1.4162, UNS S32101) was examined by both Time-of-Flight secondary ion mass spectrometry and electron back-scatter diffraction. The goal is to correlate hydrogen concentration and induced structural changes. Chemical and structural characterizations were done for the same region at the sample's surface with sub-micron spatial resolution. Regions of interest were varying in size between 50 × 50 μm and 100 × 100 μm. The results show a phase transformation of austenite to mainly a defect-rich BCC and scarcely a HCP phase. The phase transformation occurred in deuterium rich regions in the austenite.
The thermal stability of the microstructure of a heat-resistant cobalt alloy, which consists of a γ solid solution strengthened with γ'-phase precipitates, has been studied. The temperature behavior of the dissolution of the hardening γ' phase and the kinetics of its coarsening at 700 and 800°C have been determined. It is found that, during prolonged annealing at 800°C, the γ' → β phase transformation occurs.
The inverse pole figure (IPF) coloring for a suitable evaluation of crystal
orientation data is discussed. The major goal is a high correlation between
encoding color and crystal orientation. Revised color distributions of the
fundamental sectors are introduced which have the advantages of (1) being
applicable for all point groups, (2) not causing color discontinuities within grains,
(3) featuring carefully balanced regions for red, cyan, blue, magenta, green and
yellow, and (4) an enlarged gray center in opposition to a tiny white center. A
new set of IPF color keys is proposed which is the result of a thorough analysis
of the colorization problem. The discussion considers several topics: (a) the
majority of presently applied IPF color keys generate color discontinuities for
specifically oriented grains; (b) if a unique correlation between crystal direction
and color is requested, discontinuity-preventing keys are possible for all point
groups, except for 4, 3 and 1; (c) for a specific symmetry group several IPF color
keys are available, visualizing different features of a microstructure; and (d) for
higher symmetries a simultaneous IPF mapping of two or three standard
reference directions is insufficient for an unequivocal orientation assignment.
All color keys are available in MTEX, a freely available MATLAB toolbox.
Crystal structures that show a broken symmetry in their cubic and hexagonal modifications are of great relevance for optoelectronic and photonic applications. This is why methods which are sensitive to non-centrosymmetric structures are important for analysis of these materials in technological applications.
Computational Advances
(2014)
The advent of simultaneous energy dispersive X-ray spectroscopy (EDS) data collection has vastly improved the phase separation capabilities for electron backscatter diffraction (EBSD) mapping. A major problem remains, however, in distinguishing between multiple cubic phases in a specimen, especially when the compositions of the phases are similar or their particle sizes are small because the EDS interaction volume is much larger than that of EBSD, and the EDS spectra collected during spatial mapping are generally noisy due to time limitations and the need to minimize sample drift. The backscatter electron (BSE) signal is very sensitive to the local composition due to its atomic number (Z) dependence. BSE imaging is investigated as a complimentary tool to EDS to assist phase segmentation and identification in EBSD through examination of specimens of meteorite, Cu dross, and steel oxidation layers. The results demonstrate that the simultaneous acquisition of EBSD patterns, EDS spectra, and the BSE signal can provide new potential for advancing multiphase material characterization in the scanning electron microscope.
Since the BSE signal depends on many factors, like the chemistry of the phase and the acceleration voltage, the size and position of the detector array is (slightly) different from phase to phase so that an (iterative) post-processing of the stored patterns is highly recommended. The derived BSE signal can be used for phase assignment in high resolution and high speed maps when EBSD fails and/or EDS (energy dispersive spectroscopy) needs too much time for a suitable and parallel signal acquisition.
The macro- and microstructure of iron meteorites provide valuable insights into both the inner structure of our planet and the history of our solar system. High speed collision events in the asteroid belt send the meteorites careening toward Earth. The collisions produce unique deformation microstructures. With cooling rates on the scale of a few degrees per million years, iron meteorites can consist of crystal sizes on the order of meters prior to the collision events. These extremely slow cooling rates result in phase transformations occurring at conditions near thermodynamic equilibrium. Preserving meteorite fragments is important for future studies of phase transformations, material behavior at high strain rates, and the origin of the universe.
Biofilms living on gold (Au) grains play a key role in the biogeochemical cycle of Au by promoting the dispersion of Au via the formation of Au nanoparticles as well as the formation of secondary biomorphic Au. Gold grains from Queensland, Australia, are covered by a polymorphic, organic-inorganic layer that is up to 40 μm thick. It consists of a bacterial biofilm containing Au nanoparticles associated with extracellular polymeric substances as well as bacterioform Au. Focused ion beam (FIB) sectioning through the biofilm revealed that aggregates of nanoparticulate Au line open spaces beneath the active biofilm layer. These aggregates (bacterioform Au type 1) resulted from the reprecipitation of dissolved Au, and their internal growth structures provide direct evidence for coarsening of the Au grains. At the contact between the polymorphic layer and the primary Au, bacterioform Au type 2 is present. It consists of solid rounded forms into which crystal boundaries of underlying primary Au extend, and is the result of dealloying and Ag dissolution from the primary Au. This study demonstrates that (1) microbially driven dissolution, precipitation, and aggregation lead to the formation of bacterioform Au and contribute to the growth of Au grains under supergene conditions, and (2) the microbially driven mobilization of coarse Au into nanoparticles plays a key role in mediating the mobility of Au in surface environments, because the release of nanoparticulate Au upon biofilm disintegration greatly enhances environmental mobility compared to Au complexes only.
Modern EBSD systems perform diffraction pattern “quality” (PQ) calculations, essentially measurements of the contrast of the brighter bands in the pattern above background, for every pattern analyzed. Since the calculations are independent of EBSD indexing, data are generated from all points on the analyzed sample surface, regardless of indexability or the state of the material beneath. EBSD maps generated from PQ data are like microstructurally sensitive SEM images, collected at EBSD speeds and grid resolutions, with contrast arising from phase density, crystal structure, crystallographic orientation, grain boundary location, near-surface plastic strain, coating density/thickness, and to some extent topography. Grain boundaries and other aspects of sample microstructure are readily revealed, so the PQ map is a very useful characterization tool in its own right, and serves as a reference for EBSD maps generated from indexing-derived data, such as orientation, grain boundary character, phase distribution and strain maps.