Three-dimensional (3D) γ-MnO2@ZnFe2O4/reduced graphene oxide (rGO) nanohybrids were synthesized using a one-pot hydrothermal self-assembly method. The morphology and properties of the nanohybrids were investigated.
The synergistic interactions among γ-MnO2, ZnFe2O4, and rGO resulted in 3D nanoflakes distributed uniformly in the rGO structure with a thickness of approximately 2–5 nm, leading to a high surface area. The nanohybrid containing 10 wt. % rGO exhibited superior catalytic activities for phenol degradation through the activation of peroxymonosulfate (PMS) to generate active sulfate radicals (SO4 •–). Typically, 50 mL of a 20 ppm phenol solution was degraded completely and 85% of the carbon content had been mineralized in 30 min at 25 °C using 10 mg of the nanohybrid. The nanohybrid could be recovered easily using a magnet and reused, maintaining high stability during catalytic oxidation. The 3D γ-MnO2@ZnFe2O4/rGO nanohybrid catalyst could be applied to the removal of hard-to-degrade waste materials owing to its high efficiency and excellent reusability.
With the vast exploration of the applications of graphene, researchers are assessing different methods for fabricating graphene-based electrode material with high capacitance but low material and energy costs. In this study, reduced graphene oxide/nickel oxide (RGO/NiO) nanocomposites were prepared using a non-aqueous solvent-based method followed by calcination. Nickel acetate tetrahydrate and tert-butanol were used as the precursor and solvent, respectively. Ultrasmall nickel oxide nanoparticles, ca. 8.0 nm in size, were deposited on the surface of the graphene sheets simultaneously with the partial reduction of graphene oxide. The resulting RGO/NiO electrode exhibited a high capacitance of 689 F g⁻1 at a current density of 0.8 A g⁻1. After 1500 cycles, the specific retention and the coulombic efficiency yielded to 86.34% and 96.39%, respectively, which supports the viability of this composite as an alternative activated material with high electrochemical performance.