- Carbon steel (4)
- Methanogen-induced microbiologically influenced corrosion (3)
- Modelling studies (3)
- Microbiologically influenced corrosion (2)
- Biocorrosion (1)
- Environmental condition (1)
- Flow Model (1)
- Hi-Tension (1)
- Korrosion (1)
- MIC (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
Corrosion is a very expensive and serious problem in the different industry sectors, eg. Petroleum-, On- and off-shore, infrastructure. It is estimated that 20% of all corrosion damage is caused by microorganisms or microbiologically influenced corrosion (MIC). Several microorganisms are known to cause corrosion, including sulfate-reducing bacteria, nitrate-reducing bacteria, methanogens etc. For several years, methanogens were regarded as a mild corroder (~0.065 mm/yr), largely due to a lack of detailed investigation on the corrosion mechanism under real-environment simulated conditions. Resulting in the common belief that siderite, a non-conductive compound, is the sole corrosion product (CP) of methanogen-induced MIC (Mi-MIC).
To simulate natural environmental conditions, we developed and introduced the multiport flow column system (MFC), a multi-sectional corrosion flow-cell. Using the MFC, we obtained ten times higher corrosion rates than previously reported. With a combination of several analytical techniques, such as ToF-SIMS, SEM-EDS and FIB-SEM, we found strong indication that siderite is not the sole corrosion product of Mi-MIC. The corrosion layers contained phosphorus, oxygen, magnesium, calcium and iron. The differences in the CP between static and dynamic environments demonstrated the impact of testing procedures on the corrosive potential of methanogens. To further verify and deepen our understanding of Mi-MIC, we are currently studying the influence of additional environmental parameters (e.g. pH, salinity, flow rate) on Mi-MIC.
Overall, results of this study will expand the current understanding of MIC from both analytical and mechanistic points of view, thus aiding the development of different mitigation strategies for various industry sectors.
The role of methanogens in microbiologically influenced corrosion (Mi-MIC) is often neglected, due to 1) low reported corrosion rates and 2) the suspected corrosion product siderite, which is electrically non-conductive. Typically, MIC corrosion studies are carried out using batch cultures, which did not represent the dynamic conditions, i.e. pipeline and provide insufficient information on the overall corrosion potential.
We established a unique approach, a multiport flow column (MFC), to simulate pipeline conditions and obtained 10-times higher corrosion rates than previously published. Our result showed that testing procedures have a large impact on the corrosive potential of methanogens. We found strong indications with a combination of ToF-SIMS, SEM-EDS and FIB-SEM analyses that siderite is not the sole corrosion product. The corrosion layers contain phosphorus, oxygen, magnesium, calcium and iron. To verify and deepen our understanding of Mi-MIC, we are currently studying the influence of other environmental parameters (e.g. pH) on Mi-MIC.
Microbiologically influenced corrosion (MIC) is a now well-known challenge and affects industry, society and infrastructure. For a long time, the impact of methanogen-induced MIC (Mi-MIC) was underestimated. This was mainly due to the rather low published corrosion rates and the presumed corrosion product siderite, which is not electrically conductive. In our laboratory, we were able to show that this trivialization or underestimation of Mi-MIC was due to the nature of the testing. The static systems used so far do not provide environmentally relevant information about the corrosion rate and the corrosion product, especially for methanogens
To further illustrate the importance of the environment on the MIC process, we established a multiport flow column (MFC), to simulate the natural environment. With this method, and in contrast to published results using the static conditions, we obtained ten times higher corrosion rates. We analyzed the corrosion products with a combination of techniques, like ToF-SIMS, SEM-EDS and FIB-SEM, and found strong evidence that siderite is not the sole corrosion product of Mi-MIC. The corrosion layers contain phosphorus, oxygen, magnesium, calcium and iron and lacked on carbon-related species. It is hypothesized that methanogens may have influenced the nucleation process of siderite, converting bicarbonate into carbon dioxide for methanogenesis. This results in increased localized corrosion and reduced siderite formation. To verify and deepen our understanding of Mi-MIC, we are currently studying the influence of additional environmental parameters (e.g. pH, salinity, flow rate etc.) on Mi-MIC and the subsequent impacts on corrosion rates and the corrosion products.
Overall, results of this study will expand the current understanding of MIC from both analytical and mechanistic points of view, thus aiding the development of different mitigation strategies for various industry sectors.
MFC was used to study the corrosiveness of iron-utilizing methanogen, Methanobacterium IM1 under flow conditions. Comparing against electrical SRM, Desulfovibrio ferrophilus IS5, results showed under standard mesophilic conditions, average corrosion rates of Methanobacterium IM1 was double that of SRM. The highest corrosion rate of Methanobacterium IM1 reached up to 0.60 mm/yr under neutral conditions, and severe pitting was observed on the iron surface. Furthermore, the corrosion products of Methanobacterium IM1 were characterized with TOF-SIM, FIB-SEM and EDX, and preliminary results revealed FeCO3 is not the only corrosion product of Mi-MIC, as previously reported. Under low pH conditions, the maximum corrosion rate of Methanobacterium IM1 reached 1.57 mm/yr, which resulted in severed deformity of the iron specimen. Additional comparisons using different types of incubation material were conducted to standardize MFC MIC testing.
Currently, corrosion rates (CR) and/or corrosion products (CP) obtained for methanogen-induced microbiologically influenced corrosion (Mi-MIC) on carbon steel are mainly analyzed from static-incubations. By using a multiport-flow-column, much higher CRs (0.72 mm/yr) were observed, indicating static-incubations are not suitable for determining the corrosive potential of Mi-MIC. With the combination of various analytical methods (ToF-SIMS/SEM-EDS/SEM-FIB) and contrary to previously published data, we observed that CPs contained phosphorus, oxygen, magnesium, calcium and iron but lacked carbon-related species (e.g. siderite). Overall, siderite nucleation is disrupted by methanogens, as they convert aqueous bicarbonate into carbon dioxide for methanogenesis resulting in increased localized corrosion.