Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (2) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (1)
- Vortrag (1)
Sprache
- Englisch (2)
Referierte Publikation
- nein (2)
Schlagworte
- Alkali-silica reaction (1)
- Concrete motorway pavements (1)
- Hydrothermal treatment (1)
- Mechanical strength (1)
- Microstructure (1)
- Performance test (1)
- Phase composition (1)
- Raman microscopy (1)
- UHPC (1)
Organisationseinheit der BAM
- 7.1 Baustoffe (2) (entfernen)
Eingeladener Vortrag
- nein (1)
Alkali silica reaction (ASR) is a major concrete durability problem resulting in significant maintenance and reconstruction costs for concrete infrastructures all over the world. To determine whether an aggregate is potentially reactive, accelerated concrete tests are used. Aim of this study is the chemical and microstructural characterization of ASR-products formed under the performance conditions of motorway pavements and during subsequent tests on the remaining ASR susceptibility. Samples were taken from concrete motorway pavements. Some of the samples already showed first indications for beginning damages whereas others showed deteriorations only after applying a performance testing procedure for the estimation of future risk of ASR damage. In a first step ASR-products were identified by polarized light microscopy in thin sections. The reaction products where then analyzed by Raman Spectroscopy and finally the chemical composition of the ASR-products was identified by SEM with EDX.
The results indicate that most reaction products show an increasing Ca/Si-ratio with progressive crack length. If an ASR-product develops inside an aggregate and moves through the cement paste, it has a high (Na+K)/Si-ratio at the beginning which decreases with increasing distance from its place of origin. The Raman spectra of the ASR-products are characterized by two broad bands indicating specific Q-species of different amorphous gel networks. Within the scope of the analysis distinctions in the microstructure and the chemical composition of the ASR-gels were detected relating to various conditions of accelerated testing.
The advantages of treating prefabricated components made of Ultra-High-Performance Concrete (UCPC) at 90 °C are largely recognized, while hydrothermal treatment at 185 °C and the corresponding saturation pressure of 1.1 MPa, in contrast, is not applied in building practice so far and was studied only by a few researchers.
In the research presented, the parameters pre-storage-time before treatment and dwell time in the autoclave were systematically varied. The results illustrate in which way compressive strength increases with the duration of treatment. Already samples which were only heated up and immediately cooled down show an increase in strength compared to the 28-day reference of about 10 %. After 20 h the maximum increase of about 25 % is reached. Interestingly the compressive strength of samples treated very long hardly decreases. It can be therefore concluded that for the composition investigated the achievable mechanical strength is not severely sensitive regarding the duration of the treatment.
Also, pre-storage times before autoclaving longer than 0.5 days showed no significant impact on strength development.
The phase composition measured by XRD exhibits significant changes compared to the reference. The amount of ettringite and portlandite have vanished, the cement clinker phases are substantially decreased and hydroxylellestadite and hydrogarnet are formed as new phases. The increase in strength can be assigned to an improved pozzolanic and hydraulic reaction. Contradictory to literature, there was found no tobermorite, a mineral which is known to be susceptible for disintegration at Long autoclaving duration. This explains why no significant strength loss appeared.