Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (102) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (102) (entfernen)
Referierte Publikation
- nein (102) (entfernen)
Schlagworte
- Corrosion (7)
- Steel (5)
- TiB2 (5)
- CO2 (4)
- AISI D2 (3)
- Additive Manufacturing (3)
- Carbon steel (3)
- Eigenspannungen (3)
- Laser implantation (3)
- Laserimplantation (3)
Organisationseinheit der BAM
- 9 Komponentensicherheit (41)
- 9.3 Schweißtechnische Fertigungsverfahren (29)
- 7 Bauwerkssicherheit (26)
- 8 Zerstörungsfreie Prüfung (14)
- 5 Werkstofftechnik (12)
- 6 Materialchemie (10)
- 7.6 Korrosion und Korrosionsschutz (10)
- 7.1 Baustoffe (9)
- 5.1 Mikrostruktur Design und Degradation (8)
- 9.4 Integrität von Schweißverbindungen (8)
AKR an Betonfahrbahndecken – ausgewählte Einflussgrößen und neuartige AKR-Vermeidungsstrategie
(2019)
In den letzten Jahren sind im deutschen Bundesautobahnnetz vermehrt Schäden an vor 2005 hergestellten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Vor diesem Hintergrund werden in diesem Beitrag zunächst die Voraussetzungen und ausgewählte Einflussgrößen für eine schädigende AKR aufgezeigt. Besondere Aufmerksamkeit wird dabei der Rolle des Tausalzeintrags durch den Winterdienst bei Betonfahrbahndecken geschenkt. So wird mit Löseversuchen in 1 M KOH-Lösung zweier Gesteinskörnungen bei 80 °C gezeigt, dass mit zunehmender NaCl-Zugabe die Löslichkeit von SiO2 zunimmt und die von Al2O3 eine Verminderung erfährt. Basierend auf dem so exemplarisch erbrachten Nachweis für die Verstärkung der schädigenden AKR durch das Tausalz wird die Notwendigkeit und Richtigkeit der Durchführung von AKR-Betonversuchen mit Alkalizufuhr im ARS 04/2013 zur zukünftigen Vermeidung von AKR-Schäden an Betonfahrbahndecken im Rahmen von Neubau- und Erneuerungsmaßnahmen im Bundesfernstraßennetz belegt. Zusätzlich durchgeführte WS-Grundprüfungen nach dem ARS 04/2013 mit den beiden Gesteinskörnungen der Löseversuche veranschaulichen, dass die nach der Alkali-Richtlinie des DAfStb als unbedenklich eingestuften Gesteinskörnungen bei den Betonversuchen mit Alkalizufuhr durchaus als alkaliempfindlich bewertet werden können. Dies wiederum führt zu einer Verminderung der für den Betonstraßenbau verfügba-ren Gesteinskörnungen. Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung der als grenzwertig alkaliemp-findlich eingestuften Gesteinskörnungen erlaubt. Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungsprozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innenhydrophobierung zur Vermeidung bzw. Verminderung einer schädigenden AKR in Betonfahrbahndecken wird zurzeit im Auftrage der BASt an der BAM ein Forschungsvorha-ben bearbeitet. Im Rahmen dieses Beitrags werden erste Ergebnisse dieses Projekts vorge-stellt. So wird exemplarisch an einem Oberbeton (D > 8)/Unterbeton und einem Oberbeton 0/8 mit einer alkaliempfindlichen Gesteinskörnung der Einfluss zweier Hydrophobierungsmit-tel auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letz-teren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss beider Hydro-phobierungsmittel auf die schädigende AKR mittels AKR-Betonversuchen mit Alkalizufuhr beleuchtet. Dabei gelangen ergänzend zur Beurteilung des Tausalzeintrags die Laser-Induced Breakdown Spectroscopy (LIBS) und zur Bewertung der Ausprägung der AKR und sekundä-ren Ettringitbildung (SEB) die Dünnschliffmikroskopie zum Einsatz.
The determination of mechanical properties of welded Steel structures such as strength or ductility is a subject of high interest for the majority of Companies in the area of metal Processing. The material Parameters can be obtained by performing the tensile test on the samples made from a part of a component. In some cases, it is highly expensive to produce the tensile specimens especially from the weld metal, which contains different type of microstructure such as weld seam or heat affected zone in an extremely small area. Therefore, a method is described in this paper to determine the material Parameters of high strength Steel structures and welded joints locally and without any additional effort to perform the tensile test. In this method, instrumented indentation technique (IIT), an indenter is pushed on the flat surface of a specimen in a certain period of time and simultaneously the applied force and the corresponding indentation path are measured. The data related to the force-indentation diagram is given as input to an artificial neural network (ANN) to obtain the material Parameters. The ANN can be trained by generating the large qualitative data sets with numerical Simulation of the IIT procedure. The Simulation must be run several times with the different material model parameter sets to generate the numerous
force-indentation diagrams as the inputs of ANN. Then, the trained ANN is validated by performing the IIT on the welded joints and comparing the obtained material Parameters from ANN with the tensile test.
Consequently, the mechanical properties of welded joints can be determined by performing the IIT and evaluating the resulting data by the ANN.
Additive Fertigungsverfahren gewinnen aufgrund der schnellen, flexiblen und kosten-günstigen Fertigung von Bauteilen zunehmend an Bedeutung. Das Laserpulverauf-tragschweißen (LPA) wurde anfangs hauptsächlich als Beschichtungsverfahren ein-gesetzt. Diese Technologie bewerkstelligt aber auch das Reparieren von verschlisse-nen Bauteilen, sodass diese zeitsparend und ressourcenschonend erneuert werden können. Die hohe Aufbaurate, die flexible Pulverzusammensetzung sowie die hohe Endkonturnähe ermöglichen heutzutage die Entwicklung und additive Fertigung von neuen Materialien, wie zum Beispiel Nickel-Titan-Formgedächtnislegierungen.
During carbon sequestration the CO2-induced corrosion of injection pipe steels is a relevant safety issue when emission gasses are compressed into deep geological layers. The reliability of the high alloyed steel X35CrMo17 suitable as injection pipe for the geological onshore CCS-site (Carbon Capture and Storage) in the Northern German Basin, is demonstrated in laboratory experiments in equivalent corrosive environment (T = 60 °CC, p = 1–100 bar, aquifer water, CO2-flow rate of 9 L/h, 700–8000 h exposure time). Corrosion kinetics and microstructure were characterized and compared to other potential injection pipe steels (42CrMo4, X46Cr13, X20Cr13 and X5CrNiCuNb16-4).
Coupons of X5CrNiCuNb16-4 that may be used as injection pipe with 16% Chromium and 0.05% Carbon (1.4542, AISI 630) were exposed for 3000 h to CO2-saturated saline aquifer water similar to the conditions in the Northern German Basin at ambient pressure and 60 °C. Surface corrosion layers and pits reveal carbonate corrosion products on the surface such as FeCO3 and FeOOH as the main precipitation phases with no dependence on the original surface roughness. Corrosion rates for polished and technical surfaces were below 0.005 mm/year compared to corrosion rates of 0.035 mm/year after shot peening.
In this poster we will present some results of a research projects dealing with Arabic recipes of black inks. To improve conservation practices of Arabic manuscripts we have assessed the feasibility of the recipes collected from many Arabic sources on bookmaking and reproduced the most common inks. Ink samples were then artificially aged and analysed using an array of analytical techniques, mostly non-invasive, in order to build a database of Arabic inks and their ingredients and also to verify the detection limits of the portable equipment employed.
We will show procedures and problems concerning the identification of ink types and ingredients using reflectography (in Vis, IR and UV), X-Ray Fluorescence, Infrared and Raman spectroscopy. The focus will be in particular on squid ink and mixed inks – both in the form of carbon inks with the addition of tannins and of a mixture of carbon and iron gall inks – which are particularly difficult to detect. We will also examine the results of iron gall inks made with iron filings or nails instead of vitriol, the various precursor used to extract gallic acid that are mentioned in the sources as surrogates of gall nuts.
Without precaution, insects may cause serious damage to museum collections. Quarantine of potentially infested objects can be logistically challenging. Anoxia under controlled Nitrogen atmosphere is a most gentle but also time-consuming method to eradicate insect pests in all kinds of different materials. Treatment results are usually affected by duration, temperature, humidity and residual oxygen content. During a two-year research project, 34 relevant pest insect species of all developmental stages were tested in different materials (wood, paper, wool) to monitor treatment success and to determine optimum treatment parameters. Duration of treatment ranged from one to three weeks at temperatures of 20–27 °C. As expected, results showed significant differences in mortality among tested species. Highest tolerance of hypoxic conditions was found in elder larvae of Hylotrupes bajulus. Although this species is an unlikely museum pest, it may serve as an overall most tolerant reference. Anobiids and other wood boring beetles are more often an issue related to cultural heritage. A combination of three weeks exposure time at maximum 0.5% residual oxygen and 24 °C, alternatively 1%
residual oxygen and 27 °C are recommended for infested artefacts. Imbedding materials in general had no influence on mortality. This study was funded by Deutsche Bundesstiftung Umwelt (DBU).
Das Fügeverfahren Kleben bietet viele Vorteile wie z.B. das Verbinden schwieriger Materialklassen, geringe thermische Belastung (Strukturveränderung/-schwächung) der Fügepartner und eine Lastverteilung über den gesamten Fügebereich. Die Auswahl an verfügbaren Klebstoffen und Vorbehandlungsoptionen ist dabei ebenfalls vielfältig. Einige Polymere weisen darüber hinaus Eigenschaften auf, die eine Herstellung von festen und dauerhaft beanspruchbaren Klebverbindungen erschweren. Mittels Oberflächenbehandlung, z.B. durch Plasmafeinreinigung bzw. –aktivierung, können die Grenzflächern solcher Polymere - bezogen auf die Eignung als Fügeteilpartner – optimiert werden. Schnelle Prüfverfahren zur Ermittlung von Verbundeigenschaften sind somit erforderlich.
Das Messprinzip Centrifugal Adhesion Testing Technologie verwendet die radial gerichtete Zentrifugalkraft als Belastungsgröße des zu testenden Verbunds, die durch Variation der Drehzahl gesteuert wird. Bei Erreichen der kritischen Beanspruchung trennt sich ein aufgeklebter Prüfstempel vom Substrat. Zeitgleich wird ein positionsbezogenes IR-Signal aus dem drehenden Rotor an das Basisgerät gesendet und zusammen mit der Drehzahl an die PC-Software übertragen. Für jede Probe wird die Bruchkraft berechnet und in Echtzeit angezeigt. Der Adhesion Analyser LUMiFrac® untersucht bis zu acht Prüfkörper unter identischen Bedingungen. Das neue Messprinzip erfüllt die Anforderungen von DIN EN 15870, DIN EN 14869-2, ISO 4624 sowie DIN EN 13144.
Die Multiprobentestung ermöglicht schnelle Charakterisierungen von Klebverbindungen. So kann der Effekt einer Plasmabehandlung von Bauteilen auf die Verbundfestigkeit zeitsparend bestimmt werden. Die gezielte Veränderung unterschiedlicher Plasma-Parameter, wie beispielsweise, die Plasmazusammensetzung, der Abstand vom Plasmabrenner zur Oberfläche oder die Verweildauer unter dem Brenner, beeinflußt die Festigkeit des Klebsystems und ist dem LUMiFrac direkt quantifizierbar.
Neben der Festigkeitsbestimmung von Klebverbindungen ist die Haftung von Schichtsystemen ein wichtiger Anwendungsbereich. Ergebnisse für Zug- und Scherbeanspruchung, realisiert mit unterschiedlichen Prüfkörper-Geometrien, werden vorgestellt. Ferner werden verschiedene festigkeitsbeeinflussende Faktoren, wie Prüfgeschwindigkeit oder Substratverformung bei Beanspruchung untersucht
Von der Anwendung ins Prüflabor: Maßstabsgetreues Bewerten von Spannungen in geschweißten Bauteilen
(2019)
Eigenspannungen sind von zentraler Bedeutung für die Performance geschweißter Bauteile. Die Bewertung schweißbedingter Beanspruchungen im Labormaßstab ist oft nicht zielführend. Reale Bauteilschweißungen weisen geometrisch und konstruktiv bedingt meist divergente Wärmeableitungs- und Einspannbedingungen auf. Dadurch lassen sich häufig nur eingeschränkt Aussagen über Eigenspannungshöhen, -verteilungen und die wesentlichen Einflussfaktoren treffen. Dies führt oftmals zur eher konservativen Konstruktionsauslegung und damit zu einer geringerenRessourcen- und Energieeffizienz. Dieser Beitrag widmet sich den Bestrebungen, reale Randbedingungen beim Bauteilschweißen in das Labor zu übertragen. Es werden die Möglichkeiten eines speziell für diesen Zweck an der BAM entwickelten Prüfsystems mit einer maximalen Tragkraft von 2 MN aufgezeigt. Durch die konstruktive Gestaltung der Anlage lassen sich in Schweißversuchen schweißbedingte Beanspruchungen nachbilden und die komplexen Einflüsse und Wechselwirkungen durch Schweißprozess, Bauteilgeometrie und -konstruktion sowie durch die eingesetzten Grund- und Zusatzwerkstoffe quantifizieren. Darüber hinaus können mittels Röntgenbeugung die resultierenden lokalen Eigenspannungen präzise und mit hoher Ortsauflösung bestimmt werden. Anhand von Beispielen wird die Nachbildung realer Produktionsbedingungen im Labor erörtert und gezeigt, wie die Spannungen beim Schweißen hochfester Baustähle von konstruktiven, werkstoff- und prozessseitigen Randbedingungen abhängen.
So wurde geklärt, wie erhöhte Arbeitstemperaturen zum signifikanten Anstieg der Beanspruchungen führen.
Charakterisierung von Hochtemperaturwerkstoffen durch Zug- und Ermüdungsversuche an Kleinproben
(2019)
Die Verwendung von miniaturisierten Probengeometrien in der mechanischen Prüfung ermöglicht die Entnahme des Probenmaterials direkt aus kritischen Bereichen wie Fügeverbindungen und ermöglicht die Prüfung von kleinen Bauteilen wie additiv gefertigten Strukturen. In der vorliegenden Arbeit werden exemplarisch die Ergebnisse von vergleichenden Zug- und niederzyklischen Schwing-versuchen (LCF) an dem austenitischen Stahl AISI 316L und der Nickelbasislegierung IN718 vorgestellt. Die Prüfergebnisse der Kleinproben aus AISI 316L weisen die charakteristischen Eigenschaften des Werkstoffs auf, und die Analyse der Zug- und Ermüdungsdaten führt zu Werten, die den Literaturdaten weitgehend entsprechen. Der direkte Vergleich mit Standardprobendaten zeigt jedoch systematische Abweichungen bei Zugfestigkeit, Dehngrenze und Gleichmaßdehnung, die in diesem Beitrag diskutiert werden.