Dark-field Transmission electron microscopy (DFTEM) results were obtained and presented. The results are discussed with regard to additional microstructural characterisation of the primyra Phase and creep experiments of alloy 2618A. Different methods to determine the volume fractions of precipitate phases are presented.
Visualization of surface modifications may be very challenging for coating/substrate systems of either almost identical optical constants, e.g. transparent films on substrates of the same material, or minor film thickness, substance quantity and affected area, e.g. ultra-thin or island films. Methods for visualization are optical microscopy (OM), imaging ellipsometry (IE), and referenced spectroscopic ellipsometry (RSE). Imaging ellipsometry operates at oblique incidence near Brewster angle of the bare, clean or unmodified substrate. In this configuration, reflected intensities are rather weak. However, the contrast to add-on and sub-off features may be superior. Referenced spectroscopic ellipsometry operates in a two-sample configuration but with much higher intensities. In many cases, both ellipsometric techniques reveal and visualize thin films, printed-pattern, laser-induced changes, and impurities better than optical microscopy. In particular for stratified homogeneous modifications, ellipsometric techniques give access to modelling and hence thickness determination. Modifications under investigation are polymer foil residue on silicon, laser-induced changes of ta-C:H coatings on 100Cr6 steel, imperfections of ta-C:H on thermal silicon oxide, degradation of glass, thin film tin oxide pattern on silicon, printed and dried pattern of liquids such as deionized water, cleaning agents, and dissolved silicone. © 2016 Elsevier B.V. All rights reserved.
Ethylene-propylenene-diene copolymer rubbers (EPDM) are used in a wide range of sealing applications e.g. in automotive industry or in containers for dangerous goods. Investigations with regard to the ageing behavior and lifetime prediction of commercial EPDM rubber seals consisting of 48 % polypropylene (PP) and 4.1 % of 5-ethylidene-2-norbornene (ENB) were conducted [1]. However, structural parameters (monomer ratio, diene type, curing agent etc.) and additives (filler, plasticizer etc.) are known to affect the ageing behavior of rubber compounds [2, 3]. The aim of the current study was to elucidate the influence of each component on the overall deterioration of material properties after thermal ageing. Therefore, different EPDM mixtures were prepared at BAM, the reference being an EPDM with 48 % PP and 4.1 % ENB reinforced with Sillitin. Five more formulations were prepared in order to assess the effect of (i) filler type (carbon black or sillitin), (ii) curing agent (sulfur or peroxide), (iii) plasticizer, (iv) ethylene-propylene ratio and (v) ENB content. Initially, the properties of the unaged materials were investigated by tensile testing, hardness and density measurements, TGA, DSC and DMA. Sulfur vulcanization resulted in higher elongation at break due to the flexibility of the sulfidic crosslinks. Carbon black resulted in better reinforcement compared to Sillitin. A higher ethylene and ENB content lead to higher hardness due to higher crystallinity and higher crosslink density, respectively.
Thermal ageing for up to 30 days (with 10 days intervals) took place in circulating hot air ovens at 125 °C. Pronounced crosslinking was found to take place in all peroxide-cured materials, as the unreacted double bonds of the ENB units acted as starting points for oxidation and crosslinking. Increasing the ethylene content resulted in an increase in the ageing resistance of EPDM. This improvement was attributed to the higher crystallinity that inhibits oxygen diffusion and to the smaller number of chain scissions which occur in the PP units. Although significant loss of the plasticizer was observed, the remaining plasticizer adequately improved the tensile properties of the material. The filler type did not significantly affect the ageing behavior of EPDM. Finally, the lower thermal stability of the sulfidic crosslinks resulted in desulfurization and, thus, in an increase in the crosslinking density.
To sum up, it has been shown that the monomer composition, curing agent and additives used in EPDM formulations greatly influence the properties and ageing resistance of these materials.
BAM is the federal institute for materials research and testing in Germany. One of our tasks is to evaluate the safety of casks designed for transport and/or storage of radioactive waste. As elastomeric seals are used in the containers as safety-relevant parts, it is our goal to be able to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. For this reason, an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) was started. Ageing was performed at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) for up to 2 years. For assessing properties related to the sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates. For comparison, uncompressed O-rings were aged as well. The aged materials were characterized with conventional polymer analysis methods such as hardness and tensile tests, but also with more seal-specific methods such as compression stress relaxation (CSR, reflecting the loss of sealing force of a compressed seal over time), and compression set (CS, representing the recovery behaviour of a seal after release from compression). CS is chosen as the property for lifetime prediction as it is both sensitive to degradation and related to the seal performance. CS data is extrapolated to 60 °C, which yields lifetimes of approximately 5 years for HNBR and 64 years for EPDM for a criterion of 85 % CS respectively, and approx. 40 years for FKM for a criterion of 65 % CS (the highest value measured so far).
At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the containers. Besides examining the low-temperature behaviour and irradiation effects of elastomeric seals, it is our goal to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1 year. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays constant or even decreases until shrinkage and the loss of resilience of the aged seal leads to the formation of a leakage path. This indicates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity for the degradation of the seal material.
At BAM, which is a federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the containers. Besides examining the low-temperature behaviour and irradiation effects of elastomeric seals, it is our goal to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used in seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1.5 years. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. In order to understand the underlying ageing mechanisms in each material, the change in material properties is examined using thermal and mechanical analysis. The experimental results indicate that while material properties, CSR and CS show considerable degradation effects, the leakage rate stays constant or even decreases until shrinkage and the loss of resilience of the aged seal leads to the formation of a leakage path. This indicates that static leakage rate, which is the most relevant criterion for seal performance, has only limited sensitivity for the degradation of the seal material.
Two polyethylene types with ultra high (UHMWPE) and high molecular weight (HMWPE), which are used as neutron radiation shielding materials in storage casks for radioactive waste, were subjected to gamma irradiation doses up to 600 kGy and subsequent thermal ageing at 125 °C for up to one year. One material was a medical grade UHMWPE and the other a HMWPE containing an antioxidant. Degradation effects in the materials were characterized using colorimetry, UV-Vis spectroscopy, MIR and FTIR measurements, DSC and, in the case of HMWPE, insoluble content determination. Both materials exhibited a yellowing upon irradiation. The discoloration of UHMWPE disappeared again after thermal ageing, which is why it was attributed to annealable color centers in the form of free radicals entrapped in the crystalline regions of the polymer that recombine during thermal ageing. Furthermore, oxidation species were observed with MIR and FTIR spectroscopy. For HMWPE, the yellowing occurred during both irradiation and thermal ageing and was correlated to antioxidant decomposition. Additionally, black spots were observed after thermal ageing of HMWPE that were attributed to reaction products of antioxidant derivatives and catalyst residues. While only little evidence of oxidation species was found in the light material parts, oxidation is expected to concentrate in the black spots as the catalyst residue promotes hydroperoxide decomposition and thus radical formation that initiate polymer oxidation
Renewable resources become more and more relevant to maintain energy demands for an increasing global population. Biosynthetic fuels like biodiesel might replace conventional petrochemical fuels, such as diesel. However, more research is needed to characterize the interaction between the different fuels and the polymeric material, especially with respect to ageing and degradation.
The poster will present several interaction and degradation phenomena of high density polyethylene (PE-HD) induced by diesel and biodiesel 1-3. Also the possible influence of microbial growth (fungi and bacteria) is considered. The chosen PE-HDs are typical thermoplastic resins for container and storage tank applications. Degradation of PE-HD will be investigated by changes of the mechanical properties – with main emphasis on the Charpy impact strength 2. Furthermore, with alternating sorption and desorption cycles in combination with oven ageing the co-oxidation 3 of PE-HD in contact with biodiesel will be addressed.
Industrial quality control (QC) nowadays requires the visualization of surface modifications from the macro-scopic to the microscopic or even nanoscopic scale. This is a prerequisite to the evaluation of functionality and reliability, the detection of defects and their separation of artefacts. The diversity of applications ranges from low-E glazings and solar panels, micro- and optoelectronics, micro- and smart devices to sensor-on-chip and lab-on-chip systems [1]. Optical microcopy (light, confocal laser scanning, white light interference) as established QC-tool is operated at normal incidence, i.e. p- and s-polarization are undistinguishable. Either light-intensity in terms of grey scale and colour or intensity-correlated effects of phase shifts are used. In case of ellipsometry, operated at oblique incidence, p- and s-polarization matter, and amplitude ratios and phase shifts upon reflection are measured. Hence, information content must be much higher.
The visualization of surface modifications may be very challenging for coating/substrate systems of either al-most identical optical constants, e.g. transparent films on substrates of the same material, or minor film thick-ness, substance quantity and affected area, e.g. ultra-thin or island films. Ellipsometry gives access to the con-trast of intensity (I), amplitude ratio (Ψ), and phase shift (Δ) with nanometer-scaled vertical and micrometer-scaled lateral sensitivity, one is able to identify tiny changes within an unmodified surface. As both mapping ellipsometry (ME) and imaging ellipsometry (IE) are operated in the optical far-field, surface inspection is also possible on the macroscopic scale. Near the Brewster-angle of the bare, undamaged, clean, and fresh substrate, the contrast to add-on and sub-off features is superior.
Fig. 1 shows three examples of ellipsometric imaging, i.e. a thin SnO:Ni film on SiO2/Si (Fig. 1a), a dried stain of an anti-body solution on cyclo-olefin-polymer (COP) shown in Fig. 1b, and a polyimide film residue on SiO2/Si (Fig. 1c). For all of these examples, ellipsometry provides much better contrast between substrate and surface modification than optical microscopy, sometimes primarily caused by the oblique incidence (Figs. 1a and 1c), in other cases related to the phase sensitivity of ellipsometry (Fig. 1b). Other examples are laser surface modifications and the corrosion of glass. In these cases, optical microscopy and IE yield to similar results, how-ever only ellipsometry gives access to modelling.
Further investigated coating/substrate systems are 100Cr6 steel, native oxide on silicon, borosilicate glass, and the polymer polycarbonate with deposited films of graphene and ta-C:H, printed and dried pattern of liquids such as water, cleaning agents, and dissolved silicone. Besides imaging ellipsometry, referenced spectral ellipsometry (RSE) has been applied, combining the advantages of both optical microscopy (fast measurement) and ellipsometry (high sensitivity to tiny modifications).