- AC weld pool support (2)
- Electron backscatter diffraction (2)
- Graphene (2)
- Kikuchi pattern (2)
- Wasserstoff (2)
- Welding of aluminum (2)
- Welding of thick metal plates (2)
- 3D FE-simulation (1)
- AC magnetic fields (1)
- Additive manufacturing (1)
Eingeladener Vortrag
- nein (8)
Aus wirtschaftlichen, konstruktiven sowie ästhetischen Aspekten werden moderne Stahlbaukonstruktionen immer schlanker und leichter ausgeführt. Dazu werden zunehmend hochfeste Feinkornbaustähle mit Dehngrenzen ≥ 690 MPa eingesetzt, wodurch eine Gewichtsreduzierung von 30 % bis 50 % und eine Kostenersparnis von 5 % bis 15 % erreicht werden kann.
Das Potential hochfester Feinkornbaustähle ist unter Beachtung der heutigen Richtlinien und Regelwerke jedoch nicht ohne weiteres nutzbar. Durch das Forschungsvorhaben wurde der Einfluss der Wärmeführung auf die Eigenspannungsausbildung und Kaltrissbildung unter Berücksichtigung realitätsnaher Steifigkeitsbedingungen untersucht. Auf der Grundlage dieser Erkenntnisse wurde ein Beitrag zur Verbesserung der Verarbeitungsrichtlinien erarbeitet, welche dem Verarbeiter eine sichere schweißtechnische Verarbeitung bei verbesserter Ausnutzung der Materialeigenschaften ermöglicht. Vor allem die Tragfähigkeit und die Sicherheit der Schweißverbindung bestimmen die Bemessung der Konstruktion und somit den nachhaltigen und ökonomischen Einsatz dieser Güten. Der Zusammenhang zwischen der Höhe der entstehenden Eigenspannungen und der Wärmeführung in realen Konstruktionen ist zurzeit nur qualitativ überschaubar und führt zu einer eher konservativen Auslegung heutiger Schweißkonstruktionen. Die wirtschaftliche Verarbeitung hochfester Stähle wird neben dem Erreichen anforderungsgerechter mechanischer Eigenschaften im Schweißnahtbereich vor allem durch die Vermeidung von Kaltrissen bestimmt. Die diesbezüglichen Empfehlungen in den geltenden Regelwerken beruhen jedoch vornehmlich auf Erkenntnissen aus Laborschweißungen an Kleinproben unter freier äußerer Schrumpfung. Die Hauptursachen für die Entstehung von Eigenspannungen wie inhomogene, lokale Erwärmung und Abkühlung der schweißnahtnahen Bereiche und insbesondere die konstruktive Schrumpfbehinderung infolge umgebender Montagegruppen werden damit jedoch nicht abgebildet. Der Einfluss der Wärmeführung, insbesondere der lokalen Vorwärmung, auf die Eigenbeanspruchung einer Konstruktion ist derzeit weitgehend unbekannt.
Ziel des Forschungsvorhabens war es, den Einfluss der Wärmeführung auf die Eigenspannungsausbildung in geschweißten Konstruktionen zu quantifizieren sowie Aussagen zur Beeinflussung und Absenkung der Eigenspannungen und somit der Gesamteigenbeanspruchung von Schweißkonstruktionen zu erarbeiten. Dazu wurden durch die sukzessive Steigerung des Einspanngrades der Zusammenhang zwischen Wärmeführung und resultierender Eigenspannung unter zusätzlicher Schrumpfbehinderung geklärt. Ferner wurde die Übertragbarkeit der den Regelwerken zugrundeliegenden Kleinprobenergebnisse auf reale Konstruktionen untersucht. Mithilfe systematischer Klein- und Großlastschweißversuche an definiert schrumpfbehinderten Proben konnte der Einfluss der Wärmeführung sowohl auf die lokalen nahtnahen Eigenspannungen als auch globale Eigenbeanspruchungen durch Reaktionsspannungen analysiert werden. Es zeigte sich, dass eine Reduktion der lokalen Eigenspannungen und der Eigenbeanspruchung von geschweißten Konstruktionen durch eine geringere Wärmeeinbringung möglich ist. Eine Absenkung der Zwischenlagentemperatur erwies sich dabei unter anderem als besonders günstig. Damit ist es möglich vorhandene Wärmeführungskonzepte für hochfeste Stähle zu optimieren und dadurch die Kaltrissbildung zu vermeiden.
Aus der Möglichkeit mittels Zentrifugentechnologie bis zu 8 Proben gleichzeitig einer Zugprüfung unter wirklich identischen Bedingungen, schnell über einfaches Einstecken der Proben und unter Ausschluss jeglicher Querkräfte, zu unterziehen , ergab sich für Klebverbindungen erstmals die Möglichkeit einer statistisch abgesicherten Prüfung identischer bzw. einer vergleichend bewertenden Prüfung unterschiedlicher Verbundsysteme. Es war deshalb naheliegend, auch das Aufkleben der Prüfstempel unter möglichst identischen Bedingungen und ebenfalls frei von Querkräften im OKTETT durchzuführen. Außerdem sind beim durchgehenden Handling im OKTETT die identische Vorbehandlung vor dem Kleben, identische Transferzeiten und -bedingungen zwischen den verschiedenen Prozessschritten, eine weitgehend gleichartige Klebstoffaufbereitung und -applikation sowie die bessere Einhaltung von gleichen Verarbeitungs- und Aushärtezeiten der Klebstoffe vor der Prüfung der Verbundfestigkeit für jeweils 8 Proben sichergestellt. Im Ergebnis dieser Überlegungen stellte sich schnell heraus, dass das Mehr-Proben-Kleben unter identischen Bedingungen für in Grenzen unterschiedliche Verbundsysteme eine ungelöste Aufgabenstellung ist.
Today’s light weight design trends lead to a growing application of high-strength structural steels (yield strength ≥ 690 MPa). The mechanical properties of the weld and the component safety have to meet the increased requirements of these steel grades. However, high residual stresses in welded components are detrimental to their safety and integrity. Analyses concerning weld stresses in high-strength steels welded under component related restraint conditions revealed that heat control significantly affects global and local stresses. This occurs especially in highly restrained joints due to superimposing local and global stresses and may cause crack-critical stress-levels. In this study weld tests were performed with plates of high-strength steel in a special test facility. The experimental setup allowed transferring defined restraint conditions to the test welds similarly to real components. Temperature and reaction forces due to restraint were observed online while welding and cooling of multilayer-component MAG-welds. Mobile X-ray diffraction was used for local stress determination in the weld seam areas of the restrained specimens. It was found that interpass temperature has a major influence on the local and global welding forces and stresses. Thus, among the analysed results especially transverse residual stresses of the heat affected zone were strongly affected.
Chemischer Angriff auf Betonbauwerke - Bewertung des Angriffsgrads und geeignete Schutzprinzipien
(2014)
In verschiedenen Bereichen des Betonbaus ist Beton einem chemischen Angriff von außen ausgesetzt, der die Dauerhaftigkeit des betreffenden Bauteils bzw. des gesamten Bauwerks beeinträchtigen kann. Für einen chemischen Angriff in natürlichen Böden und Grundwässern bestehen normative Vorgaben in DIN 4030-1 [R10] bzw. DIN 1045-2 [R19], um den Angriffsgrad anhand der Art und Konzentration der angreifenden Stoffe in Expositionsklassen XA1 (schwach angreifend) bis XA3 (stark angreifend) einzustufen. Hinsichtlich weiterer maßgeblicher Einflussfaktoren wird an dieser Stelle nicht näher differenziert, ob und inwieweit die Regelungen für Böden und Grundwässer auch auf andere Bereiche mit chemischem Angriff auf Beton zu übertragen sind, ist stets im Einzelfall zu überprüfen. Ebenfalls sind die zu treffenden Maßnahmen über die Vorgaben der DIN EN 206-1/DIN 1045-2 [R19] hinaus anwendungsspezifisch festzulegen. Der Hauptausschuss Baustofftechnik (HABT) des DBV hat daher den Arbeitskreis "Chemischer Angriff auf Beton" beauftragt, dieses Merkblatt zu erarbeiten, das Hilfestellung bei der Bewertung einer projektspezifischen chemischen Angriffssituation auf Beton sowie bei der Planung und Ausführung von Schutzprinzipien leisten soll.
Emergency response units increasingly use pressure cylinders made from fibre composites for breathing air as elements of personal protective equipment (PPE). Such applications expose the composite cylinders to harsh temperature and handling conditions. At least in Europe, standards have been used for certifying PPE, which are designed and mandatory for the approval of pressure receptacles for the transport of dangerous goods. Therefore, service conditions specific to PPEs are not accounted for in these standards. In this paper, BAM (Federal Institute for Materials Research and Testing) investigates the residual safety of a composite cylinder design at the end of their designated service life of 15 years. The cylinders (test pressure PH 450 bars; 6.8 Litres) are of one design type with aluminium liner and fully wrapped with carbon fibres, which is commonly considered a “Type III” cylinder. All cylinders were used as PPE by the Berlin fire department and randomly picked in three samples of 25 cylinders each before tested.
At BAM, the cylinder samples underwent hydraulic load cycle tests (LCT), conventional burst tests (BT) and so called slow burst tests (SBT). A concept for quantification of strength degradation already introduced by BAM was applied. This concept is based on a probabilistic assessment of the average strength and scatter of each sample of cylinders. The strength distributions of the used PPEcylinders is shown and analysed. Some unexpected effects are shown and a refinement of the statistical assessment is introduced.
The impact of pressure, sliding velocity and property variation of constituents on the sliding behaviour of a model tribofilm was studied with the method of movable cellular automata (MCA). Whereas a clear pressure dependency of the coefficient of friction (COF) was always observed and could be correlated with the structure formation in terms of varying thickness of a mechanically mixed layer, the impact of the other parameters was either negligible or rather weak. Only if a brittle-to-ductile Transition of the oxide-based tribofilm was assumed, a significant decrease in the COF level was predicted.
Temperature-dependent property changes can be neglected during MCA modelling, unless this transition takes place. For magnetite-based tribofilms, the transition temperature is beyond 800 °C, i.e. a temperature leading to fading effects during braking anyway. Thus, it could be concluded that, except for very severe braking conditions, sliding simulations with the MCA method yield meaningful results without considering temperature-dependent mechanical properties.
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements