The use of coconut fiber (CF) agricultural waste was considered as an environmentally friendly and inexpensive alternative in flame retarded biocomposites. To decrease the high content of aluminum trihydrate (ATH) required, the thermal decomposition (thermogravimetry), flammability [oxygen index (LOI) and UL 94 test] and fire behavior (cone calorimeter) of a combination of CF and ATH were investigated in a commercial blend of thermoplastic starch (TPS) and cellulose derivatives. CF induced some charring activity, slightly decreasing the fire load and burning propensity in cone calorimeter test. ATH decomposes endothermically into water and inorganic residue. Significant fuel dilution as well as a pronounced residual protection layer reduces the fire hazards. Replacing a part of ATH with coconut fibers resulted in improved flame retardancy in terms of ignition, reaction to small flame, and flame-spread characteristics [heat release rate (HRR), fire growth rate (FIGRA), etc.]. The observed ATH and CF synergy opens the door to significant reduction of the ATH contents and thus to interesting flame retarded biocomposites.
Effect of well dispersed amorphous silicon dioxide in flame retarded styrene butadiene rubber
(2013)
Spherically shaped amorphous silicon dioxide with broad size particle distribution was used in combination with aluminium trihydroxide (ATH) in styrene butadiene rubber composites. The pyrolysis, flammability, fire properties, flame spread and gas diffusion were investigated. The kind and amount of ATH, but in particular the fine silicon dioxide chosen as an additive, influenced the thermal decomposition and fire behaviour of styrene butadiene rubber composites. Gravimetric gas sorption measurements showed that the gas diffusion was systematically lower with silicon dioxide. The initial pyrolysis gas release was hindered, increasing the temperature at which decomposition begins as well as the ignition time in fire tests. During combustion, ATH and silicon dioxide accumulate on the surface of the specimen, forming a residual protective layer. A reduced peak heat release rate and fire spread were observed. The addition of a special kind of silicon dioxide is proposed to play a key role in optimising fire retardancy.