AbstractViscous healing of cracks induced by the Vickers indentation in a soda lime magnesium silicate, a soda borosilicate, and a soda aluminosilicate glass (NAS) was studied by laser scanning microscopy. Plots of the crack length, width, and depth normalized to the initial crack length versus time over viscosity merge into single master curves of each of these quantities for each glass. Despite glass properties do not differ strikingly from each other, however, these master curves strongly differ among the glasses. This finding was attributed to a different interplay of various crack healing phenomena. Lateral cracks were found to be responsible for the bulging of the sample surface around the Vickers imprint, which in turn promotes radial crack widening as the main cause of healing delay. The most rapid healing of lateral cracks was observed in NAS in which bulging and crack widening were least pronounced.
To explore the impact of ambient and structural water on static fatigue, the initiation and growth of 3279 Vickers induced median radial cracks were automatically recorded and analyzed. We find that humidity is more efficient in initiating cracks and promoting their growth than water, which is dissolved in the glass structure. In particular for slow crack growth (< 3x10-6 m s-1), tests in dry nitrogen showed a considerable decrease in the crack growth exponent with increasing water content of the glasses. On the other hand, if tests were performed in humid air, the crack growth exponent was independent of the water content of the hydrous glasses, while stress intensity decreased slightly. These observations indicate that water promotes the processes at the crack-tip regardless of its origin. However, ambient water is more efficient.
Due to the stochastic nature of crack nucleation by Vickers indentation, a statistical analysis of propagation rates of 185 radial cracks was performed. Crack growth was observed directly using a video camera with high Image acquisition rate. It is found that propagation rates are controlled by the environmental reactions at the crack-tip shortly after their initiation (< 1 s). Calibration of the stress intensity KI showed that the residual stress factor χ and the exponent n of the equation KI==χPc−n (with P==load and c==crack length) are broadly distributed among the 185 analyzed cracks, ranging from 10−16 to 104 and from 0.1 to 5, respectively. For the most frequent crack, the equation KI==0.052Pc−1.47 holds. The results show that correlations of indentation-induced crack length to stress intensity necessitate the use of statistical significant data that are calibrated by the environmental reactions at the crack-tip.
Surface water-induced broadening of crack initiation probability of zinc aluminosilicate glasses
(2017)
The crack generation probability by Vickers indentation of glass surfaces is known to be influenced by the atmospheric conditions under which the Vickers experiment is performed [1]. However, the effect of surface water due to preparation and storage of the glass surfaces prior to the indentation is less understood. Therefore, zinc aluminosilicate glasses of perzinc, peraluminous as well as nominally NBO-free meta-aluminous composition were prepared by melt quenching. Surfaces of cut and polished specimens of these glasses were either stored for seven days under constant atmosphere (50 °C; 55% RH) or etched (HF: 20vol%; 20 min) shortly before indentation. The obtained results show a strong variation of crack initiation behavior depending on chemical composition of the glasses as well as sample preparation. All experiments were performed in dry nitrogen gas to minimize the influence of atmospheric humidity during indentation. While the regular glass surfaces exposed to humid air prior to Vickers indentation show a broad distribution of crack initiation probability, this distribution narrows down if etched glass surfaces are tested. SNMS depth profiling shows a water enriched layer at the surface (150 μm) for the non-etched and stored specimens leading to the conclusion that surface water causes broadening of the crack initiation probability of glass surfaces.
Zinc aluminosilicate glasses are studied by Vickers indentation in order to reveal the effect of non-bridging oxygen (NBO) and incorporation of aluminium in the silica network on micromechanical properties. Therefore glasses of perzinc and peraluminous compositions as well as nominal NBO-free glasses on the meta-aluminous join are prepared by melt quenching.
To investigate the effect of environment on hardness, crack generation and propagation indentation was performed in air and in dry nitrogen atmosphere on HF etched surfaces. For constant silica fractions the increase in the Zn-to-Al ratio led to a characteristic step-like course of the micromechanical properties at the meta-aluminous composition.
The effect of the cation size is verified by comparing the results with those obtained in the calcia-alumina-silica system.