Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene
(2024)
The craze‐crack mechanism occurring in high‐density polyethylene (HDPE) causing slow crack growth and environmental stress cracking is investigated in detail with respect to the relation of crack length and the related craze zone. This is essential for the understanding of the resulting features of the formed fracture surface and their interpretation in the context of the transition from crack propagation to ductile shear deformation. It turns out that an already formed craze zone does not inevitably result in formation of a propagating crack, but could also undergo ductile failure. For the examination, the full notch creep test (FNCT) was employed with a subsequent advanced fracture surface analysis that was performed using various imaging techniques: light microscopy, laser scanning microscopy, scanning electron microscopy, and X‐ray micro computed tomography scan. FNCT specimens were progressively damaged for increasing durations under standard test conditions applying Arkopal, the standard surfactant solution, and biodiesel as test media were used to analyze the stepwise growth of cracks and crazes. From considerations based on well‐established fracture mechanics approaches, a theoretical correlation between the length of the actual crack and the length of the preceding craze zone was established that could be evidenced and affirmed by FNCT fracture surface analysis. Moreover, the yield strength of a HDPE material exposed to a certain medium as detected by a classic tensile test was found to be the crucial value of true stress to induce the transition from crack propagation due to the craze‐crack mechanism to shear deformation during FNCT measurements.
Highlights
- Progress of crack formation in high‐density polyethylene is analyzed by different imaging techniques
- Determined growth rates depend on distinction between craze zone and crack
- The ratio of the present crack to the anteceding craze zone is validated theoretically
- The transition from crack propagation to ductile shear deformation is identified
- An already formed craze zone may still fail by ductile mechanisms
Characteristics of environmental stress cracking of PE-HD induced by biodiesel and diesel fuels
(2024)
In the context of the increasing effect of carbon dioxide emissions on the global climate biodiesel produced from renewable sources has emerged as a promising contender replacing fossil fuels, especially in long-range transport vehicles, using existing engines and infrastructure.
High-density polyethylene is one of the prevailing materials for pipe and container applications for storage and transport of such fuels, both, from fossil and renewable resources. The contact with the respective fuels raises questions concerning material compatibility as biodiesel exhibits significant differences compared to conventional diesel fuel affecting its sorption and plasticization behavior in polyethylene. In this study, its behavior with respect to environmental stress cracking, considered one of the most frequent damage mechanisms leading to failure of polymer parts and packaging, was evaluated using the well-established Full Notch Creep Test. This
approach allows for a detailed fracture surface analysis using imaging techniques, such as optical and laser scanning microscopy, as well as infrared spectroscopy. Comparing the environmental stress cracking behavior in standard surfactant solutions with that in biodiesel and diesel, respective crack propagation rates, showing different levels of acceleration, were determined and details of the underlying mechanisms could be revealed.
Furthermore, the specific infrared absorption of the biodiesel’s ester functionality allows its semi-quantitative determination on the fracture surface of the tested specimens after failure. Thus, a preferred uptake of sorptive fluids in the fracture zone due to local morphological changes of the polyethylene could be directly evidenced by infrared spectroscopy.
A phenomenological criterion for an optical assessment of PE-HD fracture surfaces obtained from FNCT
(2021)
The full-notch creep test (FNCT) is a common test method to evaluate the environmental stress cracking (ESC) behavior of high-density polyethylene (PE-HD), e.g. for container materials. The test procedure as specified in ISO 16770 provides a comparative measure of the resistance against ESC using the time to failure of PE-HD specimens under constant mechanical load in a well-defined liquid test environment. Since the craze-crack damage mechanism underlying the ESC phenomenon is associated with brittle failure, the occurrence of a predominantly brittle fracture surface is a prerequisite to consider an FNCT measurement as representative for ESC, i.e. a time to failure dominated by craze-crack propagation.
The craze-crack propagation continuously reduces the effective residual cross-sectional area of the specimen during the test, which results in a corresponding increase of the effective mechanical stress. Thus, a transition to ductile shear deformation is inevitable at later stages of the test, leading usually to a pronounced central ligament.
Therefore, an optical evaluation of FNCT fracture surfaces concerning their brittleness is essential. An enhanced imaging analysis of FNCT fracture surfaces enables a detailed assessment of craze-crack Propagation during ESC. In this study, laser scanning microscopy (LSM) was employed to evaluate whether FNCT fracture surfaces are representative with respect to craze-crack propagation and ESC. Based on LSM height data, a phenomenological criterion is proposed to assess the validity of distinct FNCT measurements. This criterion is
supposed to facilitate a quick evaluation of FNCT results in practical routine testing. Its applicability is verified on a sample basis for seven different commercial PE-HD container materials.
The full-notch creep test (FNCT) is a common method to evaluate the environmental stress cracking (ESC) behavior of high-density polyethylene (PE-HD) container materials . The test procedure as specified in ISO 16770 provides a comparative measure of the resistance against ESC using the time to failure of specimens mechanically loaded in a well-defined liquid environment. Since the craze-crack damage mechanism underlying the ESC process is associated with brittle failure, the occurrence of globally brittle fracture surfaces is a prerequisite to consider an FNCT measurement as representative for ESC . Therefore, an optical evaluation of FNCT fracture surfaces concerning their brittleness is essential. Due to the experimental setup, an inevitable increase of the true mechanical stress and the associated appearance of small ductile parts on fracture surfaces is induced in any case. Hence, an FNCT experiment is considered as 'valid', if the corresponding fracture surface is predominantly brittle . Based on laser scanning microscopy (LSM) height data of FNCT fracture surfaces , a universal and easy-to-use phenomenological criterion was developed to assess the validity of distinct FNCT experiments. This criterion is supposed to facilitate a quick evaluation of FNCT results in practical routine testing.
As the well-known damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC) are the major causes for possible failure of polyolefin-based materials, especially for PE-HD, they are highly relevant and need to be considered thoroughly. Furthermore, due to slight but perceptible differences in damaging effect, a differentiation between SCG and ESC is expedient. SCG appears in “inert” or “neutral” media without a decisive influence of the surrounding medium whereas ESC occurs in “active” media, which influence the failure behavior and time to failure crucially.
To characterize the inherent resistance of the material against those damage mechanisms, the well-established Full-Notch Creep Test (FNCT) is used. In this study, the FNCT – usually applied according to ISO 16770 [3] using a few universal model liquid media and mainly for pipe materials – is extended by investigations with appropriate parameters of selected relevant PE-HD container materials also in real media, such as the topical fuels diesel and biodiesel. The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Especially, mechanical stress and temperature were varied systematically during FNCT and time to failure values, time-dependent elongation data as well as detailed fracture surface analysis by laser scanning microscopy (LSM) were combined for the first time (Fig. 1). Particularly, the fracture surface analysis provides a sound basis to characterize failure behavior, mainly regarding the balance between brittle crack propagation and ductile deformation. Therefore, fracture surface analysis is an essential tool for a decent assessment of SCG and ESC by FNCT measurements.
Different imaging techniques were employed to monitor Full Notch Creep Test (FNCT) experiments addressing environmental stress cracking in more detail. The FNCT is a well-established test method to assess slow crack growth and environmental stress cracking of polymer materials, especially polyethylene. The standard test procedure, as specified in ISO 16770, provides a simple comparative measure of the resistance to crack growth of a certain material based on the overall time to failure when loaded with a well-defined mechanical stress and immersed in a liquid medium promoting crack propagation.
Destructive techniques which require a direct view on the free fracture surface, such as light microscopy and laser scanning microscopy, are compared to non-destructive techniques, i.e. scanning acoustic microscopy and xray micro computed tomography. All methods allow the determination of an effective crack length. Based on a series of FNCT specimens progressively damaged for varied Durations under standard test conditions, the estimation of crack propagation rates is also enabled. Despite systematic deviations related to the respective Imaging techniques, this nevertheless provides a valuable tool for the detailed evaluation of the FNCT and its further development.
Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications.
Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant mechanisms of damage. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure. To characterize the intrinsic resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used and of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD.
In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigations of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed. The underlying diffusion-controlled sorption process was assessed before comparing non-saturated specimens with samples previously saturated with sorbing media.
The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
In addition to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Fracture surface analysis (LM, LSM) and quasi in-situ imaging (CT scan) via measurement in different load stages are considered explicitly. Correlations of elongation behavior and data derived from imaging analysis such as fracture plane roughness and height of areas of ductile deformation were obtained.
Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications.
Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant damage mechanisms. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure. To characterize the inherent resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used. Therefore, the FNCT is of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD – especially in the field of polymer development and improvement for high-performance applications.
In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigation of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed.
The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Additional to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Correlations of elongation behavior and data derived from imaging analysis were obtained.
The damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC), relevant for PE-HD materials are characterized based on improved full notch creep testing (FNCT) of two selected typical PE-HD materials for container applications. In this context, a distinction of the failure mechanisms as well as a categorization of involved media is suggested. Employing a novel FNCT device, elongation data were obtained in addition to conventional time-to-failure results of stress-dependent as well as temperature-dependent measurements. Changes in failure behavior, as determined by fracture surface analysis based on light microscopy (LM) and laser scanning microscopy (LSM), are correlated with FNCT results and used to introduce an additional possibility for the identification of brittle/ductile fracture behavior.
The full-notch creep test (FNCT) is widely used to characterize the slow crack growth (SCG) behavior of polyolefin materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure. The test is of greatest importance for pipe and blow molding types of polyethylene, high density (PE-HD). Usually the full-notch creep test is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100. In our study, selected relevant polyethylene, high density materials are investigated also in real media – practical formulations as well as representative pure chemicals – and influences of temperature and geometry of specimen and notch are explicitly addressed. Furthermore, the investigations comprise also the environmental stress cracking behavior of polyethylene, high density in media that are sorbed to a significant extent – examples are diesel and biodiesel – based on comparison with samples previously saturated with those media. Thus, also the underlying diffusion controlled sorption process has to be assessed before. The investigations were performed using a full-notch creep testing device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.