Based on state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a recently started German joint research project between BAM Berlin and MPA Stuttgart. This paper outlines the research approach and the planned investigations and provides first results.
According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as interim and final storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods under dynamic loading conditions. Within fracture mechanics safety assessments for steels in nuclear technology, the probabilistic MC concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. The MC concept allows for an effective statistical consideration of the scatter of the material toughness in the transition regime. Furthermore, the MC can also be used for elevated loading rates as they occur in accident or crash scenarios. However, for DCI, a systematic review of potential modifications to the MC assumptions and procedure according to ASTM E1921 and an associated validation are still lacking. Therefore, a corresponding methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component.
For the experimental program, a DCI material was produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests is planned. A comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Moreover, numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered, and modifications will be made if necessary.
CHG is very different compared to other graphite degenerations or defects;
Filigree, multi-branched string-like, 3d interconnected structure;
Morphology and volumetric amount of CHG cannot be accessed by stereological interpretation of 2d section data;
Field-tested, technically established method to quantify CHG in components not available;
Fatigue: CHG causes substantial reduction in fatigue limit and significant increase in crack growth rate;
Therefore: Avoid or exclude CHG!
Experimental determination and analysis of dynamic fracture toughness data of ductile cast iron
(2017)
Ductile Cast Iron materials (DCI) have become important structural materials. Neverthe-less, to draw maximum benefit from DCIs property potential, tailored testing methods must be provided. The established dynamic Jd-R and CTOD 5d-R curve procedures are based on material specifically developed, independent experimental techniques but pro-vide almost matching results. This can be seen as additional validation of the Jd procedure which was mandatory.
Experimental determination and analysis of dynamic fracture toughness data of ductile cast iron
(2017)
Ductile Cast Iron materials (DCI) have become important structural materials. Neverthe-less, to draw maximum benefit from DCIs property potential, tailored testing methods must be provided. The established dynamic Jd-R and CTOD 5d-R curve procedures are based on material specifically developed, independent experimental techniques but pro-vide almost matching results. This can be seen as additional validation of the Jd procedure which was mandatory.
Fracture mechanics based component design requires appropriate fracture mechanics toughness data with respect to both, loading rate as well as test temperature. Taking high-rate loading into account such as with accidental scenarios, different standards such as ASTM E 1820 or BS 7448-3 provide some information on dynamic fracture mechanics testing. Nevertheless, the designations differ so that a validation of the own material specific test method used for dynamic R-curve determination is mandatory. In order to address this for ductile cast iron materials an experimental method for the reliable determination of dynamic J-integral crack resistance curves at -40 °C following the multiple specimen approach has been established and validated. The experimental concept offers some additional valuable features. Single values of dynamic crack initiation toughness can be determined using a single specimen technique based on crack sensors. Furthermore, an experimentally independent method is provided according to which CTOD δ5 R-curves can be established. The focus of the present paper is on the validation of the experimental low blow technique using a drop tower test system.
A drop tower test system was developed and set up to perform low blow tests at temperatures down to -40 °C. The system allows for a variation of the impact mass and height and was optimized for testing of ductile cast iron at stress intensity rates from approximately 5∙10⁴ to 3∙10⁵ MPa√ms⁻¹. This range of loading rate is characteristic for instance with crash scenarios of heavy sectioned DCI casks for radioactive materials. In order to address characteristic challenges of impact tests (test duration of microseconds up to milliseconds, inertial effects, signal oscillations), an appropriate full bridge strain gage method for the measurement of force directly on the specimen as well as a non-contact measurement of load line displacement using an optical extensometer have been developed and validated.
The low blow test requires either to prevent bouncing strikes of the hammer by using the stop block technique or to catch the hammer after its first strike. Both options are not part of the experimental concept and setup which have been realized here. The paper describes investigations which have been performed in order to make sure that bouncing strikes of the hammer do not cause additional crack extension in the specimen. This is necessary to ensure a unique relation between the work done and the achieved crack extension. The investigations covered the analysis of limit loads of the specimen with respect to the measured force. The measured stiffness of the specimen was assessed and signals of crack sensors were analyzed. Furthermore, an analysis of the mechanical behavior of the loading system and the specimen by optical observation was performed. Corresponding results are discussed in the paper. It had finally been proven that additional crack extension in the specimen due to bouncing strikes of the hammer is not to be expected under the given conditions of test setup, material and loading. It can be seen as a major experimental advantage that the striker does not have to be catched after the low blow test.