This article refers to the research article entitled “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times” [1]. It presents experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Such service-like (SL) tests with additional long-term stress- and strain-controlled dwell times are non-standard, rare, and expensive, making these data very valuable. They may be used to approximate cyclic softening in the technically relevant range, for the design of complex SL experiments, or for detailed analyses of stress-strain hystereses (e.g., for stress or strain partitioning methods, for the determination of hysteresis energies (work), inelastic strain components, etc.). In addition, the latter analyses may supply important input for advanced parametric lifetime modeling of components under creep-fatigue loading or model calibration parameters.
The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress.
Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue.
9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep and oxidation resistance. The growing share of renewable energy sources in power generation forces many of these plants into more flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue. The present contribution reports on current findings obtained in a multidisciplinary project which combines cyclic mechanical and cyclic oxidation testing of different 9-12% Cr grades with detailed microstructural analyses.
Mechanical analyses are carried out on P92 and P91 steel grades to give an overview of softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of creep and fatigue periods.
Complementary microstructural investigations by scanning and transmission electron microscopy plus EBSD are used for phase identification, substrate/oxide interface characterization and quantification of the microstructure evolution under cyclic conditions.
In recent years, the performance of heat resistant ferritic-martensitic steels under cyclic oxidation and cyclic mechanical loading has gained considerable attention. The growing contributions of renewable energy sources to electricity generation have triggered a shift from continuous (baseload) operation of conventional power plants towards cyclic or “flexible” operation, which is needed to stabilize the electric grids by balancing the highly variable renewable’s input.
Compared to the impressive amount of data on isothermal oxidation/corrosion and static
mechanical loading (creep) that was compiled over decades, only little and sometimes
contradictory information is so far available on the reaction of these alloys to cyclic
conditions. The latter may involve frequent transients or holds at intermediate temperatures, as well as shut-downs and start-ups with high temperature rates which result in cyclic mechanical loads (thermo-mechanical fatigue, TMF) and thermo-cyclic oxidation at variable temperature.
Our contribution will report on recent findings obtained within the framework of a junior
research group which investigates the oxidation and fatigue of the ferritic-martensitic grades P91, P92 and VM12 SHC under thermo-cyclic conditions. Cyclic oxidation tests are carried out in steam using different sample shapes (flat coupons, U-segments and rings taken from heat exchanger tubes). Special attention is paid to changes in the kinetics and the integrity and possible delamination/spalling of the oxide layers. Mechanical tests are carried out on material from real steam pipes with a focus on the softening behaviour and lifetime issues resulting from combined creep/TMF loadings. All experiments are carried out in the 300-620°C regime with temperature and load profiles that resemble typical loading scenarios in power plants and are complemented by detailed microstructural characterisation.