A series of field exposure tests according to ISO 9223 up to 9226 was carried out at different locations to determine the corrosivity and the corrosion progress of different test sites throughout northern and eastern Germany. Standard test specimens of steel, zinc, copper and aluminium were exposed to rural, city and marine atmosphere at test sites of the Bundesanstalt für Materialforschung und -prüfung (BAM). Test sites at city atmosphere comprised exposure on a rooftop, next to a highly frequented road and directly at a motorway. Exposure under marine conditions was carried out at Heligoland in the North Sea. The specimens were stored under sheltered and unsheltered conditions on each test site, respectively. Corrosion rates after the first year of field exposure were determined and used for the classification of the atmospheres and the test sites regarding the corrosivity category.
Results after the first year of exposure were presented at the EUROCORR 2018 in Cracow. The current presentation will present an update of results of the systematic study after five years of exposure. The corrosion progress and the mass loss of the standard metals steel, zinc, copper and aluminium will be presented and discussed with respect to the atmospheric conditions and the time of wetness at the test sites. In addition, the difference between sheltered and unsheltered conditions will be discussed.
Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt.
Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt.
A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistanc-es can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented.
The double loop electrochemical potentiodynamic reactivation (EPR) method is a standardised procedure for detecting and quantifying sensitisation on austenitic, ferritic and ferritic-austenitic stainless-steel grades. This sensitisation is caused by microstructural alternations, as the formation of chromium carbides, nitrides or sigma-phases, which generate local chromium depleted zones nearby. The latter strongly influence the corrosion resistance and the electrochemical response of a stainless steel during electrochemical potentiodynamic reactivation, providing important information on the degree of chromium depletion. In case of martensitic stainless steels, which are used for cutlery and surgical instruments, the heat treatment has a strong impact on the microstructure, the material properties and especially on the corrosion resistance. To study this interaction, the EPR method was modified for the application on martensitic stainless steels with about 13 wt.-% chromium. Different H2SO4 concentrations and EPR-parameters were tested and compared on two standard martensitic stainless-steel grades (AISI 420 A / X20Cr13 and AISI 420 C / X46Cr13) to define applicable parameters. Afterwards, these parameters were used to study the effect of austenitisation time and cooling rate on the corrosion resistance of both martensitic stainless steels. The response of both alloys was different due to the different carbon levels, which will be explained by microstructural investigations in detail. All results allow postulating a process window, in which chromium depletion is suppressed and an optimised corrosion resistance is guaranteed. Based on this research, the modified EPR-test is now used to control the heat treatment and its impact on the corrosion resistance of martensitic stainless steels in the cutlery industry. The EPR-test is thus an interesting alternative for manufacturers, processors, users and researchers to the time-consuming exposition test normally used to characterise the corrosion resistance of martensitic stainless steels.
The corrosion resistance of stainless-steels grades is of high importance for the technical safety in different environmental conditions. Processing and surface finish influences the corrosion resistance of ferritic stainless steels, which may be considered for some application in marine environment. Three ferritic stainless steel alloys (X2CrNi12, X2CrTiNb18 and X2CrMoTi18-2) were exposed in four different surface finishes (rolled, dry grinding, glass beaded and electro polished) for five years in marine environment to obtain reliable information about the corrosion resistance. All samples were assessed after 22 and 60 months according to DIN EN ISO 10289 in validation degrees from 1 to 10. Complementary investigation using accelerated chamber test (salt spray test followed by four weeks storage at 30 °C / 80 % relative humidity) and short-term electrochemical methods (electrochemical potentiodynamic reactivation, pitting potentials and the KorroPad method) were conducted to compare their results. The presentation gives an overview on all methods and the generated results, which show benefits and restrictions of long-term, accelerated and short-term corrosion tests.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten unter verschiedenen klimatischen Bedingungen erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von Untersuchungen mit gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten erlauben. Der Vortrag stellt das Promotionsthema vor und erläutert die Untersuchungsschwerpunkte.