The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.