Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2022 (109) (entfernen)
Dokumenttyp
- Vortrag (64)
- Zeitschriftenartikel (26)
- Beitrag zu einem Tagungsband (12)
- Posterpräsentation (3)
- Monografie (1)
- Buchkapitel (1)
- Dissertation (1)
- Sonstiges (1)
Schlagworte
- Additive Fertigung (20)
- Additive manufacturing (17)
- Alloy 36 (12)
- Ultraschallunterstütztes Fräsen (12)
- Eigenspannungen (11)
- Ultrasonic-assisted milling (11)
- Hochfester Stahl (10)
- Surface integrity (10)
- Additive Manufacturing (9)
- MAG-Schweißen (9)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (109) (entfernen)
Eingeladener Vortrag
- nein (64)
Laser Powder Bed Fusion (L-PBF) allow the fabrication of lightweight near net shape AlSi10Mg components attractive to the aerospace, automotive, biomedical and military industries. During the build-up process, high cooling rates occur. Thus, L-PBF AlSi10Mg alloys exhibit a Si-nanostructure in the as-built condition, which leads to superior mechanical properties compared to conventional cast materials. At the same time, such high thermal gradients generally involve a deleterious residual stress (RS) state that needs to be assessed during the design process, before placing a component in service. To this purpose post-process heat treatments are commonly performed to relieve detrimental RS. In this contribution two low-temperature stress-relief heat treatments (SRHT) are studied and compared with the as-built state: a SRHT at 265°C for 1 hour and a SRHT at 300°C for 2 hours. At these temperatures microstructural changes occur. In the as-built state, Si atoms are supersaturated in the α-aluminium matrix, which is enveloped by a eutectic Si-network. At 265°C the Si precipitation from the matrix to the pre-existing network is triggered. Thereafter, above 295°C the fragmentation and spheroidization of the Si branches takes place, presumably by Al–Si interdiffusion. After 2 hours the original eutectic network is completely replaced by uniformly distributed blocky particles. The effect of the heat and the microstructure modification on the RS state and the fatigue properties is investigated. Energy dispersive x-ray and neutron diffraction are combined to investigate the near-surface and bulk RS state of a L-PBF AlSi10Mg material. Differences in the endurance limit are evaluated experimentally by high cycle fatigue (HCF) tests and cyclic R-curve determination.
n this work, three classes of fatigue models are reviewed according to the fatigue regimes commonly considered in the current components design. Particular attention is devoted to the so-called Class III fatigue models, covering the three fatigue regimes, namely, LCF, HCF and VHCF. The applicability and limitations of the pro-posed analytical sigmoidal solutions are discussed from the viewpoint of practical design. The compatible Weibull S-N model by Castillo and Canteli is revisited and improved by considering a new reference parameter GP = E⋅σM ⋅(dε/dσ)|M as the driving force alternative to the conventional stress range. In this way, the requirement, σM ≤ σu, according to the real experimental conditions, is fulfilled and the parametric limit number of cycles, N0, recovers its meaning. The probabilistic definition of the model on the HCF and VHCF regimes is maintained and extended to the LCF regime. The strain gradients may be calculated from the monotonic or cyclic stress–strain curve of the material although a direct derivation from the hysteresis loop is recommended. Some Class III fatigue models from the literature and another one improved by the authors are applied to the assessment of one experimental campaign under different stress ratios conditions and the results compared accordingly. Finally, the new probabilistic GP-N field is evaluated. The results confirm the practical confluence of the stress- and the strain-based approaches into a single and advantageous unified methodology.
Statement of problem
The design of the implant-abutment connection has been widely researched, but the impact of different crown-abutment geometries remains unclear.
Purpose
The purpose of this in vitro study was to evaluate the effect of different crown-abutment margin geometries on the mechanical behavior and fit of screw-retained implant-supported single-crown restorations by using mechanical static and fatigue tests and mastication simulation.
Material and methods
A total of 45 cobalt-chromium premolar-shaped metal frameworks were fabricated for single-unit implant-supported screw-retained restorations on stock abutments and internal hexagon Ø4.25×11-mm cylindrical implants. They were divided into 3 groups according to margin geometry: S, shoulder; C, chamfer; and F, feather-edge. Three static load until fracture and 24 dynamic load tests were performed by using the International Organization for Standardization 14801:2016 standard (ISO 14801:2016) (number of cycles limit: 5×106 cycles, frequency: 6 Hz). The ProFatigue software program was used to optimize the procedure (S, n=12 specimens; C, n=7 specimens; and F, n=5 specimens). Six additional specimens from each group were subjected to a mastication simulation (limit number of cycles: 1×106 cycles, cyclic loading from Pmin=30 N to Pmax=300 N, frequency: 6 Hz). Results from the fatigue tests were reported descriptively, and the Fisher exact test was used to analyze the difference in failure modes. Data from maximum misfit were evaluated by photogrammetry and statistically analyzed with the Anderson-Darling test and the Kruskal-Wallis and Dunn multiple comparison tests (α=.05).
Results
The fatigue limit was 456 N for group S, 512 N for group C, and 514 N for group F. The mean ±standard deviation misfit was 2.6 ±0.1 μm for group S, 3.8 ±1.1 μm for group C, and 3.6 ±0.8 μm for group F. Differences in misfit between groups S and C and between groups S and F were statistically significant (P<.05).
Conclusions
Crown-abutment connections with chamfer and feather-edge margins showed better mechanical behavior, while shoulder margin exhibited better fit. However, high levels of fit were achieved for all the evaluated geometries.
Design methodology of vessel produced by L PBF stainless steel using representative specimens
(2022)
This work presents the preliminary results of an ongoing project with a double objective: on the one hand, the characterisation of the mechanical properties against fatigue damage of an additively manufactured 316 stainless steel produced by laser powder bed-based (L-PBF) technology; on the other hand, the implementation of numerical simulation techniques able to predict the mechanical behaviour of the material in order to optimise and reduce the design costs of vessels used in the chemical sector. The current state of the work developed in this research framework allows showing the first batch of experimental results of crack propagation rate (FCGR) and high cycle fatigue (HCF) tests. The geometry of the vessels studied presents three clearly differentiated regions, either in terms of thickness (11-15 mm) or concerning the inclination of the walls to the direction of manufacturing (0º - 45º). The experimental campaign carried out so far allows identifying the differences in behaviour when comparing different extraction locations around the vessel. This is due to the variations in thermal cycles that the deposited material undergoes during the manufacturing process. Therefore, this causes variations in the microstructure which lead to changes in the response of the material. In this work, these differences are analysed qualitatively and quantitatively from the results of FCGR and HCF, thus allowing to locate the regions with the highest risk in terms of structural integrity against fatigue. This preliminary phase together with the numerical simulation of the additive manufacturing process are key to achieving a reliable description and modelling of the material. The latter will make it possible to address the priority aim of this project, involving the manufacture of independent samples whose properties are representative of the original material extracted from the reference vessels. It is, therefore, a comprehensive methodology for the design of additively manufactured components based on the localised fatigue mechanical properties of representative specimens.
La tecnología de fabricación aditiva (AM) continúan progresando y permitiendo alcanzar diseños cada vez más complejos y optimizados. La industria química es uno de los sectores donde componentes AM han adquirido un gran interés. La falta hasta la fecha de una directiva europea que regule la inspección, certificación y aceptación de equipos sometidos a presión hace necesario progresar en esta línea. El objetivo que se persigue en este trabajo es el de desarrollar una metodología de diseño sobre componentes fabricados aditivamente basada en la estimación de vida a fatiga de las zonas más susceptibles de sufrir dicho tipo de fallo. El estudio comprende diversas facetas de análisis, simulaciones numéricas, análisis de la microestructura del material y una extensa campaña experimental. La evaluación de la integridad estructural se realiza aplicando mecánica de fractura. La historia térmica a lo largo del proceso de fabricación determina la microestructura del componente en cada región y, por ende, influye en las propiedades mecánicas en cada una. Se presentan los resultados preliminares de un proyecto de investigación en curso dirigido a la caracterización de propiedades mecánicas en recipientes de presión producidos por fusión láser en lecho de polvo (L-PBF, por sus siglas en inglés) de acero inoxidable 316L. Se detallan los resultados preliminares en términos de velocidad de crecimiento de grietas por fatiga (FCGR), y se comparan los resultados de probetas extraídas de diferentes regiones de los depósitos.
The robust determination of the threshold against fatigue crack propagation DKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of DKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic DK– da/dN test data to calculate DKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating DKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density.
To assess the ability of cracks to grow, a robust determination of the threshold against fatigue crack propagation ∆Kth is of paramount importance. The standards ASTM E647 and ISO 12108 introduce operational definitions of ∆Kth based on the crack propagation rate da/dN. For evaluating ∆Kth, both suggest fitting a linear function to a defined subset of the logarithmic ∆K – da/dN test data, where ∆Kth follows by evaluating the linear function at da/dN = 10-7 mm/cycle and da/dN = 10-8 mm/cycle, respectively.
In general, this kind of fit suffers from a bad representation of the actual curvature of the crack propagation curve. Therefore, we propose a robust method for evaluating ∆Kth using a non-linear function that reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. The method is calibrated against a large set of S690QL crack growth data obtained from a total of 48 specimens, and validated against a set of S355NL and S960QL data (3 specimens each), obtained as a part the IBESS (integral fracture mechanics determination of the fatigue strength of welds) project.
Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process.
Nichtrostende Duplexstähle (DSS) werden häufig verwendet, insbesondere bei Anwendungen, die eine hohe Festigkeit in Verbindung mit einer hohen Korrosionsbeständigkeit in aggressiven Medien erfordern. Beispiele hierfür sind Kraftwerkskomponenten und maritime Anwendungen. Beim Schweißen dieser Stähle kann es zu lokalen Schwankungen in der chemischen Zusammensetzung kommen. Dies führt zu einer Ferritisierung des Werkstoffs und beeinträchtigt die mechanischen Eigenschaften der Bauteile. In dieser Arbeit wurden Versuche zum Wolfram-Inertgas-Schweißen (WIG) mit DSS durchgeführt. Die Analyse der chemischen Zusammensetzung wurde in situ mit Hilfe der laserinduzierten Plasmaspektroskopie (LIBS) durchgeführt. Ziel der Arbeit ist es, die chemische Zusammensetzung in der Schweißnaht verschiedener DSS quantitativ zu messen und mögliche Einflüsse der Schweißparameter auf die Mikrostruktur des Werkstoffs zu ermitteln. Gemessen wurden die chemischen Konzentrationen der Hauptlegierungselemente Cr, Ni, Mn auf der Oberfläche der Probe während des Schweißprozesses und des Abkühlungsprozesses. Mn und Ni sind Austenitstabilisatoren, deren Gehalt beim Schweißen durch die Verwendung bestimmter hochlegierter Schweißzusatzwerkstoffe zunimmt. Die Spektren wurden alle 1,3 s in einem Abstand von etwa 2 mm aufgezeichnet. Während des Abkühlungsprozesses wurde der Ort der Messung nicht verändert. Die LIBS-Methode eignet sich nachweislich zur quantitativen Darstellung der chemischen Zusammensetzungen während des Schweißvorgangs.