In the last years flowable concrete has become increasingly important in applications such as, for systems with highly reinforced concrete with a complicated formwork, or sprayed concrete and 3D-printing of concrete. For all these applications it is necessary to have tailored rheological properties. Rheology can be described by values of yield stress and plastic viscosity, which can be determined for example by evaluation of rheometer measurements. But for different materials various rheometers with different geometries and stirrers are being used. To see the effects from paste in concrete, it is necessary to investigate mixes of paste, mortar and concrete, stepwise. But currently there exists no device, which is calibrated for these different systems at once. Due to this fact, conventional tests such as V-funnel efflux-time and flow diameter were determined, as well as rheometer data in different cell sizes and geometries.
In this study the assessment of rheological effects in the binder on the rheology of mortar and concrete was investigated by using combination of two rheometers.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed addition time of PCE SPs on hydration of cement and alite pastes, investigated by isothermal heat flow calorimetry. For cement as well as for alite pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. The retardation caused by PCE is much more pronounced for alite than for cement mixes. If PCE is added later to the mix, the induction period is shortened and the hydration is accelerated compared to simultaneous addition. This applies for cement and alite pastes. With delayed PCE addition the alite shows a clearly less retarded setting and main hydration than after simultaneous addition. It is obvious that for alite pastes there is less retardation the later the addition of SP.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has enormous influence on the early hydration of cement. C3A as the most reactive phase of Portland cement plays a significant role in early hydration reactions and affects the rheological performance. Therefore, this paper presents experimental results about the influence of delayed addition of PCEs on the Hydration of cement and C3A-gypsum pastes investigated by isothermal heat flow calorimetry. Complementary in-situ XRD was carried out on C3A pastes to analyze hydration and phase changes related to the addition of PCE.
Cement pastes with a delayed addition of PCE showed less Retardation compared to simultaneous addition. The alteration caused by PCE is much more pronounced for C3A-gypsum mixes. With a delayed addition of SP, the hydration of C3A is less retarded or even accelerated. It is obvious that there is less retardation the later the addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. XRD results showed that more C3A is dissolved in the presence of PCE. Also, the gypsum depletion occurs earlier in the presence of PCE and even faster with delayed addition. Without PCE AFm starts to form just after the gypsum depletion. However, in the presence of PCE AFm already starts to form at the beginning of the hydration. Due to the faster gypsum depletion in the presence of PCE, also the transformation from ettringite into AFm begins earlier, but takes longer as without SP.
Carbon Capture and Storage (CCS) is identified as an excellent technology to reach the target of CO2 reduction. However, the safety issue and cost-effectiveness hinder the future of CCS. For the reliability and safety issues of injection wells, the corrosion resistance of the materials used needs to be determined.
In this study, representative low-cost materials including carbon steel 1.8977 and low alloyed steel 1.7225 were investigated in simulated pore water at 333 K and under CO2 saturation condition to represent the worst-case scenario: CO2 diffusion and aquifer fluid penetration. These simulated pore waters were made from relevant cement powder to mimic the realistic casing-cement interface. Electrochemical studies were carried out using the pore water made of cement powder dissolved in water in comparison with those dissolved in synthetic aquifer fluid, to reveal the effect of cement as well as formation water on the steel performance. Two commercially available types of cement were investigated: Dyckerhoff Variodur® and Wollastonite. Variodur® is a cement containing high performance binder with ultra-fine blast furnace slag which can be used to produce high acid resistance concrete. On the other hand, Wollastonite is an emerging natural material mainly made of CaSiO3 which can be hardened by converting to CaCO3 during CO2 injection.
The results showed the pH-reducing effect of CO2 on the simulated pore water/aquifer (from more than 10 to less than 5) leading to the active corrosion process that happened on both 1.8977 and 1.7225. Electrochemical characterization showed negative free corrosion potential and polarisation curves without passive behaviors. The tested coupons suffered from pitting corrosion, which was confirmed by surface analysis. Interestingly, basing on the pit depth measurements from the tested coupons and the hardness of cement powder, it is suggested that Variodur® performed better than Wollastonite in both aspects. The electrochemical data was compared to that resulted from exposure tests to give a recommendation on material selection for bore-hole construction.