Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2018 (11) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (11) (entfernen)
Schlagworte
- Niobium carbide (6)
- Cermet (4)
- Wear (4)
- Mechanical properties (3)
- Sintering (3)
- Hardness (2)
- NbC (2)
- Nickel (2)
- Niobium carbide (NbC) (2)
- Alumina (1)
- Aluminium oxide (1)
- Carbon (1)
- Carbonitride (1)
- Ceramic (1)
- Coating (1)
- Cylindrical turning (1)
- DEM (1)
- Diaspore (1)
- FEM (1)
- Friction (1)
- Hard metals (1)
- Hardmetal (1)
- Hot steam (1)
- Liquid phase sintering (1)
- Machining (1)
- Microstructure (1)
- Monte-Carlo simulation (1)
- Niobcarbid (NbC) (1)
- Particle erosion (1)
- Physical vapor deposition (PVD) (1)
- Temperature (1)
- Tool (1)
- Tool wear (1)
- Tungsten carbide (WC) (1)
- Turning (1)
- Verschleiß (1)
- Werkzeug (1)
Organisationseinheit der BAM
Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2.
Niobcarbid (NbC) stellt aufgrund vorteilhafter Eigenschaften, wie zum Beispiel eine geringe Diffusionsneigung, in der Zerspannung eine vielversprechende Alternative zu konventionellen Schneidstoffen wie Wolframcarbid (WC) dar. Als Substitution der Hartstoff-Phase WC im Hartmetall wird NbC in der trockenen Drehbearbeitung von eisen-basierten Werkstoffen untersucht. Diesbezüglich wurden zwei NbC-Substrate mit WC hinsichtlich ihres Werkzeugverschleißes quantitativ verglichen. Im Gegensatz zu WC-Werkzeugen wird das Potential von NbC bei zunehmender Schnittgeschwindigkeit vc durch eine steigende Prozessstabilität deutlich.