- Crack growth (3) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (2)
- 5.5 Materialmodellierung (1)
- 5.6 Glas (1)
Crack growth velocity in alkali silicate glasses was measured in vacuum across 10 orders of magnitude with double cantilever beam technique. Measured and literature crack growth data were compared with calculated intrinsic fracture toughness data obtained from Young´s moduli and the theoretical fracture surface energy estimated from chemical bond energies. Data analysis reveals significant deviations from this intrinsic brittle fracture behavior. These deviations do not follow simple compositional trends. Two opposing processes may explain this finding: a decrease in the apparent fracture surface energy due to stress-induced chemical changes at the crack tip and its increase due to energy dissipation during fracture.
Environmentally-assisted material degradation involves mass transport and mechanical processes interacting in the material. A well-known example is hydrogen-induced stress-corrosion cracking. One major challenge within this scope is the quantification of the coupling mechanisms in question. The computational modeling of environmentally-assisted cracks is the key objective of this investigation and realised within the theory of gradient-extended dissipative continua with lengthscales. The modeling of sharp crack discontinuities is replaced by a diffusive crack model based on the introduction of a crack phase-field to maintain the evolution of complex crack topologies. Within a thermodynamical framework allowing for mechanical and mass transport processes the crack phasefield is capable to model crack initiation and propagation by the finite element method. As complex crack situations such as crack initiation, curvilinear crack patterns and crack branching are usually hard to realise with sharp crack models, they can be assessed without the requirement of a predefined crack path within this method. The numerical modeling of a showcase demonstrates a crack initiation as well as a crack propagation situation with respect to the determination of stress-intensity factors; a crack deviation situation with a curvilinear crack path is modeled by the introduction of a geometrical perturbation and a locally enhanced species concentration.
Crack propagation under low cycle fatigue and thermomechanical fatigue is characterized by high plastic and creep strains that extend over large regions around the crack, so that concepts of linear-elastic fracture mechanics cannot be applied. In these cases, the cyclic crack tip opening displacement 𝛥CTOD is a promising loading parameter to quantify crack growth. In this work, suitable definitions and Finite Element techniques are investigated and compared for an accurate calculation of 𝛥CTOD under cyclic mechanical and/or thermal loading. A viscoplastic temperature dependent material model of Chaboche-type is used along with large strain settings, specified for the austenitic cast iron Ni-resist. Extensive two-dimensional analyses of Single Edge Notch Tension specimens revealed that collapsed special crack tip elements are superior compared with commonly used regular quadrilateral 8-node elements. At the same level of accuracy of 𝛥CTOD, they require an about ten times coarser mesh and show less sensitivity
w.r.t. element size for both stationary and propagating cracks. In order to simulate fatigue crack growth, an efficient, fully automated FE-technique is developed for an incremental crack propagation by successive remeshing, whereby the deformations and internal state variables are mapped from the old mesh onto the new one. Recommendations are made regarding important numerical control parameters like optimal size of crack tip elements, length of crack growth increment in relation to plastic zone size and 𝛥CTOD value.