The influence of temperature and counterbody material on the tribological properties of a-C:H
coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk
contact situation with alpha-alumina and silicon nitride as counterbodies. The results show, that the wear volumes of the systems increase exponentially with increasing temperature, for alpha-alumina more than for silicon nitride. Two different wear mechanisms seem to have a
major influence: First, the abrasive action due to materials hardness and second, the tribo-oxidation when silicon nitride is counter material.
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
Tribology in hot steam
(2017)
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2, alumina and antimony impregnated carbon.
The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining.
Besides carbon, metal sulphides are used in every standard brake pad formulation as friction stabilisers. In order to investigate their impact, various powder mixtures were tribologically stressed in a pin-on-disc device in order to produce and test artificial third bodies. containing the three main components of a real friction film, namely magnetite, graphite and a metal sulphide of interest. Since the sliding behaviour is influenced by the relative humidity the powder mixtures are tested at low, medium and high moisture levels. The tests revealed that the presence of graphite dominates the friction behaviour as well as the humidity sensitivity.
The powders were prepared by either manual mixing or high energy ball-milling. Interestingly, all ball-milled blends provided coefficients of friction within the desired range for braking, which was attributed to the effect of zirconia particles from wear debris of the milling balls. The zirconia particles prevent the formation of solid lubricant films on the surfaces and support a homogeneous mixture of all constituents of the powder. Optimum brake performance is gained by an optimum combination of solid lubricants and abrasives.
The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation.