Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2018 (10) (entfernen)
Dokumenttyp
- Vortrag (4)
- Zeitschriftenartikel (3)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (1)
Schlagworte
- Residual stress (4)
- Welding (4)
- High-strength steels (3)
- Large-scale test (3)
- Process parameters (3)
- Residual stresses (3)
- Restraint (3)
- Eigenspannungen (2)
- HSLA steel (2)
- MAG-Schweißen (2)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (10) (entfernen)
Eingeladener Vortrag
- nein (4)
Die Beschaffung und Verarbeitung von Werkstoffen für hochbelastete Komponenten sind meist kostenintensiv. Bestrebungen zur Kosten- und Ressourceneffizienz führen zu komplexeren Strukturen bzw. Konturen, sodass generative Fertigungsschritte zur Bauteilreparatur und -fertigung deutliche ökonomische Vorteile bieten. Hierfür sind generative und abtragende Fertigungsschritte komplementär und gezielt aufeinander abzustimmen, um beanspruchungsgerechte Funktionsflächen herzustellen. Hinsichtlich Inhomogenität und Anisotropie der Gefüge und Eigenschaften sowie fertigungsbedingter Beanspruchungen sind für den wirtschaftlichen Einsatz bei KMU, gerade für drahtbasierte Fertigungsverfahren und Wechselwirkungen nachfolgender Zerspanung dieser schwer spanbaren Werkstoffe noch viele Kenntnisse notwendig. Deshalb sind Untersuchungen zu diesen Einflüssen und Wechselwirkungen unter Nutzung innovativer Ansätze geplant. Mit typischen kostenintensiven Ni- und Co-Cr-Legierungen werden generativ Bauteile, Auftrag- und Reparaturschweißungen hergestellt und Schweißzusätze für das PTA-Verfahren modifiziert, um die Erstarrungsmorphologie und das Eigenschaftsprofil zu optimieren. Die Übertragung auf MSG-Verfahren sichert einen breiten industriellen Einsatz für hohe Auftragraten ab. Die wirtschaftliche spanende Bearbeitbarkeit wird mit Zerspanbarkeitsanalysen für Schlichtfräsen und vergleichend für ultraschallunterstütze Fräsprozesse sichergestellt. Instrumentierte Experimente und Werkstoffanalytik hinsichtlich der Einflüsse auf Schmelzbad, Gefüge und Ausscheidungen sowie auf Randzoneneigenschaften und Eigenspannungen ermöglichen umfassende Erkenntnisse zur kombinierten generativen und abtragenden Fertigung. Durch Bauteilversuche und -prüfungen, Übertragbarkeitsstudien weiterer innovativer Werkstoffe verbunden mit Handlungsempfehlungen und der Zusammenarbeit mit den jeweiligen Normungsgremien profitieren KMU von einer hochwirtschaftlichen Herstellung und Reparatur kostenintensiver Komponenten.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Two examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the bending stresses in the welded joint and therefore the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
The performance and safety of welded high-strength low-alloyed steel (HSLA) components are substantially affected by the stresses occurring during and after welding fabrication, especially if welding shrinkage and distortion are severely restrained. The surrounding structure of the whole component affects loads in the far-field superimposing with welding stresses in the near-field of the weld. In this study a unique testing facility was used to restrain shrinkage and bending while analyse multiaxial far-field loads (max. 2 MN) during assembly of thick-walled component. A novel approach for the assessment of the in-situ-measured far-field data in combination with the actual weld geometry was elaborated. For the first time, analyses of the global bending moments of restrained welds based on the neutral axis of the actual weld load bearing section were achieved. Hence, far-field measurements offered the possibility to determine critical near-field stresses of the weld crosssections for the entire joining process. This work presents the approach for far-to-near field in-situ determination of stresses in detail for the 2-MN-testing system based on an extensive experimental work on HSLA steel welds, which demonstrates sources and consequences of these high local welding stresses. Thus, it was clarified, why the first weld beads are crucial regarding welding stresses and cold cracking, which is well known, but has never been measured so far. Accompanying analyses using X-ray diffraction (XRD) after welding show effects on local residual stress distributions. These analyses indicated viable prospects for stress reduction during assembly of thick-walled HSLA steel components.
The performance and safety of welded high-strength low-alloyed steel (HSLA) components are substantially affected by the stresses occurring during and after welding fabrication, especially if welding shrinkage and distortion are severely restrained. The surrounding structure of the whole component affects loads in the far-field superimposing with welding stresses in the near-field of the weld. In this study a unique testing facility was used to restrain shrinkage and bending while analyse multiaxial far-field loads (max. 2 MN) during assembly of thick-walled component. A novel approach for the assessment of the in-situ-measured far-field data in combination with the actual weld geometry was elaborated. For the first time, analyses of the global bending moments of restrained welds based on the neutral axis of the actual weld load bearing section were achieved. Hence, far-field measurements offered the possibility to determine critical near-field stresses of the weld crosssections for the entire joining process. This work presents the approach for far-to-near field in-situ determination of stresses in detail for the 2-MN-testing system based on an extensive experimental work on HSLA steel welds, which demonstrates sources and consequences of these high local welding stresses. Thus, it was clarified, why the first weld beads are crucial regarding welding stresses and cold cracking, which is well known, but has never been measured so far. Accompanying analyses using X-ray diffraction (XRD) after welding show effects on local residual stress distributions. These analyses indicated viable prospects for stress reduction during assembly of thick-walled HSLA steel components.
Today, an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore, the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters.
However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. Lower working temperatures revealed to be particularly effective to reduce the local and global welding-induced residual stresses of the complete weld significantly. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows strategies to reduce these in-process stresses.
With help of multi-axial welding stress analyses in component-related weld tests, using a special 2-MN-testing facility, differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum load capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
Ausgehend vom derzeit vorrangigen Einsatz in Mobilkranen, kommen höherfeste Feinkornbaustähle mit Streckgrenzen ab 960 MPa zunehmend auch in anderen modernen Stahlkonstruktionen zur Anwendung. Dies ist aufgrund aktueller Forderungen nach Energie- und Ressourceneffizienz im Sinne des konstruktiven Leichtbaus vielfach notwendig. Die Verwendung höherfester Stähle sowie deren schweißtechnische Verarbeitung, insbesondere in sicherheitsrelevanten Tragstrukturen, erfordert ein tiefgreifendes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und den nahtnahen Bereichen. Vorwiegend werden höherfeste Güten mittels MAG-Prozess geschweißt. Bedeutende Fortschritte in der Regelungstechnik führten unter den Herstellern von Schweißstromquellen in den letzten Jahren zur Entwicklung zahlreicher modifizierter Sprühlichtbogenprozesse (mod. SLB). Diese Prozesse ähneln sich in ihren Eigenschaften und ermöglichen die bekannten positiven Aspekte, wie Einsparung an Schweißzusatz sowie Schweiß- und Rüstzeit aufgrund der Möglichkeit reduzierter Nahtöffnungswinkel. Der mod. SLB bedingt zusammen mit einer anderen Nahtgeometrie veränderte Naht- und Schweißraupenquerschnitte sowie einen abweichenden Lagenaufbau. Diese wirtschaftlich-technisch attraktive Möglichkeit reduzierter Nahtöffnungswinkel findet in den Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dabei gilt es, gerade die Interaktion der Haupteinflussgrößen auf die Kaltrissbildung unter reduziertem Nahtöffnungswinkel zu betrachten. Im Rahmen zweier AiF-Forschungsvorhaben (IGF-Nr. 17.978 N, 18.596 BR) wurde daher der Einfluss der Wärmeführung anhand vergleichender Mehrlagenschweißungen mittels konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration auf schweißbedingte Beanspruchungen sowie auf die Wasserstoffkonzentration im Schweißgut untersucht.
Der zunehmende Bedarf an hochfesten Feinkornbaustählen in modernen Schweißkonstruktionen, in einer deutlich wachsenden Anzahl von Branchen wie dem Hoch-, Anlagen- und Kranbau, führte in den letzten Jahren zur Entwicklung zahlreicher Grund- und Zusatzwerkstoffe. Neben der Erreichung anforderungsgerechter mechanischer Eigenschaften wird die wirtschaftliche Verarbeitung dieser Güten durch hohe Sicherheitsanforderungen an die Schweißnaht bestimmt. Hohe Zugeigenspannungen in der Schweißverbindung können die Beanspruchbarkeit und Sicherheit eines geschweißten Bauteils wesentlich reduzieren. Insbesondere bei einer hohen konstruktiven Schrumpfbehinderung können die Beanspruchungen auch schon während der Fertigung ein risskritisches Niveau erreichen.
Mittels geeigneten Wärmeführungen beim Schweißen und der adäquaten Auswahl von Schweißprozess und Zusatzwerkstoffen ist sowohl eine Minimierung der sich lokal in der Naht bildenden Zugeigenspannungen als auch der globalen infolge von Abstützeffekten auftretenden Reaktionsspannungen und -momente erzielbar. Im Rahmen zweier AiF-Forschungsvorhaben IGF.-Nr. 17267 N und 17978 N wurden verschiedene experimentelle Beanspruchungsanalysen durchgeführt, um den Schweißprozess hinsichtlich der resultierenden schweißbedingten Beanspruchungen zu untersuchen. Hierfür war es erforderlich, die Steifigkeitsverhältnisse so wie sie beim Schweißen realer Bauteilstrukturen auftreten, auf Schweißexperimente im Labor zu übertragen.
Dazu wurde bspw. eine an der BAM eigens entwickelte Prüfanlage eingesetzt, mit der die mehraxialen Belastungen analysiert wurden, die mit bis zu 2 MN beim Vorwärmen, Schweißen und Abkühlen auftreten. Die Schweißeigenspannungen wurden mittels Röntgendiffraktometrie bestimmt. Zwar zeigten sich für niedrige Arbeitstemperaturen beim Schweißen ein signifikant reduziertes Gesamtbeanspruchungsniveau nach der Abkühlung der gesamten Schweißnaht. Die langen Abkühlphasen während der mehrlagigen schweißtechnischen Fertigung führen jedoch speziell bei den ersten Schweißraupen zu sehr hohen Reaktionsspannungen. Dabei erwiesen sich schmalere Nahtfugen verbunden mit dem Einsatz modifizierter Schweißprozesse und der Einsatz dehnfähiger Schweißzusätze für das Wurzelschweißen als geeignete Mittel, um eine deutliche Absenkung des Beanspruchungsniveaus beim Schweißen unter Schrumpfbehinderung zu erreichen. Ferner ist damit eine weitere wesentliche Reduzierung der Gesamtbeanspruchung und insbesondere der Zugeigenspannungen in der WEZ möglich. Mithilfe dieser Erkenntnisse ist die Optimierung der schweißbedingten Beanspruchungen unter Nutzung einer adaptierten Wärmeführung zur verbesserten Ausnutzung des Festigkeitspotentials höherfester Feinkornbaustähle erreichbar.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analysed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behaviour, welding and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively.