Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (39) (entfernen)
Dokumenttyp
- Vortrag (39) (entfernen)
Referierte Publikation
- nein (39)
Schlagworte
- Additive Manufacturing (8)
- Wasserstoff (8)
- Residual stress (7)
- Welding (7)
- Hochfeste Feinkornbaustähle (5)
- MAG-Schweißen (5)
- Schweißen (5)
- Diffraction (4)
- Eigenspannungen (4)
- Kaltrisse (4)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (39) (entfernen)
Eingeladener Vortrag
- nein (39)
An overview of the BAM funed Focus Area Materials Project "AGIL" will be presented. AGIL focussed on the stdiy of the ageing characteristics of additively manufactured austenitic stainless steel with a "powder to mechanical failure" Approach. Recent Highlights are presented and a perspective for future studies.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour (Fig. 1). During testing, energy input per unit length and bending speed were varied (especially the latter is usually kept at standard values), in addition to the most commonly altered factor - total deformation.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach - microscopic analysis of the specimen surface. It was found that not all parameter changes had the expected outcome. For the Cr8Ni6 and Cr11Mn5 filler materials, influences of energy input per unit length and welding speed were in direct opposition.
In order to investigate those apparent contradictions, µCT scans of MVT specimens were made. The results consistently show sub surface cracking, to significant, yet varying extents. Different primary solidification types were found using WDX-analysis, an aspect that is believed to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Die klassische Beurteilung der Heißrissneigung erfolgt bislang primär über das Prüfen der Schweißeignung des Werkstoffes. Die konstruktiven Bedingungen und bauteilspezifischen Beanspruchungszustände bleiben dabei meist unberücksichtigt. Die Vielzahl an Heißrisstests liefert dabei lediglich werkstoff-spezifische, empiri-sche Heißrissparameter, wie z. B. Gesamtrisslänge oder Gesamtrissanzahl. Eine Bauteilübertragbarkeit ist somit oftmals nicht gegeben, gerade wenn es sich um hochbeanspruchte Konstruktionsmerkmale des Leichtbaus handelt. Folglich sind mechanische Kenngrößen (risskritische Verformungen/Spannungen) zu identifizieren, die sicher und unter realitätsnahen Bedingungen erfasst werden können. Diese dienen als Transfergrößen, um die Heißrissanfälligkeit geschweißter Bauteile mit typischen Konstruktionsmerkmalen zu bewerten.
Laser based Powder Bed Fusion (L-PBF) is an additive manufacturing technique that has been continuously developed in the past years. It offers unparalleled design freedom and the resulting mechanical properties match, in some cases even exceed, those of materials processed by conventional manufacturing techniques. Nonetheless the process is prone to create Residual Stresses (RS) resulting from the sequential melting and solidification of the material. RS can reduce load bearing capacity and generate unwanted distortions thus diminishing the potential of L-PBF. This research activity aimed at characterizing the RS state in Inconel 718 L-PBF specimens using multiple diffraction methods. The microstructure as well as the surface and bulk residual stresses were investigated. The RS analysis was performed using X-ray, synchrotron and neutron diffraction methods to provide information at different depths within the specimen. The measurements were performed at the Bundesanstalt für Materialforschung und –prüfung (BAM), the EDDI beamline at BESSY II synchrotron and E3 line at BER II neutron reactor of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results revealed a depth depending RS state. The longitudinal and transverse stress components measured by X-ray and synchrotron at the surface agree well, exhibiting stress values around the yield strength of the material. In addition, synchrotron mapping showed gradients along the width and length of the sample for the longitudinal and transverse stress components. Lower RS values compared to surface RS were measured in the bulk of the material using neutron diffraction. The longitudinal stress component in the bulk was tensile and gradually decreased towards the edge of the specimen. The normal component however did not change significantly along the specimen dimensions and was of compressive nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers, which has to be further investigated.
Residual stresses count among the most limiting factors in the application of additively manufactured materials in safety relevant components subject to cyclic loading. The source of such stresses is inherent in the manufacturing Laser Beam Melted (LBM) process due to rapid cooling and solidification and their distribution in the specimen or component is not homogeneous, but it is usually characterized by high gradients. Moreover, the magnitude of the residual stress field depends very much on the orientation, being higher in the build direction.
Many works in the literature advise to carry out a post-LBM treatment to relieve residual stresses, even though particular attention should be paid in choosing the parameters for the thermal treatment in order to avoid microstructural/phase transformations, which would affect greatly the mechanical properties of the material.
Particularly in the case of the austenitic stainless steel 316L, it has been shown that annealing at high temperatures (above 900°C), besides relieving the residual stresses, may cause recrystallization, grain growth and even phase transformation. In contrast, if a too low annealing temperature is chosen in order to preserve the microstructure, the residual stresses cannot be completely relieved.
This work aims to address the effect of residual stresses on short and long crack propagation for SEN(B) specimens made of 316L fabricated by LBM, in which notches have been machined by electro-discharge machining (EDM) on the mid-plane, perpendicular to the build direction. The specimens underwent different annealing treatments in inert atmosphere, in which the maximum temperature has been varied up to 900°C. The amount of residual stresses and their distribution has been measured by X-ray and neutron diffraction and the specimens have been subject to cyclic loading in a resonant testing machine. The tests show a massive influence of the residual stresses in the build direction on the resistance to fatigue crack propagation of additively manufactured 316L. Finally, a comparison with conventionally manufactured 316L is presented.
Effect of weld penetration depth on hydrogen-assisted cracking of high-strength structural steels
(2019)
The need for steels with highest mechanical properties is a result of the increasing demands for energy and resource efficiency. In this context, high-strength structural (HSS) steels are used in machine, steel and crane construction with yield strength up to 960 MPa. However, welding of HSS steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of (1) microstructure, (2) local stress/strain and (3) local hydrogen concentration. In addition to the three main factors, the used weld-arc process is also important for the performance of the welded joint, especially when using modern arc variants. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of HSS grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been used increasingly for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared to the conventional process. Economic benefits of using this arc type are: a reduced number of necessary weld beads and a lower weld seam volume, which result in decreased total welding time and costs. Nonetheless, investigations on a high-strength S960QL showed significantly higher hydrogen concentrations in the weld metal at a reduced seam opening angle with Mod. SA. This indicates an increased susceptibility of the welded component to HAC. Hence, existing recommendations on HAC-avoidance cannot be transferred directly to the Mod. SA-process. In the present study, the susceptibility to HAC of the HSS steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded implant test was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). However, the test series with Mod. SA showed a significant extension of the time to failure of several hours compared to tests carried out with Conv. A.
In the present study, the susceptibility to HAC of the HSLA steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same weld heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded Implant-test [ ] was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). But in all specimens, cracks initiated at the notch root of the spiral notch of the implants within the coarse-grained HAZ. However, the test series with Mod. SA showed a significant extension of the time-to-failure of several hours compared to tests carried out with Conv. A, see Fig. 1a. The reason is the deeper weld penetration in case of Mod. SA (Fig. 1b and Fig. 1c), which causes longer diffusion path for hydrogen. The fracture topography of the ruptured implant specimens with Conv. A was typical ductile in specimen center and quasi-cleavage like at the edge of the specimens. When using Mod. SA, the topography changed to primarily quasi-cleavage fracture topography with shares of intergranular fracture and secondary crack appearance.
The need for steels with highest mechanical properties is a result of the increasing demands for energy and resource efficiency. In this context, high-strength low-alloyed (HSLA) structural steels are used in machine, steel and crane construction with yield strength up to 960 MPa. HSLA steels enable lightweight construction by thinner necessary plate thickness. However, welding of HSLA steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of (1) microstructure, (2) local stress/strain and (3) local hydrogen concentration. In addition to the three main factors, the used weld-arc process is also important for the performance of the welded joint, especially when using modern arc variants. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of HSLA grades. In the past decade, the so-called modified spray arc process (Mod. SA) was increasingly used for welding production. This modified arc enables reduced seam opening angles with increased deposition rates compared to the conventional process. Economic benefits of using this arc type are: a reduced number of necessary weld beads and a lower weld seam volume, which result in decreased total welding time and costs. Nonetheless, investigations on a high-strength S960QL showed significantly higher hydrogen concentrations in the weld metal at a reduced seam opening angle with Mod. SA. This indicates an increased risk for the susceptibility of the welded component to HAC. Hence, existing recommendations on HAC-avoidance cannot be transferred directly to the Mod. SA-process.
In the present study, the susceptibility to HAC of the HSLA steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same weld heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded Implant-test was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). But in all specimens, cracks initiated at the notch root of the spiral notch of the implants within the coarse-grained HAZ. However, the test series with Mod. SA showed a significant extension of the time-to-failure of several hours compared to tests carried out with Conv. A. The reason is the deeper weld penetration in case of Mod. SA, which causes longer diffusion path for hydrogen. The fracture topography of the ruptured implant specimens with Conv. A was typical ductile in specimen center and quasi-cleavage like at the edge of the specimens. When using Mod. SA, the topography changed to primarily quasi-cleavage fracture topography with shares of intergranular fracture and secondary crack appearance.
Wirtschaftliche und ökologische Aspekte führten in den letzten Jahren zu deutlich gesteigerten Anforderungen an die Effizienz und die Flexibilität petrochemischer Anlagen. Die heutzutage geforderten Prozesstemperaturen und -drücke lassen sich nur durch den Einsatz neuer warmfester Stahlgüten erreichen. Der mit Vanadium modifizierte Stahl 13CrMoV9-10 weist eine bessere Kriech- und Druckwasserstoffbeständigkeit auf und wird seit Mitte der 90er Jahre im petrochemischen Reaktorbau eingesetzt. Aufgrund der niedrigen Zähigkeit und hohen Festigkeit des Schweißgutes im geschweißten, nicht spannungsarm geglühten Zustand sowie einer erhöhten Sensitivität gegenüber Spannungsrelaxationsrissen bedarf dieser Stahl allerdings einer äußerst sorgfältigen schweißtechnischen Verarbeitung. Bisherige Untersuchungen zur Rissentstehung in warmfesten Stählen konzentrierten sich vorrangig auf thermische und metallurgische Einflussfaktoren, bieten jedoch nur wenige Erkenntnisse zum Einfluss des Schweißprozesses auf die Rissbildung beim Spannungsarmglühen unter Berücksichtigung realitätsnaher Fertigungsbedingungen.
Im ersten Teil wurde zunächst der Einfluss der Wärmeführung auf die mechanischen Eigenschaften anhand von frei schrumpfenden Laborproben untersucht. Während sich die Wärmeführung wesentlich auf die Schweißnahtstruktur auswirkte, war ein signifikanter Effekt auf die mechanischen Eigenschaften nicht nachweisbar. Auch traten infolge der Wärmenachbehandlung der frei schrumpfend geschweißten Proben keine Spannungsrelaxationsrisse auf.
Der zweite Teil umfasste die realitätsnahe Abbildung der Fertigungsbedingungen im petrochemischen Reaktorbau. Zu diesem Zweck wurden die konstruktiven Randbedingungen während des Vorwärmens, Schweißens, des Wasserstoffarmglühens und der abschließenden Wärmenachbehandlung realitätsnah in einer speziellen 3-D-Prüfanlage zur Simulation von Bauteilschweißungen abgebildet. Unter konstruktiver Schrumpfbehinderung gelang der Nachweis der unterschiedlichen Wirkung von Vorwärm- / Zwischenlagentemperatur und Streckenenergie auf die resultierenden Kräfte, Momente und Spannungen. Die Gesamtreaktionsspannung nach dem Schweißen wurde innerhalb des untersuchten Parameterfeldes maßgeblich durch die Streckenenergie beeinflusst.
Ein möglichst geringer Gesamtwärmeeintrag hat die niedrigste Bauteilbeanspruchung zur Folge. Während der Wärmenachbehandlung kam es in allen Versuchen zu Spannungsrelaxationsrissen. Deren kumulierte Länge korrelierte mit den ermittelten schweißbedingten Reaktionsspannungen.
Die Detektion der Risse während der Wärmenachbehandlung im Bauteilversuch erfolgte erstmalig in-situ mittels Schallemissionsanalyse. Die Rissinitiierung fand nachweislich im Temperaturbereich von 300 °C bis 500 °C statt. Die Reaktionsspannungen nach der Wärmenachbehandlung lagen unabhängig von der Ausgangsbelastung auf einem vergleichbaren Niveau. Die Zähigkeit der Schweißverbindung nahm klar gegenüber den frei schrumpfend geschweißten Proben ab.
Mittels REM- und TEM-Analysen an vergleichbaren belasteten und unbelasteten Proben wurde eine beschleunigte Alterung, durch das frühzeitige Ausscheiden von Sonderkarbiden während der Wärmenachbehandlung unter definierter Einspannung (d. h. unter Belastung), nachgewiesen. Die verstärkte Korngrenzensegregation korrelierte mit der signifikanten Abnahme der Kerbschlagarbeit der unter Einspannung geschweißten Proben.
The present study deals with the experimental characterization of short crack propagation in SLM (selective-laser-melting) manufactured stainless steel. More specifically, the determination of cyclic R-curves is discussed. This describes the dependency of the crack propagation threshold on crack growth during the short crack propagation stage. For metals, the threshold, starting at a material-intrinsic value, increases until it reaches a value independent of the crack length due to crack closure phenomena which build up at that stage. The cyclic R-curve, when used in the frame of a cyclic R curve analysis, characterizes the resistance of a material to fatigue crack growth and the ability to arrest a physically short crack. Thus, it is the link between classical fatigue and fracture mechanics. In the high-cycle-fatigue range, the short crack propagation stage dominates the overall lifetime, i.e., the number of cycles until failure. Below the fatigue limit crack arrest of hitherto propagable micro-cracks will occur. The effort for the experimental characterization of the short fatigue crack propagation behavior and the cyclic R-curve is very high compared to experiments on long crack propagation. A very exact measurement of crack extension is required, since small increments need to be depicted. Pre-cracking must leave a closure free initial crack, since closure must be build up only by the cyclic R-curve. The closure-free status is achieved by compression pre-cracking. The aim of the present study is an insight into the influence of an AM process on the short crack propagation threshold. Cyclic R-curves are experimentally determined at different load-ratios for 316L austenitic steel specimens produced by SLM and conventional manufacturing. Residual stresses are measured in the crack plane and their influence on the cyclic R-curve is discussed.