Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
In the present work an approach is presented which combines various aspects of the former models with probability considerations. It is used to simulate the impact of more than one billion Alumina particles onto a steel substrate. This approach permits the simulation of an entire erosion experiment on an average PC within about six hours.
In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2.
Niobcarbid (NbC) stellt aufgrund vorteilhafter Eigenschaften, wie zum Beispiel eine geringe Diffusionsneigung, in der Zerspannung eine vielversprechende Alternative zu konventionellen Schneidstoffen wie Wolframcarbid (WC) dar. Als Substitution der Hartstoff-Phase WC im Hartmetall wird NbC in der trockenen Drehbearbeitung von eisen-basierten Werkstoffen untersucht. Diesbezüglich wurden zwei NbC-Substrate mit WC hinsichtlich ihres Werkzeugverschleißes quantitativ verglichen. Im Gegensatz zu WC-Werkzeugen wird das Potential von NbC bei zunehmender Schnittgeschwindigkeit vc durch eine steigende Prozessstabilität deutlich.