The aim of this research is to characterize a surface that has experienced low wear on asperities. The procedure used is similar to an Abbott-Firestone approach and based on functional bearing of projected area, surface area and material volume. Surface features extracted from surface height maps provide more comprehensive information about topography changes due to wear. Thus, they were used to detect low wear volumes on the top of asperities.
The aim of this research is to characterize a surface that has experienced low wear on asperities. The procedure used is similar to an Abbott-Firestone approach and based on functional bearing of projected area, surface area and material volume. Surface features extracted from surface height maps provide more comprehensive information about topography changes due to wear. Thus, they were used to detect low wear volumes on the top of asperities.
The cause and type of solid particle erosion varies across different industries and locations in plants, for instance the particles could be volcanic ash in aero-engines, fly ash in boilers, exfoliated scale in steam turbines or mineral matter in oil excavation. In all cases the durability of materials can be improved through better surface engineering and coatings, but the development of these is restricted also due to lack of generic models. In this respect, the simulation of a single impact with finite element methods using 100.000 knots would take about 15 minutes. In order to simulate an entire particle erosion experiment, up to one billion of such impacts would have to be considered. In order to simulate an entire particle erosion experiment, the current work presents an alternative approach capable of calculating about half a billion impacts on a substrate in less than six hours on a standard PC. The predictions of the simulation will be compared to a steel sample at 600°C eroded by aluminum oxide particles with a velocity around 210 m/s.
The cause and type of solid particle erosion varies across different industries and locations in plants, for instance the particles could be volcanic ash in aero-engines, fly ash in boilers, exfoliated scale in steam turbines or mineral matter in oil excavation. In all cases the durability of materials can be improved through better surface engineering and coatings, but the development of these is restricted also due to lack of generic models. In this respect, the simulation of a single impact with finite element methods using 100.000 knots would take about 15 minutes. In order to simulate an entire particle erosion experiment, up to one billion of such impacts would have to be considered. In order to simulate an entire particle erosion experiment, the current work presents an alternative approach capable of calculating about half a billion impacts on a substrate in less than six hours on a standard PC. The predictions of the simulation will be compared to a steel sample at 600°C eroded by aluminum oxide particles with a velocity around 210 m/s.
Commercial grade-1 titanium samples (Ti, 99.5% purity) were treated using three alternative methods, i.e., fs-laser processing in air, thermal heat treatment in an oven, or anodization in an electrochemical bath, all resulting in the formation of differently conditioned superficial oxide layers. The laser processing was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of several square-millimetres large surface areas covered homogeneously by these nanostructures. The thermal processing in the oven was done at two different temperatures, while the electrochemical anodization was performed at room temperature, aiming to generate different polymorphs of titanium oxide at similar oxide layer thickness. The irradiated surface regions were characterized by optical and scanning electron microscopy, and micro Raman spectroscopy. The tribological performance of the differently treated titanium surfaces was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in un-additivated paraffin oil and fully formulated engine oil as lubricants. The specific tribological performance of the differently treated surfaces is discussed on the basis of possible physical and chemical mechanisms.