Neutron diffraction: the forgotten non-destructive technique for residual stress analysis … and more
(2016)
3-D Stress Analysis
(Bulk) Stress mapping
Thick (and thin) films & Interfaces
Bulk high temperature
Real time
In-situ testing: Large sample environment (Stress rigs, Furnaces, …)
Neutrons and Synchrotron Radiation allow all this because they are FASTER , DEEPER and MORE PRECISE than lab equipment
(Flux)(Energy)(Parallel Beam)
The combination of tomographic, microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on material and component properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. This logic thread equally holds for industrial and academic research, and valorizes expensive experiments such as those carried out at synchrotron sources, which cannot be daily repeated.
I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing. Examples of micro-structured inhomogeneous materials will be given, such as Composites, Ceramics, Concrete, and Additively manufactured parts. I will also show how X-ray refraction computed tomography (CT) can be highly complementary to classic absorption CT, being sensitive to internal interfaces.
Additionally, I will present a new technique in our portfolio, Neutron Diffraction, which is extremely well suited to the study of internal stresses, both residual and under external load.
The evolution of the microstructure of multiphase metal matrix composite AlSi12CuNiMg with 7% vol. Al2O3 + 15% vol. SiC (short fibers and whiskers, respectively) was studied by synchrotron computed tomography. It comprehended as cast and after heat treatment conditions, as well as damage evaluation after ex-situ compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and damage events are studied.
The influence on mechanical properties of the orientation of the planar random short fibres Al2O3 towards loading was investigated. Phase-specific load partition analysis for samples with fiber plane parallel and orthogonal to load, respectively, was performed by means of neutron diffraction (ND) during in-situ compression tests at room temperature. ND results proved that damage occurrence in the fillers strongly depends on the preferential orientation of those, playing a crucial role in the failure of the sample. The computed tomography observations confirm the damage observations from curves of load partition analysis of each phase.