- Korrosion (26)
- Corrosion (8)
- Deckschichtbildung (7)
- Nichtrostender Stahl (7)
- Gelartige Elektrolyte (6)
- Korrosionsprüfung (4)
- Korrosionsschutz (4)
- Zink (4)
- Zinküberzüge (4)
- Additive Fertigung (3)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (79) (entfernen)
Eingeladener Vortrag
- nein (79) (entfernen)
High performance polymers of intrinsic microporosity (PIMs) have emerged as novel materials with broad applications from gas separation to electronic devices. Sufficiently rigid, even contorted polymer chains show only limited molecular mobility, therefore undergo inefficient packing and give rise to intrinsic microporosity with pore size generally smaller than 1 nm and BET surface areas larger than 700 m2/g. Further performance optimization and long-term stability of devices incorporating PIMs rely on our understanding of structure-processing-property relationships and physical aging, in which glass transition plays a key role. Up to now no glass transition temperature (Tg) of PIMs could be detected with conventional thermal analysis techniques before degradation. Decoupling the time scales responsible for the glass transition and the thermal decomposition is a reliable strategy to overcome this. This was achieved by employing fast scanning calorimetry (FSC) based on a chip sensor, which is capable to heat and cool a small sample (ng-range) with ultrafast rates of several ten thousand K/s. FSC provides definitive evidence of glass transition of a series of PIMs with a special consideration on the chain rigidity. The determined glass transition temperature of these PIMs follows the order of the rigidity of their backbone structures. FSC provides the first clear-cut experimental evidence of the glass transition of PIM-EA-TB with a Tg of 663 K, PIM-1 of 644 K and PIM-DMDPH-TB of 630 K at a heating rate of 1Χ104 K/s. Local fluctuations are featured in glass transition of highly rigid PIMs. As conformational changes are prevented by the backbone rigidity, the glass transition must rather be assigned to local small scale fluctuations.
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt.
Metallene Werkstoffe:
Weder örtliche Korrosion noch erhöhte Flächenkorrosion (Korrosionsrate:< 0,1 m/Jahr) sind bei den bisher geprüften Werkstoffen: Aluminium,
C-Stahl 1.0037, austenitischer CrNi-Stahl 1.4301, Kupfer und Messing in Heizöl und B20 (Heizöl mit 20% Biodiesel) aufgetreten. Diese Werkstoffe sind in den Prüfmedien Heizöl und B20 als beständig zu bewerten.
Es wurde keine signifikante Veränderung des pH-Wertes der Prüfmedien gemessen.
Polymere:
Massebestimmung:
Die Prüfkörper der Elastomere ACM, HNBR und PUR sowie in geringerem Maße PE neigten zur Quellung in Heizöl und B20 nach 42 d und 84 d Auslagerung; für PA 6, POM und PVC wurde keine Masseänderung gemessen. Die Masseänderung der Prüfkörper in Heizöl und B20 ist mit Ausnahme von PUR vergleichbar. Bei PE traten Verfärbungen durch die Brennstoffe auf.
Zugeigenschaften:
ACM, HNBR, PE und PVC sind in Heizöl und B20 beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 15 % beträgt. PA und POM sind bedingt beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 30% beträgt.
Compatibility of polymeric materials with heating oil/biodiesel blends at different temperatures
(2019)
Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with admixtures of 10 % biodiesel (B10) and 20 % biodiesel (B20).
The polarity of biodiesel increases its solvency and facilitates permeation and extrac-tion. Solvation, swelling and/or extraction lead to changes in the physical properties and chemical changes of polymeric materials.
The objective of this research was to determine the resistance of frequently used sealing materials such as FKM, EPDM, CR, CSM, NBR, IIR, VMQ, FVMQ, PA and PUR in up to four-year aged B10 for 84 days at 20 °C, 40 °C and 70 °C.
The polymeric materials: ACM, FKM, HNBR, PA, PE; POM, PUR and PVC were ex-posed to B20 for 84 days at 40°C and 70°C in another research project.
Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after the exposure for 84 (42) days in the heating oil blends B10 and B20.
There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was deter-mined for the evaluation of the compatibility.
Measurements of the variations in mass, tensile properties and Shore hardness after exposure of the polymers in non-aged and aged heating oil B10 showed clearly that FKM, FVMQ and PA were the most resistant materials in B10. The elastomers CR, CSM, EPDM, IIR, NBR and VMQ were generally not resistant to B10. Damage to the materials increased with higher test temperatures and the age of B10.
FKM, POM and PVC showed high compatibility in B20 at 40°C and 70 °C. ACM, HNBR and PA were evaluated as resistant in B20 at 40 °C but not at 70°C.
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt.
Die untersuchten Werkstoffe Aluminium, Stahl 1.0037, 1.4301, Kupfer, Messing (CuZn40Pb) und Zink (ZP0410) sind in B0, B20, B100 und in 6 Jahre altem B100 beständig.
Auch in einem Jahr alten B20 und in einem Jahr alten B100 sind die Werkstoffe beständig.
Bei Kupfer blieb die Korrosionsrate in der Flüssigphase sowohl in B20 (0 μ m/ a) als auch in B100 (4 μ m/ a) nach einem Jahr unverändert. Für das 6 Jahre alte B100 stieg die Korrosionsrate des Kupfers an (16 μ m/a). Im Gegensatz dazu sank bei Messing die Korrosionsrate in der Flüssigphase mit dem Alter des Brennstoffs, nach einem Jahr für B20 von 4 μ m/ a auf 1 μ m/a und für B100 von 36 μ m/ a auf 6 μ m/ a, im 6 Jahre alten B100 lag die Korrosionsrate des Messings bei 0 μ m/ a.
In 8 Jahre altem B10 trat bei Zink in der Flüssigphase Flächenkorrosion auf, es ist in dem Medium demnach nicht beständig. Messing zeigte örtliche Korrosion in der Gasphase, es ist folglich unbeständig und für den Einsatz in stark gealterten B10 nicht geeignet.
Aluminium, 1.0037, 1.4301 und Kupfer sind in dem 8 Jahre alten B10 beständig.
Die Änderung der Zugfestigkeit und der Reißdehnung von ACM, HNBR und FKM in Heizöl, B20 und gealterten B10 beträgt < 15 %. Diese Werkstoffe sind in Heizöl, B20 und in gealterten B10 unter Berücksichtigung des von der BAM zur Beurteilung der Beständigkeit festgelegten Grenzwertes von 15 % bei 40 °C als beständig zu bewerten.
PUR ist bei 40 °C nicht beständig in B20 und in gealtertem B10. Bei 70 °C ist HNBR nicht in B20 beständig aufgrund der Verringerung der Zugfestigkeit (40 %) und der Reißdehnung (50 %). FKM ist bei 70 °C in Heizöl und in B20 beständig.
Biodiesel is subject to degradation processes like oil and grease. The oxidative degradation products of vegetable oil esters in biodiesel particularly lead to enhanced sedimentation in blended fuels.
The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties and chemical changes of polymeric materials. It also accelerates the degradation (hydrolysis and oxidation) of these materials with the loss of additives and stabilizers.
The objective of this research was to determine the resistance of frequently used polymeric materials such as ACM, EPDM, FKM, FVMQ, CR, CSM, IIR, HNBR, NBR, PA, PE; POM, PUR, PVC and VMQ in biodiesel and heating oil with 10 %/20 % biodiesel (B10/B20) at 40°C and 70°C.
Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the biodiesel heating oil blends. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D were determined before and after exposure of the test specimens in the biofuels for 42 days.
The elastomers CR, CSM, EPDM, IIR, NBR and VMQ were generally not resistant to biodiesel and B10 at 40°C and 70°C. FKM, ACM, HNBR, PA, PE, POM, and PVC showed high compatibility in B10/B20 at 40°C. A lower compatibility was determined for ACM in biodiesel. ACM and HNBR were not resistant in B20 at 70°C.
Biodiesel is viewed as a major source of energy. In areas such as the European Union, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies.
Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil.
The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers.
The objective of this research was to determine the resistance of frequently used materials for components in middle distillate facilities such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and heating oil blend B20 for 84 days at 40 °C, and FKM, HNBR, PA, POM, PUR and PVC at 70 °C.
Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions.
For the investigations under compressed conditions, the mass and the compression set of FKM test specimens were determined before and after exposure for 3, 7, 14, 28, 56 and 90 days in B20 at 40 °C and 70 °C according to ISO 815-1 “Rubber, vul-canized or thermoplastic - determination of compression set – Part 1: At ambient or elevated temperatures”.
There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was determined for the evaluation of the compatibility.
The change of tensile strength and breaking elongation of test specimens made of ACM, FKM, HNBR, PA, PE, POM, PUR and PVC exposed to heating oil and the blend B20 was less than 15 % at 40 °C. A maximum reduction in Shore hardness A of 14 % was determined for ACM at 40 °C and for HNBR of 15 % at 70 °C.
It can be concluded that ACM, FKM, HNBR, PA, PE, POM, PVC and PUR were resistant in B20 at 40°C. FKM, PA, POM and PVC were evaluated as resistant in heat-ing oil and B20 at 70 °C, HNBR and PUR were not resistant in these fuels at 70°C.
Based on the mass increase and compression set values of FKM test specimens it can be stated that FKM is resistant in B20 under compressed conditions at 40 °C and 70 °C.
AKR an Betonfahrbahndecken - ausgewählte Einflussgrößen und neuartige AKR-Vermeidungsstrategie
(2019)
In den letzten Jahren sind im deutschen Bundesautobahnnetz vermehrt Schäden an vor 2005 hergestellten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion(AKR) in Verbindung gebracht werden. Vor diesem Hintergrund werden in diesem Beitrag zunächst die Voraussetzungen und ausgewählte Einflussgrößen für eine schädigende AKR aufgezeigt.
Besondere Aufmerksamkeit wird dabei der Rolle des Tausalzeintrags durch den Winterdienst bei Betonfahrbahndecken geschenkt. So wird mit Löseversuchen in 1 M KOH-Lösung zweier Gesteinskörnungen bei 80 °C gezeigt, dass mit zunehmender NaCI-Zugabe die Löslichkeit von SiÖ2 zunimmt und die von AI2O3 eine Verminderung erfährt. Basierend auf dem so exemplarisch erbrachten Nachweis für die Verstärkung der schädigenden AKR durch das Tausalz wird die Notwendigkeit und Richtigkeit der Durchführung von AKR-Betonversuchen mit Alkalizufuhr im ARS 04/2013 zur zukünftigen Vermeidung von AKR-Schäden an Betonfahrbahndecken im Rahmen von Neubau- und Erneuerungsmaßnahmen im Bundesfernstraßennetz belegt. Zusätzlich durchgeführte WS-Grundprüfungen nach dem ARS 04/2013 mit den beiden Gesteinskörnungen der Löse versuche veranschaulichen, dass die nach der Alkali-Richtlinie des DAfStb als unbedenklich eingestuften Gesteinskörnungen bei den Betonversuchen mit Alkalizufuhr durchaus als alkaliempfindlich bewertet werden können. Dies wiederum führt zu einer Verminderung der für den Betonstraßenbau verfügbaren Gesteinskörnungen.
Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung der als grenzwertig alkaliempfindlich eingestuften Gesteinskörnungen erlaubt.
Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungsprozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innenhydrophobierung zur Vermeidung bzw. Verminderung einer schädigenden AKR in Betonfahrbahndecken wird zurzeit im Aufträge der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste Ergebnisse dieses Projekts vorgestellt. So wird exemplarisch an einem Oberbeton (D > 8)/Unterbeton und einem Oberbeton 0/8 mit einer alkaliempfindlichen Gesteinskörnung der Einfluss zweier Hydrophobierungsmittel auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss beider Hydrophobierungsmittel auf die schädigende AKR mittels AKR-Betonversuchen mit Alkalizufuhr beleuchtet. Dabei gelangen ergänzend zur Beurteilung des Tausalzeintrags die Laser-Induced Breakdown Spectroscopy (LIBS) und zur Bewertung der Ausprägung der AKR und sekundären Ettringitbildung (SEB) die Dünnschliffmikroskopie zum Einsatz.
Verstärkt auftretende Schäden in Betonfahrbahndecken des Bundesfernstraßennetzes, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden, haben zu einer massiven Verschärfung der Prüfvorschriften zur Bewertung der Alkaliempfindlichkeit von Ge-steinskörnungen geführt. Die damit verbundene Einschränkung potenziell für den Straßenbau einsetzbarer Gesteinskörnungen ruft eine verstärkte Ressourcenknappheit und ein erhöhtes Transport- und damit einhergehendes Kostenaufkommen hervor. Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung grenzwertig alkaliempfindlich eingestufter Gesteinskörnungen erlaubt. Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungs-prozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innen-hydrophobierung zur Vermeidung einer schädigenden AKR in Betonfahrbahndecken wird zur-zeit im Auftrage der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste ausgewählte Ergebnisse dieses Forschungsvorhabens vorgestellt. So wird exemplarisch an einem Oberbeton (0/8) mit einer alkaliempfindlichen Gesteinskörnung der Einfluss eines Hydrophobierungsmittels auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss der Innenhydrophobierung auf die schädigende AKR mittels verschiedenartiger AKR-Performanceprüfungen beleuchtet.
Ziel des Projektes ist die Qualifizierung von Duplexstählen in Tunnelbauwerken um die Einsatzmöglichkeiten alternativer nichtrostender Stähle zu den bislang gebräuchlichen rostfreien Edelstählen 1.4404 und 1.4571 zu eruieren. Da Duplexstähle im Vergleich zu austenitischen Stählen über eine doppelt so hohe Festigkeit verfügen, können Bauteile schlanker konstruiert werden, wodurch Material eingespart werden kann. Neben der Wirtschaftlichkeit muss die Dauerhaftigkeit untersucht werden. Dazu wurden speziell konzipierte Wand- und Deckenracks mit unterschiedlichen metallenen Werkstoffen und Oberflächen hergestellt und in den Tunnelbauwerken montiert. Nach bestimmten Auslagerungszeiten von bis zu drei Jahren werden die Proben demontiert und auf ihr Korrosionsverhalten untersucht. Ein weiteres Ziel neben der Qualifizierung der Werkstoffgruppe sind die Reduktion der Instandsetzungs- und Wartungsmaßnahmen der Tunnelbetreiber
Ziel des Projektes ist die Qualifizierung von Duplexstählen in Tunnelbauwerken um die Einsatzmöglichkeiten alternativer nichtrostender Stähle zu den bislang gebräuchlichen rostfreien Edelstählen 1.4404 und 1.4571 zu eruieren. Da Duplexstähle im Vergleich zu austenitischen Stählen über eine doppelt so hohe Festigkeit verfügen, können Bauteile schlanker konstruiert werden, wodurch Material eingespart werden kann. Neben der Wirtschaftlichkeit muss die Dauerhaftigkeit untersucht werden. Dazu wurden speziell konzipierte Wand- und Deckenracks mit unterschiedlichen metallenen Werkstoffen und Oberflächen hergestellt und in den Tunnelbauwerken montiert. Nach bestimmten Auslagerungszeiten von bis zu drei Jahren werden die Proben demontiert und auf ihr Korrosionsverhalten untersucht. Ein weiteres Ziel neben der Qualifizierung der Werkstoffgruppe sind die Reduktion der Instandsetzungs- und Wartungsmaßnahmen der Tunnelbetreiber.