By the combination of an optimized granulometry, a reduced water cement ratio and the use of superplasticizers ultra-high performance concrete achieves a compressive strength of over 150 N/mm2 and a high resistance regarding acids and water-soluble salts. In different Research projects the effect of an autoclavation on the mechanical strength and the phase composition was analyzed. In systematic studies, the concrete mix and the process parameters were varied.
The results show that autoclavation leads to an improved pozzolanic and hydraulic reaction and significantly improves the mechanical strength compared to a conventional thermal treatment. If a minimum time-span for hydration is ensured, the achievable strength level is not dependent on the prestorage time. However, the duration of the autoclaving is significant. After the Maximum strength is reached there is only a very slight decrease, even if unrealistically long autoclaving times are applied.
By the combination of an optimized granulometry, a reduced water cement ratio and the use of superplasticizers ultra-high performance concrete achieves a compressive strength of over 150 N/mm2 and a high resistance regarding acids and water-soluble salts. In different Research projects the effect of an autoclavation on the mechanical strength and the phase composition was analyzed. In systematic studies, the concrete mix and the process parameters were varied.
The results show that autoclavation leads to an improved pozzolanic and hydraulic reaction and significantly improves the mechanical strength compared to a conventional thermal treatment. If a minimum time-span for hydration is ensured, the achievable strength level is not dependent on the prestorage time. However, the duration of the autoclaving is significant. After the Maximum strength is reached there is only a very slight decrease, even if unrealistically long autoclaving times are applied.
This paper presents the development of ultra-high performance concrete (UHPC) for façade elements with self-cleaning properties. For creating self-cleaning surfaces two different approaches are proposed. One approach is based on the photocatalytic activation of the external UHPC shell by incorporation of TiO2 particles. The second approach consists of the modification of the UHPC surface by micro structuring in combination with the application of hydrophobic agents to create durable super hydrophobicity. In the framework of the H-HOUSE Project funded by the European Commission the experimental investigations were performed with UHPC based on Dyckerhoff Nanodur® technology. The special properties of this material enable the precise reproduction of any micro structure without flaws. The current results obtained from laboratory and outdoor weathering tests are promising and demonstrate the feasibility of the approaches.
The aim of this study was to develop a lightweight composite façade element for refurbishment of existing façades. It was crucial to minimize the thermal bridges and to undercut the thermal requirement of the system existing façade new element. The awareness of the environmental impact of the building sector is increasing. In this context, ultra-high performance concrete (UHPC) materials are shown to be promising alternatives with advantages such as lower embodied energy and reduced environmental impact. Predictions suggest that UHPC composite elements for building envelopes could have other benefits such as an increased service life, optimized use of building area due to thinner elements and minimized maintenance due to the absence of reinforcement or use of non-corrosive reinforcing materials such as carbon fibers. In this framework, composite elements have been developed combining an autoclaved aerated concrete insulation layer with an external UHPC supporting layer. The results show that the lightweight composite element has a good performance in term of thermal transmittance and minimization of thermal bridges.
Thermal treatment improves the excellent properties of UHPC. Recent studies have shown that an increase in compressive strength of more than 30 % is possible. However, the accurate conditions of thermal treatment for a maximal strength are considered as yet undetermined. A multitude of parameters can be varied: temperature, pressure, water saturation, and duration of the process steps. These parameters influence the phase development and in consequence the macroscopic properties of UHPC. The primary objective of the presented study was the optimisation of the conditions for thermal treatment, concerning compressive strength. It focuses on pre-storage time and duration of the treatment at defined temperatures and pressures (90 °C and 185 °C/1.1MPa).
As expected, experimental results showed a fundamental change of phase composition in hydrothermally treated UHPC in comparison to standard cured UHPC: Ettringite decomposes at higher temperatures and is absent after thermal treatment; the amount of portlandite and clinker phases decreases. The change of phase composition is accompanied by increased compressive strength.
Experimental studies of calcium-silicate-systems at hydrothermal conditions predict the formation of the crystalline C-S-H phase tobermorite. In fact, this is a typical phase occurring in other hydrothermally treated calcium-silicate-systems like Autoclaved Aerated Concrete (AAC). Commonly, high strength is attributed to the presence of tobermorite; however, in the presented study tobermorite was not detected in the hydrothermally treated UHPC. Therefore, tobermorite cannot be responsible for the increased strength of hydrothermally treated UHPC.
In conclusion the development of phases and strength of UHPC at hydrothermal conditions differs fundamentally from AAC and the experimental studies with water saturation. Results of these systems cannot be transferred to UHPC. In thermally treated UHPC, the hydration of clinker is enhanced and the puzzolanic reaction is intensified. Hence, more C-S-H is formed that fills pores and cracks, leading to a denser structure and finally to higher strength.
Thermal treatment improves the excellent properties of UHPC. Recent studies have shown that an increase in compressive strength of more than 30 % is possible. However, the accurate conditions of thermal treatment for a maximal strength are considered as yet undetermined. A multitude of parameters can be varied: temperature, pressure, water saturation, and duration of the process steps. These parameters influence the phase development and in consequence the macroscopic properties of UHPC. The primary objective of the presented study was the optimisation of the conditions for thermal treatment, concerning compressive strength. It focuses on pre-storage time and duration of the treatment at defined temperatures and pressures (90 °C and 185 °C/1.1MPa).
As expected, experimental results showed a fundamental change of phase composition in hydrothermally treated UHPC in comparison to standard cured UHPC: Ettringite decomposes at higher temperatures and is absent after thermal treatment; the amount of portlandite and clinker phases decreases. The change of phase composition is accompanied by increased compressive strength.
Experimental studies of calcium-silicate-systems at hydrothermal conditions predict the formation of the crystalline C-S-H phase tobermorite. In fact, this is a typical phase occurring in other hydrothermally treated calcium-silicate-systems like Autoclaved Aerated Concrete (AAC). Commonly, high strength is attributed to the presence of tobermorite; however, in the presented study tobermorite was not detected in the hydrothermally treated UHPC. Therefore, tobermorite cannot be responsible for the increased strength of hydrothermally treated UHPC.
In conclusion the development of phases and strength of UHPC at hydrothermal conditions differs fundamentally from AAC and the experimental studies with water saturation. Results of these systems cannot be transferred to UHPC. In thermally treated UHPC, the hydration of clinker is enhanced and the puzzolanic reaction is intensified. Hence, more C-S-H is formed that fills pores and cracks, leading to a denser structure and finally to higher strength.