Zinc oxide - polymer interfaces are known to exhibit interesting properties regarding molecular adhesion. This work is aimed at the investigation of the effect of the morphology and surface chemistry on the macroscopic adhesion of a model epoxy-based adhesive to nanorod (ZnO NR) and nanocrystalline (ZnO NC) ZnO-modified surfaces. Both ZnO films have been prepared using hydrothermal synthesis on hot-dip galvanized steel (HDG) surfaces by varying the precursor chemistry in order to control the film morphology. Poly (acrylic acid) (PAA) was used to improve the interfacial adhesion by modifying the morphology and surface chemistry of ZnO nanostructured films. The strong interaction of PAA from a dilute and neutral aqueous solution with the ZnO nanocrystallites was shown to significantly improve the interfacial adhesion by means of a nanoetching process.
It was shown that the wet peel-forces correlate well with the considered morphology and surface chemistry.
Plasma polymers and electrospray-ionization (ESI) polymer layers are compared for most efficient adhesion promotion in carbon fiber-epoxy resin composites. The ultra-thin ESI layers (2–30 nm) of commercial poly(acrylic acid) and poly-(hydroxyethylmethacrylate) produce an significant increase of adhesion measured by single-fiber pull out tests.
However, plasma Treatment has also advantages, such as simultaneous activation of the fiber substrate. Chemical structure and composition are rather far from the regular structure of commercial polymers as deposited by ESI processing.
In contrast to most of the existing literature on plasma polymerization of acrylic acid (AA), not only the chemical structure and film thickness of the deposits were studied, but also a new way to obtain COOH-rich surfaces. This is an important aspect when applying the obtained coatings for biomedical and electronics applications. Therefore, acrylic acid/CO2 polymer films with a thickness of ca. 150 nm were deposited in the pulsed plasma regime onto polyethylene and aluminium as organic and inorganic substrates. Their structure–property relationships were studied in dependence on the mixture ratio of acrylic acid monomer and CO2 gas. The influence of the CO2 gas on the regularity and functionality of plasma deposited poly(acrylic acid) (PAA) was studied in detail using bulk-sensitive (dielectric spectroscopy and Fourier transforms infrared spectroscopy) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy. For a clear identification of the functionality of the deposited films, the COOH groups were estimated after derivatization with trifluoroethanol by XPS measurement as well as by the quantitative analysis of the FTIR data. Results show, in presence of a small amount of CO2 gas within the acrylic acid plasma, a structure of poly(acrylic acid) with high concentration of COOH groups was obtained. However, the excess of CO2 gas in the plasma chamber leads to fragmentation of the monomer or/and degradation of the layer which is already deposited. A polymer network is obtained with an increasing abundance of branched groups for AA/CO2 with increasing CO2 gas in the mixture.