With increasing focus on industrialized processing, investigating, understanding, and modelling the structural build-up of cementitious materials becomes more important. The structural build-up governs the key property of fresh printable materials -- buildability -- and it influences the mechanical properties after the deposition. The structural build-up rate can be adjusted by optimization of the mixture composition and the use of concrete admixtures. Additionally, it is known, that the environmental conditions, i.e. humidity and temperature have a significant impact on the kinetic of cement hydration and the resulting hardened properties, such as shrinkage, cracking resistance etc. In this study, small amplitude oscillatory shear (SAOS) tests are applied to examine the structural build-up rate of cement paste subject to different temperatures under controlled humidity. The results indicate significant influences of the ambient temperature on the intensity of the re-flocculation (Rthix) rate, while the structuration rate (Athix) is almost not affected. A bi-linear thixotropy model extended by temperature dependent parameters coupled with a linear viscoelastic material model is proposed to simulate the mechanical behaviour considering the structural build-up during the SAOS test
MFC was used to study the corrosiveness of iron-utilizing methanogen, Methanobacterium IM1 under flow conditions. Comparing against electrical SRM, Desulfovibrio ferrophilus IS5, results showed under standard mesophilic conditions, average corrosion rates of Methanobacterium IM1 was double that of SRM. The highest corrosion rate of Methanobacterium IM1 reached up to 0.60 mm/yr under neutral conditions, and severe pitting was observed on the iron surface. Furthermore, the corrosion products of Methanobacterium IM1 were characterized with TOF-SIM, FIB-SEM and EDX, and preliminary results revealed FeCO3 is not the only corrosion product of Mi-MIC, as previously reported. Under low pH conditions, the maximum corrosion rate of Methanobacterium IM1 reached 1.57 mm/yr, which resulted in severed deformity of the iron specimen. Additional comparisons using different types of incubation material were conducted to standardize MFC MIC testing.
This work presents the use of limited experimental measurements to develop a set of calibrated Simulation parameters that can then be used for reliable simulation of subsea pipeline inspections. The modelling software aRTist is used as the simulation tool, and the calibration is through comparison with experimental images of a well characterised sample in a water tank. Image Quality parameters such as signal-to-noise ratio, contrast and basic spatial resolution are compared with the aim of matching simulated values to experimental results. Currently the model is partially calibrated, with signal-to-noise ratio successfully matched while differences are still found in contrast-to-noise ratio comparisons. This means that measurements depending on absolute intensity are not accurate enough in the simulation at this stage. However, the simulation is found to be accurate for wall thickness measurements in tangential images, which are not based on absolute intensity, with simulated and experimental cases producing similar results.