It is known that the spalling risk of dense, high-strength concretes (HSC) can be reduced by the addition of polypropylene (PP) fibres and, in particular, PP-fibres that have been pre-treated using electron irradiation. It is presumed that the enhanced reduction in spalling resulting from electron irradiation pre-treatment of the fibres can be attributed to enhanced penetration of the molten fibre material into the micro-cracks around the fibres, due to their significantly decreased viscosity. So far there has been no experimental evidence for this. Against this background, this paper gives a com-parative analysis of the mode of action of PP-fibres with and without pre-treatment using multi-scale test methodology.
Initially, fire tests on small-scale building components with accompanying damage monitoring veri-fied that the amount of PP-fibres can be halved by using pre-treated PP-fibres without reducing the fire performance of HSC. Detailed investigations of PP-fibres carried out in a completed research project funded by DFG (the German Research Foundation) using digital scanning calorimetry and thermogravimetry measurements (DSC/TG) as well as viscometer measurements showed that the pre-treatment has no significant influence on the melting temperature of the PP-fibres. However, a drastic reduction of the melt viscosity due to the electron irradiation was detectable. Additional dila-tation tests showed that the expansion behaviour of both fibre types and their melts do not differ significantly [1]. Rather, both fibre types generate high pressures when their thermal expansion is hindered. Further detailed investigations by means of continuous heating tests with a low heating rate were carried out on separately produced concrete cylinders. These tests showed that the pre-treatment of the PP-fibres causes earlier dehydration in conjunction with stagnation of thermal expansion of the concrete cylinders (temperature reduction from 180 °C to 170 °C). This is accompanied by in-creased acoustic emission activity during the thermal expansion tests. This leads to the assumption that the pre-treatment of PP-fibres results in earlier micro-crack development. However, it was not possible to confirm this assumption by microscopic examination of drilling cores with a diameter of 30 mm exposed to defined temperatures in the range between 150°C and 300°C. Microscopic obser-vations and additional X-ray 3D computed tomography (3D-CT) scans on miniaturised drilling cores exposed to temperature cycles showed a similar networking of fibre beds by means of micro-cracks in HSC for both fibre types. However, energy dispersive X-ray spectroscopy and wavelength disper-sive X-ray spectroscopy revealed fundamental differences in the penetration capacity of the fibre melts of the two fibre types. The increased penetration of the pre-treated PP-fibre melt revealed in these tests, confirms the initial working hypothesis.
It is known that the spalling risk of dense, high-strength concretes (HSC) can be reduced by the addition of polypropylene (PP) fibres and, in particular, PP-fibres that have been pre-treated using electron irradiation. It is presumed that the enhanced reduction in spalling resulting from electron irradiation pre-treatment of the fibres can be attributed to enhanced penetration of the molten fibre material into the micro-cracks around the fibres, due to their significantly decreased viscosity. So far there has been no experimental evidence for this. Against this background, this paper gives a com-parative analysis of the mode of action of PP-fibres with and without pre-treatment using multi-scale test methodology.
Initially, fire tests on small-scale building components with accompanying damage monitoring veri-fied that the amount of PP-fibres can be halved by using pre-treated PP-fibres without reducing the fire performance of HSC. Detailed investigations of PP-fibres carried out in a completed research project funded by DFG (the German Research Foundation) using digital scanning calorimetry and thermogravimetry measurements (DSC/TG) as well as viscometer measurements showed that the pre-treatment has no significant influence on the melting temperature of the PP-fibres. However, a drastic reduction of the melt viscosity due to the electron irradiation was detectable. Additional dila-tation tests showed that the expansion behaviour of both fibre types and their melts do not differ significantly [1]. Rather, both fibre types generate high pressures when their thermal expansion is hindered. Further detailed investigations by means of continuous heating tests with a low heating rate were carried out on separately produced concrete cylinders. These tests showed that the pre-treatment of the PP-fibres causes earlier dehydration in conjunction with stagnation of thermal expansion of the concrete cylinders (temperature reduction from 180 °C to 170 °C). This is accompanied by in-creased acoustic emission activity during the thermal expansion tests. This leads to the assumption that the pre-treatment of PP-fibres results in earlier micro-crack development. However, it was not possible to confirm this assumption by microscopic examination of drilling cores with a diameter of 30 mm exposed to defined temperatures in the range between 150°C and 300°C. Microscopic obser-vations and additional X-ray 3D computed tomography (3D-CT) scans on miniaturised drilling cores exposed to temperature cycles showed a similar networking of fibre beds by means of micro-cracks in HSC for both fibre types. However, energy dispersive X-ray spectroscopy and wavelength disper-sive X-ray spectroscopy revealed fundamental differences in the penetration capacity of the fibre melts of the two fibre types. The increased penetration of the pre-treated PP-fibre melt revealed in these tests, confirms the initial working hypothesis.
Nondestructive investigation of the VHCF-endurance on cyclically loaded CFRP by X-Ray-Refractography
(2016)
Carbon fiber-reinforced-plastics (CFRP) are already used under high-cycle- (HCF) and very-high-cycle-fatigue (VHCF) at relatively low loads not only in aerospace industry, but also in other growing markets like especially wind energy and increasingly also automotive industry. While the static strength of CFRP is satisfyingly predictable by means of layerwise-strenght-analysis and material data from single layers, it is more and more uncertain to predict residual strength or lifetime as the design lifetime increases. Previous studies showed that local minor cracks and inter-fiber-fracture (IFF) originate long before total failure of single layers. Reliable fatigue estimation for fiber-reinforced-plastics is not available at present. Subsequently safety-related primary structures made out of FRP are over dimensioned.
It is possible to detect the change of inner surface in a specimen by means of X-Ray-Refractography. This includes voids, intact fiber-matrix-interfaces as well as defective ones, cracks and all interfaces in plane with the X-Ray-beam. As the crack-density (including IFF) increases, the inner surface of the material correspondingly increases.
The borderline where even at high cycles no early cracks were detected was identified for selected laminates out of woven and non-crimped fabric with epoxy-matrix.
When no micro-cracks were detected up to 106 cycles, the specimens also lasted in the VHCF-regime. Furthermore for the epoxy resin LY556 in combination with carbon fiber it was distinguished that at a load minor to 50% IFF-load level, no micro cracks were detected and consequently the VHCF-endurance reached.
The integration of the set-up small-sized testing machine into the X-Ray buildup in order to achieve in-situ non-destructive detection of the crack initiation while loading the specimens (CFRP and GFRP- woven fabric and non-crimped-fabric) at the same time will increase the performance of the studies.
In earlier investigations at BAM it was shown, that the matrix has a strong influence on the micro-crack formation and finally on the total lifetime. In order to determine the influence of the matrix properties on the boarderline to infinite life, research is done on laminates while replacing the epoxy-based matrix with an equivalent one with different fracture mechanical properties.
With the evolution of early cracks and IFF monitored as well as the influence of the matrix on the crack propagation investigated we are working on an appropriate model to improve lifetime prediction in CFRP. This work is done within the priority program “infinite life” (SPP 1466) funded by Deutsche Forschungsgemeinschaft (DFG).