The passivation behavior of alloy 31 was investigated as a function of passivation potential in a green-death solution at 40 °C. The alloy 31 surface is in a stable passive state during cyclic potentiodynamic polarization. In potentiostatic polarization of alloy 31, passive current density increases with an increase in the passivation potential. Electrochemical impedance spectroscopy (EIS) and Mott–Schottky (M–S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The increase of the applied potential is considered to be a reason for the change in passive film stability.
The aim of the work presented was the evaluation of corrosion resistance
of various materials in geothermal Waters as a base to create a catalogue of suitable materials for applications in (not only) German geothermal power plants.
Users shall be enabled to have a basis for designing such facilities. High alloyed corrosion resistant alloys are suitable and do not cause copper or lead deposition. They shall be chosen for future design of the piping system, either in massive or in cladded form, if crevices formation with non-metallic materials can be prevented!
The electrochemical behavior of UNS N08031 was investigated as a function of electrode potential in Green-Death solution at 40 °C. The UNS N08031 surface is in a stable passive state during cyclic potentiodynamic polarization without an initiation and/or propagation of localized corrosion. In potentiostatic polarization of UNS N08031 for 3600 s, passive current density increases with an increase in the passivation potential from 0.7 to 1.0 VSSE (silver/silver chloride reference electrode in saturated potassium chloride) Electrochemical impedance spectroscopy (EIS) and Mott-Schottky (M-S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The mechanism of the defective passive film formation is discussed. The increase of the applied potential is considered to be a reason for the change in passive film stability.