We demonstrate the potential of time-resolved luminescence spectroscopy for the straightforward assessment and in situ monitoring of the stability of upconversion nanocrystals (UCNPs). Therefore, we prepared hexagonal NaYF4:Yb3+,Er3+ UCNPs with various coatings with a focus on phosphonate ligands of different valency, using different ligand exchange procedures, and studied their dissolution behaviour in phosphate-buffered saline (PBS) dispersions at 20 °C and 37 °C with various analytical methods. The amount of the released UCNPs constituting fluoride ions was quantified by potentiometry using a Fluoride ion-sensitive electrode and particle disintegration was confirmed by transmission electron microscopy studies of the differently aged UCNPs. In parallel, the luminescence features of the UCNPs were measured with special emphasis on the lifetime of the sensitizer emission to demonstrate its suitability as Screening parameter for UCNP stability and changes in particle composition. The excellent correlation between the changes in luminescence lifetime and fluoride concentration highlights the potential of our luminescence lifetime method for UCNP stability screening and thereby indirect monitoring of the release of potentially hazardous fluoride ions during uptake and dissolution in biological systems. Additionally, the developed in situ optical method was used to distinguish the dissolution dynamics of differently sized and differently coated UCNPs.
We studied the dissolution behavior of β NaYF4:Yb(20%), Er(2%) UCNP of two different sizes in biologically relevant media i.e., water (neutral pH), phosphate buffered saline (PBS), and Dulbecco’s modified Eagle medium (DMEM) at different temperatures and particle concentrations. Special emphasis was dedicated to assess the influence of different surface functionalizations, particularly the potential of mesoporous and microporous silica shells of different thicknesses for UCNP stabilization and protection. Dissolution was quantified electrochemically using a fluoride ion selective electrode (ISE) and by inductively coupled plasma optical emission spectrometry (ICP OES). In addition, dissolution was monitored fluorometrically. These experiments revealed that a thick microporous silica shell drastically decreased dissolution. Our results also underline the critical influence of the chemical composition of the aqueous environment on UCNP dissolution. In DMEM, we observed the formation of a layer of adsorbed molecules on the UCNP surface that protected the UCNP from dissolution and enhanced their fluorescence. Examination of this layer by X ray photoelectron spectroscopy (XPS) and mass spectrometry (MS) suggested that mainly phenylalanine, lysine, and glucose are adsorbed from DMEM. These findings should be considered in the future for cellular toxicity studies with UCNP and other nanoparticles and the design of new biocompatible surface coatings.
We developed a procedure to prepare luminescent LiYF4:Yb/LiYF4 and LiYF4:Yb,Er/LiYF4 core/shell nanocrystals with a size of approximately 40 nm revealing luminescence decay times of the dopant ions that approach those of high-quality laser crystals of LiYF4:Yb (Yb:YLF) and LiYF4:Yb,Er (Yb,Er:YLF) with identical doping concentrations. As the luminescence decay times of Yb3+ and Er3+ are known to be very sensitive to the presence of quenchers, the long decay times of the core/shell nanocrystals indicate a very low number of defects in the core particles and at the core/shell interfaces. This improvement in the performance was achieved by introducing two important modifications in the commonly used oleic acid based synthesis. First, the shell was prepared via anewly developed method characterized by a very low nucleation rate for particles of pure LiYF4 shell material. Second, anhydrous acetates were used as precursors and additional drying steps were applied to reduce the incorporation of OH− in the crystal lattice, known to quench the emission of Yb3+ ions. Excitation power density (P)-dependent absolute measurements of the upconversion luminescence quantum yield (Φ,UC) of LiYF4:Yb,Er/LiYF4 core/shell particles reveal a maximum value of 1.25% at P of 180 W·cm−2.
Although lower than the values reported for NaYF4:18%Yb,2%Er core/shell nanocrystals with comparable sizes, these Φ, UC values are the highest reported so far for LiYF4:18%Yb,2%Er/LiYF4 nanocrystals without additional dopants. Further improvements May nevertheless be possible by optimizing the dopant concentrations in the LiYF4 nanocrystals.
Light-induced NO release based on exogenous NO donors has attracted substantial attention in clinical applications; the induction light source usually converts near-infrared light to blue or ultraviolet light.
However, the low efficiency of near-infrared light-assisted chemical light energy conversion remains a challenge, especially for NaYF4:Yb3+/Tm3+ photoconverting near-infrared light to ultraviolet (UV) and blue light. In this paper, a luminescence-enhanced strategy is reported by doping Ca2+ into NaYF4:Yb3+/Tm3+ and coating it with NaGdF4 through a two-step solvothermal method. Then, UCNPs modified with methyl-b-cyclodextrin (M-b-CD) are loaded on a ruthenium nitrosyl complex [(3)Ru(NO)(Cl)] as nitric oxide release-molecules (NORMs). X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDS) data demonstrated that Ca2+ was successfully doped into NaYF4:Yb3+/Tm3+ nanoparticles as the core, and a pure hexagonal phase, NaYF4, was obtained from the doping of Ca2+. TEM revealed that the crystallinity was significantly improved after Ca2+ doping, and the core–shell structure was successfully synthesized, with NaGdF4 directionally grown on the NaYF4:Ca/Yb/Tm core. Fluorescence tests showed that, especially in the ultraviolet and blue light excitation wavelength regions, the UC emission intensity of the Ca-doped NaYF4:Yb3+/Tm3+@NaGdF4 core–shell UCNPs increased by 302.95 times vs. NaYF4:Yb3+/Tm3+ UCNPs. Finally, the release of NO was tested by the Griess method. Under 980 nm irradiation, the cell viability distinctly decreased with increasing UCNPs@M-b-CD-NORMs concentration. This study Shows that NORM release of NO is triggered by enhanced up-converted UV and blue light, which can be used for the development of UV photo-sensitive drugs.
Upconversion photoluminescence in hetero-oligonuclear metal complex architectures featuring organic ligands is an interesting but still rarely observed phenomenon, despite its great potential from a basic research and application perspective. In this context, a new photonic material consisting of molecular chromium(III) and ytterbium(III) complex Ions was developed that exhibits excitation-power density-dependent cooperative sensitization of the chromium-centered 2E/2T1 phosphorescence at approximately 775 nm after excitation of the ytterbium band 2F7/2!2F5/2 at approximately 980 nm in the solid state at ambient temperature. The upconversion process is insensitive to atmospheric oxygen and can be observed in the presence of water molecules in the crystal lattice.
Single particle imaging of upconversion nanoparticles (UCNPs) has typically been realized using hexagonal (β) phase lanthanide-doped sodium yttrium fluoride (NaYF4) materials, the upconversion luminescence (UCL) of which saturates at power densities (P) of several hundred W cm−2 under 980 nm nearinfrared (NIR) excitation. Cubic (α) phase UCNPs have been mostly neglected because of their commonly observed lower UCL efficiency at comparable P in ensemble level studies. Here, we describe a set of sub-15 nm ytterbium-enriched α-NaYbF4:Er3+@CaF2 core/shell UCNPs doped with varying Er3+ concentrations (5–25%), studied over a wide P range of ∼8–105 W cm−2, which emit intense UCL even at a low P of 10 W cm−2 and also saturate at relatively low P. The highest upconversion quantum yield (ΦUC) and the highest particle brightness were obtained for an Er3+ dopant concentration of 12%, reaching the highest ΦUC of 0.77% at a saturation power density (Psat) of 110 W cm−2. These 12%Er3+-doped core/shell UCNPs were also the brightest UCNPs among this series under microscopic conditions at high P of ∼102–105 W cm−2 as demonstrated by imaging studies at the single particle level. Our results underline the potential applicability of the described sub-15 nm cubic-phase core/shell UCNPs for ensemble- and single particle-
level bioimaging.
Synthesis of new upconversion (UC) materials that can convert near-infrared excitation light into visible emission light with high efficiency has crucial importance for energy and bio-applications. Herein, SrF2 single crystals with a doping concentration of 2 mol% Er3+ and 2–8 mol% Yb3+ were synthesized and the optical properties were studied. The absorption cross-section of the different doping ions was calculated. To identify the most efficient and brightest material absolute excitation power dependent UC photoluminescence quantum yields (ϕUC) and brightness values were determined. In addition, excitation characteristics and luminescence lifetimes were analysed to understand the changes in population pathways and possible quenching mechanisms. A dominant two-photon population behaviour of the red and green emission bands was observed for all investigated doping concentrations of Yb3+ and Er3+. The ϕUC value of 6.5% measured using 230 W cm−2 of 976 nm excitation for SrF2 crystal co-doped with 2 mol% Er3+ and 3 mol% Yb3+. These findings broaden the scope of efficient UC materials apart from the record UC material β-NaYF4:Yb3+, Er3+ and provide benchmark values for cubic-phase and especially SrF2- nano and micrometer sized materials.