Duplex steels are high-alloyed, stainless steels. They offer some physical advantages over other stainless steels due to the balanced phase ratio of austenite and ferrite. During welding processes, when welding fumes and vaporized material condensates, different chemical elements can accumulate on the surface of the solidified weld. Then, the formation of a protective chromium oxide layer is no longer guaranteed and pitting corrosion can occur at these places. Previous work has shown that the accumulation of manganese and chromium on the surface of the heat-affected zone of the welded high-grade steel 304L can be measured by LIBS.
We present the results of the optimization of LIBS parameters for precise thickness measurements of such thin films and for depth profile measurements Therefore, we used galvanically coated copper samples with known film thicknesses. The Concentration of manganese is reduced in the weld metal. This has a high impact on the metallografic structure of the material.
Erstellung von Tiefenprofilen auf Schweißnähten mittels Laserinduzierter plasmaspektroskopie (LIPS)
(2021)
Duplexstähle sind hochlegierte, nichtrostende Stähle. Sie bieten aufgrund des ausgewogenen Phasenverhältnisses von Austenit und Ferrit einige physikalische Vorteile gegenüber anderen nichtrostenden Stählen. Beim Schweißen können sich durch die Kondensation von Schweißrauch und verdampftem Material verschiedene chemische Elemente auf der Oberfläche der erstarrten Schweißnaht anreichern. Dann ist die Bildung einer schützenden Chromoxidschicht nicht mehr gewährleistet und es kann an diesen Stellen zu Lochfraß kommen. Frühere Arbeiten haben gezeigt, dass die Anreicherung von Mangan und Chrom an der Oberfläche der Wärmeeinflusszone des geschweißten Edelstahls 304L mit LIBS gemessen werden kann. Wir stellen die Ergebnisse der Optimierung der LIBS-Parameter für präzise Dickenmessungen solcher dünnen Schichten und für Tiefenprofilmessungen vor. Dazu haben wir galvanisch beschichtete Kupferproben mit bekannten Schichtdicken verwendet. Die Mangankonzentration im Schweißgut ist reduziert. Dies hat einen großen Einfluss auf die metallografische Struktur des Materials.
Welding processes of duplex stainless steels cause an unbalanced austenite (γ)/ferrite (δ) ratio due to high cooling rates and changes in chemical composition. That causes a degradation of mechanical properties and corrosion resistance. In situ monitoring of the weld pool is to be realized with the help of laser-induced breakdown spectroscopy (LIBS). A major advantage of this technique is the highly accurate time and spatially resolved measurement of the chemical composition during welding. Previous research has established that the LIBS method is suitable to detect chemical elements during welding and to show a distribution of selected elements. Chemical composition in the WM and HAZ can now be quantified using calibration curves generated by certified reference materials (CRM). Furthermore, a cooling rate can be plotted against the measured electron temperature.
Schweißprozesse von nichtrostenden Duplexstählen verursachen aufgrund hoher Abkühlungsraten und Änderungen der chemischen Zusammensetzung ein unausgewogenes Austenit (γ)/Ferrit (δ)-Verhältnis. Das verursacht eine Degradation der mechanischen Eigenschaften und der Korrosionsbeständigkeit. Die In-situ-Überwachung des Schweißbades soll mit Hilfe der laserinduzierten Plasmaspektroskopie (LIPS) realisiert werden. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. Bisherige Untersuchungen haben ergeben, dass die LIBS-Methode geeignet ist, chemische Elemente während des Schweißens zu detektieren und eine Verteilung ausgewählter Elemente aufzuzeigen. Chemische Zusammensetzungen können mit vorab erstellten Kalibrierkurven dargestellt weerden.