The coefficient of thermal expansion (CTE) and the thermomechanical properties of the polymers used in superconducting magnets need to be known in order to predict their stress state under the different magnet assembly and operating conditions.
We have measured Young’s moduli of typically used polymers during in situ heat cycles with the dynamic resonancemethod. The dynamic test results are compared with Young’s moduli determined from quasi-static stress–strain measurements at room temperature, 77 K and 4.2 K. A moderate elastic anisotropy is found for the fiber reinforced polymers. CTEs are compared based on dilation experiments. TheCTEs of the fiber reinforced polymers studied are similar to those of copper or steel. In contrast, the pure resins exhibit relatively larger CTEs.
The knowledge of the temperature-induced changes of the superconductor volume and of the thermomechanical behavior of the different coil and tooling materials is required for predicting the coil geometry and the stress distribution in the coil after the Nb3Sn reaction heat treatment. In this paper, we have measured the Young’s and shear moduli of the HL-LHC 11 T Nb3Sn dipole magnet coil and reaction tool constituents during in situ heat cycles with the dynamic resonance method. The thermal expansion behaviors of the coil components and of a free standing Nb3Sn wire were compared based on dilation experiments.
The magnetic plasma confinement system of the nuclear fusion experiment “Wendelstein 7-X”, which recently produced the first plasma, consists of 20 planar and 50 non-planar superconducting coils. To keep them precisely in position, these coils contact each other at special support elements. The supports are operated in high vacuum at a temperature of about 4 K, and when the magnetic field is ramped up, forces up to 1500 kN and sliding motion of some mm occurs. Because mechanical disturbances may cause severe failures, only low friction without any stick-slip behaviour is tolerable. In pre-tests a PVD-MoS2-coating had proven to be the optimum solution. It was tested with downsized samples in reciprocating motion in liquid nitrogen (T = 77 K) and liquid helium (T = 4,2 K). In long-term tests in liquid nitrogen this coating showed stable sliding for up to 14.900 friction cycles without coating failure. However, in liquid helium an unexpected stick-slip effect occurred, whose origin could not be clarified so far.