Duplex stainless steels (DSS) are used in all industries where corrosion problems play a major role. Examples include the chemical industry, the food industry and shipping industries. DSS have a balanced phase ratio of ferrite (α) and austenite (γ). Unlike single-phase stainless steels, DSS combine the advantages of these and can therefore fit many industry requirements, such as weight saving or high mechanical strength. When these steels are welded, alloying elements can burn off and condense as thin layers on cold surface regions. This loss of chemical elements can lead to changes in the microstructure. With the help of Laser-Induced Breakdown Spectroscopy (LIBS), chemical element distributions were visualized. The results were compared with those of conventional measurement methods, such as energy dispersive X-ray analysis (EDS) and X-ray fluorescence analysis (XRF), and the results from LIBS could be validated. LIBS is suitable as a fast, straightforward measurement method for producing line scans along the weld seam and provides spatially resolved information on accumulation phenomena of burned off alloying elements. LIBS is very well suited for the detection of sub-surface elements due to the exclusively superficial ablation of the material. In addition, the measurement method has been calibrated so that quantitative statements about element concentrations can also be made.
Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process.
Nichtrostende Duplexstähle (DSS) werden häufig verwendet, insbesondere bei Anwendungen, die eine hohe Festigkeit in Verbindung mit einer hohen Korrosionsbeständigkeit in aggressiven Medien erfordern. Beispiele hierfür sind Kraftwerkskomponenten und maritime Anwendungen. Beim Schweißen dieser Stähle kann es zu lokalen Schwankungen in der chemischen Zusammensetzung kommen. Dies führt zu einer Ferritisierung des Werkstoffs und beeinträchtigt die mechanischen Eigenschaften der Bauteile. In dieser Arbeit wurden Versuche zum Wolfram-Inertgas-Schweißen (WIG) mit DSS durchgeführt. Die Analyse der chemischen Zusammensetzung wurde in situ mit Hilfe der laserinduzierten Plasmaspektroskopie (LIBS) durchgeführt. Ziel der Arbeit ist es, die chemische Zusammensetzung in der Schweißnaht verschiedener DSS quantitativ zu messen und mögliche Einflüsse der Schweißparameter auf die Mikrostruktur des Werkstoffs zu ermitteln. Gemessen wurden die chemischen Konzentrationen der Hauptlegierungselemente Cr, Ni, Mn auf der Oberfläche der Probe während des Schweißprozesses und des Abkühlungsprozesses. Mn und Ni sind Austenitstabilisatoren, deren Gehalt beim Schweißen durch die Verwendung bestimmter hochlegierter Schweißzusatzwerkstoffe zunimmt. Die Spektren wurden alle 1,3 s in einem Abstand von etwa 2 mm aufgezeichnet. Während des Abkühlungsprozesses wurde der Ort der Messung nicht verändert. Die LIBS-Methode eignet sich nachweislich zur quantitativen Darstellung der chemischen Zusammensetzungen während des Schweißvorgangs.
Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process.
Modeling of Hydrogen-Assisted Cracking (HAC) in Duplex Stainless Steels (DSS):
- Hydrogen causes significant degradation in DSS and consequently HAC
- Mechanisms of HAC have not been fully understood in two-phase microstructures
- Mesoscale numerical modeling for HAC in DSS was created, coupled to the macroscale, enabling simulation of HAC in both phases independent from predefined crack paths
The high corrosion resistance and good mechanical properties of duplex stainless steel (DSS) are due to its special chemical composition, which is a balanced phase ratio of ferrite (α) and austenite (γ). Many industrial applications require the integration of DSS components. For this, tungsten inert gas welding (TIG) is an excellent choice, as it allows an automated operation with high reproducibility. However, when the weld pool solidifies, critical ratios of α- and γ- phases can occur, which leads to solidification cracking, increased susceptibility to corrosion, and a decrease in ductility and critical strength. Previous studies have shown that these defects can be caused by the accumulation of manganese and chromium in the heat affected zone (HAZ), and this accumulation can be detected using LIBS.
Unlike conventional LIBS analyses, which requires reference samples to generate a calibration curve, calibration-free LIBS (CF-LIBS) can determine the chemical composition solely from the emission spectrum of the plasma. Numerous publications show that CF-LIBS is a fast and efficient analytical method for quantitative analysis of metal samples.
We present the results of in situ CF-LIBS analysis during TIG DSS welding. Using a new approach, it is possible to quantitatively determine the chemical composition of the weld metal directly in the welding process. The results of the CF-LIBS analysis are compared with the results of the calibration-based PLS analysis and reasonable agreement is found. Thus, the CF-LIBS method offers the significant advantage of quickly measuring in situ the concentrations of the main alloying elements that prevent the formation of welding defects, without the tedious calibration procedure.
Duplex steels are high-alloyed, stainless steels. They offer some physical advantages over other stainless steels due to the balanced phase ratio of austenite and ferrite. During welding processes, when welding fumes and vaporized material condensates, different chemical elements can accumulate on the surface of the solidified weld. Then, the formation of a protective chromium oxide layer is no longer guaranteed and pitting corrosion can occur at these places. Previous work has shown that the accumulation of manganese and chromium on the surface of the heat-affected zone of the welded high-grade steel 304L can be measured by LIBS.
We present the results of the optimization of LIBS parameters for precise thickness measurements of such thin films and for depth profile measurements Therefore, we used galvanically coated copper samples with known film thicknesses. The Concentration of manganese is reduced in the weld metal. This has a high impact on the metallografic structure of the material.
The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments.
Schweißprozesse von nichtrostenden Duplexstählen verursachen aufgrund hoher Abkühlungsraten und Änderungen der chemischen Zusammensetzung ein unausgewogenes Austenit (γ)/Ferrit (δ)-Verhältnis. Das verursacht eine Degradation der mechanischen Eigenschaften und der Korrosionsbeständigkeit. Die In-situ-Überwachung des Schweißbades soll mit Hilfe der laserinduzierten Plasmaspektroskopie (LIPS) realisiert werden. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. Bisherige Untersuchungen haben ergeben, dass die LIBS-Methode geeignet ist, chemische Elemente während des Schweißens zu detektieren und eine Verteilung ausgewählter Elemente aufzuzeigen. Chemische Zusammensetzungen können mit vorab erstellten Kalibrierkurven dargestellt weerden.
Die Kombination aus hoher Korrosionsbeständigkeit und guten mechanischen Eigenschaften von Duplexstählen (DSS) ist auf ihre chemische Zusammensetzung und das ausgewogene Phasenverhältnis von Ferrit (α) und Austenit (γ) zurückzuführen.
Viele industrielle Anwendungen erfordern eine stoffschlüssige Verbindung von DSS. Das Wolfram-Inertgas-Schweißen (WIG) ist relativ einfach zu handhaben, benötigt nur wenig Platz und ermöglicht ein automatisiertes Schweißen, mit sehr hoher Reproduzierbarkeit und ist daher hervorragend zum Schweißen von DSS.
Während der Erstarrung dieser Dualphasenstähle kann es zu kritischen Phasenverhältnissen von α und γ kommen, was zu Erstarrungsrissen, Korrosionsanfälligkeit, geringerer Duktilität und kritischen Festigkeitswerten führt. Um die gewünschten Werkstoffeigenschaften zu erhalten, muss daher die α/γ-Verteilung zuverlässig vorhergesagt werden. Dies geschieht in der Regel mit Hilfe des WRC1992-Diagramms. Die Vorhersagegenauigkeit des Ferritgehalts in diesem Diagramm ist jedoch meist nicht genau genug und muss daher optimiert werden. Daher ist es notwendig, selbst kleinste Veränderungen in der chemischen Zusammensetzung des Schweißguts idealerweise während des Schweißens zu überwachen. Dies wird in diesen Experimenten mit Hilfe der laser-induzierten Plasmaspektroskopie (LIBS) durchgeführt. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. In vorherigen Arbeiten wurde bereits die chemische Zusammensetzung im Schweißgut und der WEZ quantifiziert. In der präsentierten Untersuchung wird der Einfluss einzelner Elemente, wie Nb und Cu, auf das resultierende Schweißmikrogefüge untersucht.