Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs.
Investigation of degradation of the aluminum current collector in lithium-ion batteries by GD-OES
(2022)
Lithium-ion batteries (LIBs) are one technology to overcome the challenges of climate and energy crisis. They are widely used in electric vehicles, consumer electronics, or as storage for renewable energy sources. However, despite innovations in batteries' components like cathode and anode materials, separators, and electrolytes, the aging mechanism related to metallic aluminum current collector degradation causes a significant drop in their performance and prevents the durable use of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) is a powerful method for depth-profiling of batteries' electrode materials. This work investigates aging-induced aluminum deposition on commercial lithium cobalt oxide (LCO) batteries' cathodes. The results illustrate the depth-resolved elemental distribution from the cathode surface to the current collector. An accumulation of aluminum is found on the cathode surface by GD-OES, consistent with results from energy-dispersive X-ray spectroscopy (EDX) combined with focused ion beam (FIB) cutting. In comparison to FIB-EDX, GD-OES allows a fast and manageable depth-profiling. Results from different positions on an aged cathode indicate an inhomogeneous aluminum film growth on the surface. The conclusions from these experiments can lead to a better understanding of the degradation of the aluminum current collector, thus leading to higher lifetimes of LIBs.
Aging Mechanisms of Lithium Batteries: How can we make batteries more durable and more sustainable in the future?
Lithium batteries are particularly susceptible to ageing processes. During each charging and discharging process in an electric battery, lithium ions are deposited in the electrodes of the cell like in the pores of a sponge. Over time, however, fractures and cracks occur in the filigree structures. The result: more and more lithium ions no longer fit into the hollow spaces of the „sponge“, instead they accumulate in heaps around the electrodes and hinder the movement of other ions. The performance of the battery decreases.
We present our new project, in which we are developing a fast and cost-effective method with which companies that produce lithium batteries can already assess the ageing behaviour of their batteries in the laboratory.
Lithium-ion batteries are a key technology for tackling challenges in energy and climate crisis, but up to 30 % are discarded right after production. Quality is closely related to the homogeneity of the used materials and coatings. Fluorine compounds, both in the polymer and from degradation of the electrolyte, are of special interest for the formation and aging of LIBs. Glow-discharge optical emission spectroscopy (GD-OES) emerged as a fast and convenient method for depth-profiling of battery materials. However, fluorine remains a spectroscopic challenge due to a high excitation energy and only few strong emission lines in the UV/Vis spectral range.
We investigated the partial substitution of argon with neon in the plasma gas. The main emission line at 685.603 nm was monitored by both photo multiplier tube (PMT) with Czerny-Turner monochromator at 20 µm slit-size, and charge-coupled device (CCD) with 1200 lines/mm grating. For calibration, we used a set of hot-pressed copper cylinders with varying calcium fluoride amount fraction, ranging from 1.6 % to 4.4 %. Plasma gas mixtures with a mole fraction of 5 %, 10 % and 20 % neon in argon were used. Sensitivity in comparison to pure argon was increased by factor 4, 7 and 14, respectively. In general, PMT detection was more sensitive than CCD. As expected, sputter rates decreased with higher neon content in the plasma gas. Depth-profiling of the cathodes was performed in pulsed mode at constant voltage and pressure, which resulted in stable plasma conditions. We achieve matrix-independent quantitative information on fluorine distribution by correction based on sputter rates.
This advancement in GD-OES provides a more accurate analytical approach for evaluating the homogeneity of lithium-ion battery materials, potentially leading to more sustainable and cost-effective manufacturing processes.
To address the challenges of the climate crisis, multiple solutions for sustainable energy sources and storage systems are needed. One such solution is lithium-ion batteries (LIBs). Currently, 5 to 30 % of LIBs are discarded immediately after manufacturing. The homogeneous distribution of all materials used in the coating of cathodes and anodes is critical for the quality of LIBs. Furthermore, during formation i.e., the first steps of the charge/discharge cycling, the solid-electrolyte interphase forms on the anode particles, which has a huge impact on the performance. The same happens to some extent on the cathode, forming the cathode-electrolyte interphase. Fluorinated polymers and electrolytes are used in the manufacturing of LIBs. The electrolyte in particular is prone to degradation during formation and aging of the batteries. The interface of the cathode material with the aluminum current collector is also a critical point where degraded fluorine components cause pitting corrosion and at the same time promote passivation of the metal foil. Monitoring the spatial distribution of fluorine on these surfaces and interfaces is essential for sustainable LIB production.