The subject of this study is how, and to what extent, Varestraint/Transvarestraint test results are influenced by both testing parameters and characteristics of evaluation methods. Several different high-alloyed martensitic LTT (low Transformation temperature) filler materials, CrNi and CrMn type, were selected for examination due to their rather distinctive solidification cracking behaviour, which aroused interest after previous studies. First, the effects of different process parameter sets on the solidification cracking response were measured using standard approaches. Subsequently, microfocus X-ray computer tomography (μCT) scans were performed on the specimens. The results consistently show sub-surface cracking to significant yet varying extents. Different primary solidification types were found using wavelength dispersive X-ray (WDX) analysis conducted on filler metals with varying Cr/Ni equivalent ratios. This aspect is regarded as the main difference between the CrNiand CrMn-type materials in matters of cracking characteristics. Results show that when it comes to testing of modern highperformance alloys, one set of standard Varestraint testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour. During testing, energy input per unit length and bending speed were varied (especially the latter is usually kept at standard values), in addition to the most commonly altered factor - total deformation.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach - microscopic analysis of the specimen surface. It was found that not all parameter changes had the expected outcome. For the Cr8Ni6 and Cr11Mn5 filler materials, influences of energy input per unit length and welding speed were in direct opposition.
In order to investigate those apparent contradictions, μCT scans of MVT specimens were made. The results consistently show sub surface cracking, to significant, yet varying extents. Different primary solidification types were found using WDX-analysis, an aspect that is believed to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
It was found that there is a systematic dependence of the crack growth on the welding parameters as well as on the load. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate.
Based on the results, a new crack criterion was finally selected which allows an extended assessment of the material behavior during the MVT-test. The threshold introduced can quantify the dependencies of the crack formation on the welding and testing parameters, which could not be comprehensively described with the conventional evaluation. In principle, the evaluation routine can also be transferred to other Varestraint or externally loaded hot cracking tests.
The contribution describes a newly developed software tool for crack identification and selection in Modified Varestraint Transvarestraint (MVT) testing. From the digital crack information, in addition to the classical results, such as Total Crack Length (TCL) and Maximum Crack Length (MCL), advanced evaluations can be applied, taking into account the loading and welding parameters. A numerical parameter study is conducted to demonstrate how the isolated variation of individual welding and loading parameters, affects the crack lengths that can potentially be expected based on the machine specifics. An alternative crack criterion is presented that evaluates the crack formation in relation to the machine behavior. Some examples demonstrate the possibilities and limitations of the approach. The criterion can be used to compare and transfer the results of different varestraint test variants.