This paper is a case study of complete substitution of sodium-metasilicate in zeolite Na-A synthesis by an electrostatic filterash (FA) arising in high amounts during silane waste incineration process.The silicate abundant FA is a suitable material for reinsertion in zeolite chemistry. This is shown in the presented investigation by the development of a model reaction process at low temperatures (50–60 °C) and short times (1.5–4 h). The experiments were performed under addition of NaAlO2 and variation of the alkalinity and the reaction period. Characterization and fine tuning of the process was mainly done by studying the kinetics of FA digestion and zeolite crystallization by XRD and chemical analyses (ICP-OES) of solutions and solids. It could be shown that pure FA was mostly dissolved (98%) in 8 m NaOH already after 1 h. Addition of NaAlO2 and crystallization for further 60 min under optimized conditions at 50 °C yielded to a suitable product. It consists of zeolite Na-A (92% by mass) beside some hydrosodalite (8% by mass). According to this low temperature short time process this study is a contribution for the development of energy efficient recycling solutions.
Porous materials are of a great interest due to their ability to interact with ions and molecules not only on their surface but throughout their bulk. Porous materials are conventionally used in applications; such as ion exchange, adsorption/separation and in catalysis, exploiting the huge internal surface area of highly ordered porous materials. [1, 2] The ability for these materials to succeed, in a particular field, is dependent greatly upon the uniformity of the shape and size of the pores within the material. However, despite how well we are able to understand the stability of 3-D frameworks in crystalline or polycrystalline zeolites and ZIFs, there still remains major limitations in fully understanding the synthetic mechanisms occurring prior to their formation. [3, 4] Though the syntheses of a wide variety of porous solids are already well established, their formation mechanisms continue to be of great interest to both academic and industrial communities, with the thought that with greater understanding of the formation of these solids can lead to their rational design. By obtaining a better knowledge of the underlying nucleation mechanisms, it can allow for increased predictability of new structures and in addition can reveal valuable information regarding the particle dimensions aiding in controlling particle morphology and size.
Small-angle and wide-angle X-ray scattering (SAXS/WAXS) are ideal techniques for determining morphological changes in-situ, where the shape, size and crystallinity can be followed at a high temporal resolution, and when these techniques are deployed alongside complimentary techniques, such as ex-situ microscopy, a great deal of information on the formation of materials can be obtained. The above-mentioned methodologies were utilised to study the formation of Silicalite-1 from multiple silica sources to obtain a detailed picture of the formation as a whole, including the formation of intermediate species (Image 1 show the in-situ SAXS data collected from the formation of Silicalite-1 from tetraethyl orthosilicate).
In-situ SAXS/WAXS studies were also utilized to observe the formation of ZIF-8 alongside in-situ X-ray absorption spectroscopy (XAS) experiments to probe both the morphological changes, as well as any changes occurring to the local structure during synthesis (Image 2 show the in-situ SAXS data collected from the formation of ZIF-8). These timeresolved in-situ studies have been utilised to follow changes in crystallinity and crystallite size, whilst also providing valuable information on the formation of intermediate species, the nucleation of crystalline ZIFs, and their subsequent growth.
References:
[1] M E Davis. Nature, 417(6891):813–21, 2002
[2] S T Meek, J A Greathouse, M D Allendorf, Advanced Materials, 23 (2): 249-267, 2011
[3] J Grand, H Awala, CrystEngComm,18 (5): 650–664, 2016
[4] M J V Vleet, T Weng, X Li, J R Schmidt. Chem.Rev.,118 (7): 3681–3721, 2018