Mathematical analysis of the bulging effect in high power laser beam welding of thick steel sheets
(2021)
The present work is devoted to the mathematical analysis of the bulging effect in high-power laser beam welding of thick steel sheets. The numerical results are based upon experimental results from previous studies, revealing the relationships between the bulging effect, the hot cracking formation, and the distribution of alloying elements in the weld pool. The widening of the molten pool in its middle area is observed for both complete and partial penetration welding of 8 mm - 15 mm thick structural steel sheets. The weld pool shape is extracted from the simulations to evaluate the extent of the necking and bulging of the solidification isotherm and their influence on the hot cracking formation and the mixing behavior of the weld pool. Relying on an earlier numerical study utilizing a fixed keyhole, simulation models considering a dynamic keyhole are developed thereto. The link between the bulge and the studied phenomena is found to be significant.
Recent studies have confirmed the widening of the weld pool interface, known as a bulge effect, during deep penetration high power laser beam welding. The link between such geometric particularities of the weld pool shape and the hot cracking phenomena is significant. The present work seeks to extend the level of understanding by investigating their relationship. A coupled multiphysics, multiscale numerical framework is developed, comprising a series of subsequent analyses. The study examines the influences of the bulge on the three most dominant effects causing hot cracking, namely the thermal cycles, the mechanical loading, and the local microstructure. The bulge in the weld pool shape forms approximately in the middle of the plate, thus correlating with the location of hot cracking. It increases the hot cracking susceptibility by enhancing the three dominant effects. The numerical results are backed up by experimental data.
The weld pool dynamics and shape play a fundamental role in keyhole mode welding. The presented work aims the experimental and numerical investigation of the influence of the weld pool characteristics on the formation of hot cracking. The experimental procedure allows recording the molten pool in the longitudinal section of a butt joint configuration of 15 mm thick structural steel and transparent quartz glass by using a high-speed video camera and two thermal imaging cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop-shaped weld pool. A bulge-region and its temporal evolution are observed approximately in the middle of the depth of the weld pool, where hot cracking appears. A numerical framework including models for the weld pool dynamics, global temperature field, transient stress state, crystal growth, diffusion and macro-segregation and subroutines for their one-way couplings is developed. The numerically obtained and experimentally observed results are in a good agreement. It is shown that the bulge-region leads to a delay in the solidification behavior, increased temporal tensile stresses and accumulation of impurities in the defect region and hence enhance the probability of hot cracking formation.
A laser induced breakdown spectroscopy (LIBS) system was combined with the Gas Tungsten Arc (TIG) Welding process for the in situ monitoring of chemical compositions in austenitic stainless steels during welding. The purpose of this project is to develop a prototype of an online chemical composition control system for welding applications. One of the use cases of this new LIBS-based measurement system can be the controlling of potentially dangerous emissions during the welding process in order to improve the working safety conditions.
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test
The strain rate has a significant influence on the formation of the hot crack
It was possible to determine the critical strain and strain rate that led to shot crack formation
A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed.
Good agreement between the strain field measured using the DIC technique and the simulation results
Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties