Characterization of residual stress state by neutron diffraction and residual magnetic field mapping
(2016)
Based on the residual stress characterization of tungsten inert gas welded S235JRC+C plates by means of neutron diffraction, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors is discussed. The experiments performed indicate a correlation of residual stress changes and local residual magnetic stray fields.
Neutron diffraction: the forgotten non-destructive technique for residual stress analysis … and more
(2016)
3-D Stress Analysis
(Bulk) Stress mapping
Thick (and thin) films & Interfaces
Bulk high temperature
Real time
In-situ testing: Large sample environment (Stress rigs, Furnaces, …)
Neutrons and Synchrotron Radiation allow all this because they are FASTER , DEEPER and MORE PRECISE than lab equipment
(Flux)(Energy)(Parallel Beam)
Characterization of multiphase metal matrix composites by means of CT and neutron diffraction
(2016)
The present study examines the relationship between the microstructure of multiphase MMC and their damage mechanisms. The matrix AlSi12CuMgNi was combined with 15% vol. Al2O3 (short fibres) and with 7% vol. Al2O3 + 15% vol. SiC (short fibres and whiskers, respectively). The experimental approach encompasses 3D microstructure characterization by means of computed tomography of samples (a) as-received, (b) after heat treatment, and (c) after compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation and the presence of defects and damage are studied.
Influence of addition of SiC whiskers on mechanical properties of composite was investigated. Phase-specific load partition analysis for samples with fibre plane parallel to load was perform by using neutron diffraction measurements during in-situ compression. It shows damage in the Si phase, while Al2O3 short fibres carry load without damage until failure. The computed tomography observations confirm the load partition analysis.
Magnetic testing methods are frequently applied in non-destructive evaluation of ferromagnetic materials. In the past decade, metal magnetic memory (MMM) technique according to ISO 24497 is gaining considerable interest in the magnetic NDT community. In contrast to traditional Magnetic Flux Leakage (MFL) testing, the inspection objects are not intentionally magnetized by an external magnetic field. Due to physical coupling between mechanical stress and magnetization in ferromagnetic materials, it is assumed that the distribution of the “natural” MFL (self-magnetic-leakage field, SMLF) indicate zones of different remanent magnetization, which in turn, correspond to the internal stress of specimen or in the most general sense to material degradation.
Usually, MMM measurements are performed by relatively bulky magnetic inspection sensors providing a spatial resolution in millimetre range. High precision GMR (Giant Magneto Resistance) measurements in the micrometer regime along with image based representation and evaluation can provide a higher degree of information. We present a concise summary of a broader research project aimed at studying the correlation of magnetic structure and microstructure of steels. Particularly, we compare residual stress measurements in S235JR steel by means of neutron diffraction with high resolution magnetic field measurements. In addition, we discuss the influence of deformation-induced magnetization in plastically deformed specimens with and without notches due to various quasi-static and cyclic load levels. Furthermore, comparative measurements with common non-destructive testing methods are presented.
Despite of a quantitative evaluation of material degradation, the in the field inspection by MMM remains problematic due to substantial influences on such as external magnetization, anisotropy of internal magnetization and material degradation, as well as geometry and surface effects of the inspection objects on SMFL signals. The prospects and restrictions of the MMM technique are discussed in this contribution.
In the present study, internal damage to an AlSi12CuMgNi alloy reinforced with planar random Al2O3 short fibres was investigated after compression testing. Due to the alloy composition, this composite contains a second reinforcement phase in the form of eutectic Si, which builds interpenetrated networks in the volume and increases the creep resistance and load-bearing capacity of the material. Materials with their fibre plane parallel and transversal to the load direction were characterized in order to investigate the dependence of load partition and damage on fibre plane orientation. In-situ compression testing during neutron diffraction measurements showed that internal damage is strongly influenced by the load partition between matrix and reinforcement. Moreover, micro-computed tomography was performed in the same material after ex-situ compression for damage analysis. In the case of a fibre plane perpendicular to the applied load, breakage and interconnected cracks appeared in a significantly higher volume fraction than with a fibre plane parallel to load.
Observation of martensite formation by combined use of synchrotron diffraction and dilatometry
(2016)
Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material.