We report on the in situ investigation of the Al13 sulfate synthesis by WAXS. Al13 sulfates were crystallized by precipitating hydrolyzed aluminum solutions by the addition of sodium sulfate. The measurements were performed using an acoustic levitator. The study provides information about the intermediates during the crystallization process.
Texture formation in amorphous Al86Ni6Y4.5La1.5Co2 splats by thermal and mechanical treatment
(2016)
The crystallization behavior of amorphous Al86Ni6Y4.5La1.5Co2 splats was analyzed by differential scanning calorimetry (DSC) and X-ray diffraction (XRD). Rietveld refinement was used to analyze the preferred orientation of fcc aluminum nanocrystals in the residual amorphous matrix after annealing. Fiber textures in [200] and [220] directions were found after heating to 360 C. The influence of cold rolling on the preferred crystal orientation was studied as a function of the thickness reduction of the specimen. It was found that cold rolling significantly increases the (220) texture, while the (200) texture remains unchanged. Based on the experimental results the formation of (220) and (200) texture during the crystallization of the amorphous splats was ascribed to two different processes, internal stresses induced during splat formation or cold-rolling.
Chemical variability is a main strength of glass. Glass powders are therefore promising candidates for manufacturing a broad diversity of sintered materials like sintered ¬glass-ceramics, glass matrix composites or glass bonded ceramics with tailored mechanical, thermal, electrical and optical properties and complex shape. Its wide and precise adjustability makes this class of materials, even if it may not be obvious at first sight, a key component of advanced technologies. Manufacture and processing of initial glass powders often allow even more flexibility in materials design. At the same time, however, they can cause additional problems. The lecture illustrates possible consequences of glass powder processing upon glass crystallization and sintering as well as chances for targeted utilization. Simple kinetic models describing the effect of particle size distribution, surface crystallization and rigid inclusions on sintering as well effects of different milling and seeding on sinter crystallization are presented.
Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during the sintering, which results in poor mechanical properties and reduced bioactivity. Recently, new bioactive glasses with improved crystallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. The aim of this study was to investigate the sintering and crystallization behavior of these new bioactive glasses.
Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. In addition, FTIR and XRD analyses show that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases are detected. The thermal properties of all glasses were studied by DTA measurements, and the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles progressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization of beta-HAp.
Nowadays, the use of bioactive glasses is established for bone regeneration; however glasses are used mostly as powders, granules or in a paste. Sintered scaffolds are not used clinically, because of the inherent problem of crystallization during the sintering process, resulting in poor mechanical properties and reduced bioactivity. Therefore it was the aim to design new bioactive glasses, which combine improved processing and sintering with bioactivity.
Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 8 mol% calcium fluoride were added, in order to stabilize the glass against crystallization.
The sintering behavior of the new glasses was characterized by heating microscopy and compared to that of Bioglass® 45S5. Results show that the new glasses achieve a sintered density of 88-99 % in contrast to only 57-67% for Bioglass® 45S5. In addition, FTIR and XRD analyses show that Bioglass® 45S5 crystallizes during sintering while for the new glasses no crystalline phases were detected. The thermal properties of all glasses were studied by DTA and DSC measurements, and the influence of grain size was characterized. These studies showed an increase of sintering temperature and final porosity with increasing particle size. The structure of sintered compacts during and after sintering was examined using light and electron microscopy (SEM).
Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during sintering. Recently, new bioactive glasses with improved crys-tallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. Whereas Bioglass® 45S5 powder compacts crystallize during sintering, for the new glasses no crystalline phases were detected. Additionally the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles pro-gressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization.
While polymorphism is a common phenomenon in the crystallization processes of organic compounds, polyamorphism has gained importance only recently. Using sophisticated sample environments and applying in situ scattering methods and vibrational spectroscopy, the complete crystallization process of organic compounds from solution can be traced and characterized. Diffuse scattering from amorphous intermediates can be investigated by analyzing the atomic pair Distribution function (PDF) to gain further insights into molecular pre-orientation. The crystallization behavior of Paracetamol was studied exemplarily under defined, surface-free conditions. Based on the choice of the solvent, the formation of different polymorphs is promoted. The thermodynamically stable form I and the metastable orthorhombic form II could be isolated in pure form directly from solution. For both polymorphs, the crystallization from solution proceeds via a distinct amorphous precursor phase. PDF analyses of these different amorphous states indicate a specific pre-orientation of the analyte molecules introduced by the solvent. The resulting crystalline polymorph is already imprinted in these proto-crystalline precursors. Direct experimental evidence for the polyamorphism of paracetamol is provided.