- Fatigue strength (19) (entfernen)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
The paper provides an application of the IBESS approach to the investigation of the influence of various parameters of the global and local weld geometry as well as material defects on the fatigue strength of weldments. For this purpose, the global weld parameters, such as the weld toe radius, the flank angle, the excess weld metal, local secondary notches (in the present study as a measure of surface imperfections) and inclusions sizes have been determined as statistical distributions for different joint types and geometries and two steels of different strengths. The results are in line with literature data and reveal the potential of the theoretical approach to predict the correct trends. The combination with an advanced weld quality system has been demonstrated to be possible.
If a component is cyclically loaded, its load carrying capacity is considerably lower than in the monotonic loading case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and unwelded regions (Chapter 8) and a pronounced surface roughness in the as-built condition (Chapter 9). In addition, effects due to the anisotropy of the microstructure (Chapter 6) and a complex residual stress pattern (Chapter 7) play an important role. A consequence is that common strategies of fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness and residual stresses. The chapter gives a brief introduction to these problem areas.
The safe joining of new, freshly developed steel types keeps challenging the industry–and is assumed to go on in doing so. In the body-in-white production, these materials are mainly joined using resistance spot welding. During the past ten years, various investigations on resistance spot welding of advanced high strength steels have been carried out at Fraunhofer IPK and the Federal Institute for Materials Research and Testing (BAM). This paper aims to give an overview about both the top former and recent studies and results. The investigated topics are the influences of manufacturing conditions as initial gaps and restraints on spot welds, their impact on the fatigue strength of a joint and the cracking-wise safe weldability of AHSS.
Caused by non-ideal manufacturing conditions, cracks in spot welds (e.g. caused by liquid metal embrittlement) are still regarded as a potential risk in industrial practice. Therefore, a method to evaluate the safe weldability regarding the cracking susceptibility was developed for AHSS. The method is easy to perform, even without expensive laboratory equipment. It allows the end user to establish a material ranking regarding the cracking susceptibility of the handled steels. Recently, coupled thermo-mechanical finite element modelling has been used to describe critical stress-strain conditions responsible for the occurrence of liquid metal embrittlement, and to improve the understanding of the process.
The work aims at addressing the modelling and implementation of criteria for multiple crack propagation, including interaction and coalescence, for a more reliable fracture mechanics-based prediction of stress-life curves for weldments.
A large experimental work is presented in which micro-cracks have been made visible by heat-tinting at successive stages of fatigue life of the welded specimens. Here the correlation between the number of initiation sites and the applied stress level has been also investigated.
The criteria have been implemented in in-house software, which allows multiple fatigue crack propagation, and validated against selected experimental tests. The results have shown that the modelling of multiple crack propagation and interaction is crucial for the prediction of the fatigue strength of weldments, both in finite and infinite life regime.
The work aims at addressing the modelling and implementation of criteria for multiple crack propagation, including interaction and coalescence, for a more reliable fracture mechanics-based prediction of stress-life curves for weldments.
A large experimental work is presented in which micro-cracks have been made visible by heat-tinting at successive stages of fatigue life of the welded specimens. Here the correlation between the number of initiation sites and the applied stress level has been also investigated.
The criteria have been implemented in in-house software, which allows multiple fatigue crack propagation, and validated against selected experimental tests. The results have shown that the modelling of multiple crack propagation and interaction is crucial for the prediction of the fatigue strength of weldments, both in finite and infinite life regime.
IBESS Methology for the fracture mechanics-based determination of the fatigue strength of weldments
(2018)
The presentation provides a brief overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common K concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit as defined for 107 loading cycles and the finite life branch of the S-N curve are determined.
The 21st century brought new and complex technological challenges, which need to be solved. Of primary importance is the global energy transition that pushes forward the research and innovation in order to achieve the goal of replacing the existing non-renewable energy sources with new renewable and efficient ones, with positive effects on the world climate. In many countries worldwide mid- and long-term goals have been set out in order to reduce the greenhouse gas emissions. Germany, among others, intends to reduce the emissions by 80 to 95% within 2050, compared with 1990 levels. The achievement of this goal is aimed to be realized by the development of new and more efficient energy sources, but also by substantial investments in electromobility (the goal is to bring one million electrically driven vehicles onto German streets by 2020).
Another important challenge came into play following the global financial crisis, which pushed many industries to reduce their operational and maintenance costs. In particular, the life-cycle management of a component has become of primary importance. In some cases it has been shown that the underestimation or the lack of awareness in ageing of plants led to incidents due to the loss of technical integrity. Other studies demonstrated that the component life of many of the long-life components could be extended up to 50% without compromising safety.
The third, not less important, challenge is driven by the development of new technologies and materials. The trends show a large investment in additive manufactured metal components and new metallic materials which have to assure longer in-service life, lightweighting and efficient recycling.
This works aims at addressing part of these problems by proposing a fracture mechanics-based analytical procedure for the determination of the fatigue lives of engineering components and particularly of welded joints. In fact, an analytical tool, which is able to simulate the main failure mechanisms of weldments under fatigue loading, brings many advantages: i) drastic reduction of long and expensive experimental tests; ii) optimization of the geometry and production processes (possible weight reduction); iii) better estimate of the safety margins used in the design of the components (life extension without safety issues).
The results show that the model can fairly well predict the lives of the welded joints investigated experimentally, irrespective of the geometry and loading conditions.
The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined.
Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5.
The present paper provides a discussion on all these topics and it offers solutions for it. The authors present an analytical solution of a Delta J based crack driving force based on an R6 type approach but modified for cyclic loading. The gradual build-up of the crack closure effect is modelled by the so-called cyclic R curve which describes the crack size dependency of the fatigue crack propagation threshold in the short crack regime. It is explained how the cyclic R curve is experimentally determined and how it can be estimated by a modified Kitagawa-Takahashi approach.
Common fracture mechanics based fatigue considerations are usually limited to the residual lifetime determination of so-called long cracks. The extension of this concept to the total lifetime, as in the S-N curve approach, requires an adequate description of short crack propagation which cannot be based on the Delta K concept, and it must consider the crack closure phenomenon as well as its gradual build-up at the short crack stage. Further, it has to provide a meaningful definition of initial crack dimensions and a solution for the multiple crack problem at stress levels higher than the fatigue limit as it is specific for some configurations such as weldments. This paper aims at a discussion of all these points and offers possible solutions which are illustrated by examples taken from the German IBESS project on fracture mechanics based determination of the fatigue strength of weldments, the results of which will be discussed in more detail in this Special issue.