The aim of this study is to develop nanometer-thin epoxy-based films on aluminium alloy AA2024-T3 as a model coating system for high resolution corrosion studies. Spin coating was used for the layer-by-layer (LbL) deposition of poly-(ethylenimine) (PEI) and poly([o-cresyl glycidyl ether]-co-formaldehyde) (CNER) bilayers. The film chemistry and the cross-linking process were characterized by means of Fourier-transform infrared spectroscopy (FTIR).
Ellipsometric data confirmed the linear increase of film thickness. The potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) results indicate the improvement of the film barrier properties with increasing film thickness. Mapping of the topography and the volta potential was performed by means of scanning Kelvin probe force microscopy (SKPFM).
The results indicate the presence of a homogeneous film structure, while the intermetallic phases can still be identified below the coating. The SKPFM Analysis confirmed that the model films are suitable for investigation of corrosion processes at the coating/metal interface.
Iron-doped SnO2 coatings were deposited in a 50 kHz DC-pulsed magnetron sputtering discharge. The pulses had a duration of 4 µs in selected gas mixtures from pure argon up to
60% of oxygen at a constant total pressure of 0.2 Pa. A single target of SnO2 with Fe inset was used. The mass spectrometry study detected the gas-related ions Ar+, O2+ and O+, where the last one becomes the dominant positive ion at higher oxygen contents. Atomic oxygen ions had a higher energy as it resulted from the collision-caused dissociation on the target surface. The tin-related species were detected as Sn+ and SnO+. SnO2+ species were not detected. The deposition rate decreased by using gas mixtures with oxygen as well as the corresponding amount of Sn-related species in the plasma. The increase of oxygen also increased significantly the sheet resistance of the films. The XPS study showed that the iron concentration decreased by using additional oxygen. But the O/Sn ratio in the coatings was constant, contrary to the increased FeO/Fe ratio in the films. An additional analysis of the coatings by spectroscopic ellipsometry has shown a dependence of the polarizability and the permittivity on the amount of oxygen used during the deposition. In contrast, the study has found no such dependence for the absorption of the layers.